PULSE™ 2100LG Engineering Resin is designed to provide top performance in tough applications, from single piece items to intricate components. Ideal for energy management solutions, it can withstand high and low temperature extremes and rapid, repeated temperature fluctuations.
Benefits:
Low gloss appearance
Low temperature ductility
Wide range of performance
Superior processability
Lot to lot consistency
Good chemical resistance
| Original Document | Technical Datasheet(English) | |||
| Features | High Impact at Low TemperaturGood ToughnessLow GlossEasy processingChemical Resistance | |||
| Automotive Specs | Audi TL 52231 AVAG(Volkswagen Group) TL 52231VAG(Volkswagen Group) TL 52231 AVAG(Volkswagen Group) TL 52231 BGM(General Motors) GMW15581P-ABS+PC-T1FORD WSS-M4D924-B13M 11-0003-5762-1FCA (Fiat Chrysler Automobiles) MS-DB 195-CPN3964Chrysler MS-DB 195-CPN3964GM(General Motors) GMW15581P-ABS+PC-T4 | |||
| Physical | Value/Unit(Sign in to View) | Test Standard | Test Condition |
|---|---|---|---|
Density/Specific Gravity | *** g/cm³ | ISO 1183 | |
Density/Specific Gravity | *** g/cm³ | ASTM D792 | |
Melt Mass Flow Rate(MFR) | |||
260°C/3.8 kg | *** g/10 min | ASTM D 1238 | |
260°C/5.0 kg | *** g/10min | ISO 1133 | |
Mold Shrinkage | |||
Flow | *** % | ASTM D955 | |
- | *** % | ISO 294-4 | |
Water Absorption | *** % | ASTM D570 | 24 hr, 23°C |
Water Absorption | *** % | ISO 62 | 24 hr, 23°C |
| Mechanical | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Tensile Modulus | *** Mpa | ASTM D638 | 3.20 mm,Injection Molded |
Tensile Modulus | *** Mpa | ISO 527-2 | |
Tensile Strength | |||
Yield | *** Mpa | ASTM D638 | 3.20 mm,Injection Molded |
Yield | *** Mpa | ISO 527-2 | |
Break | *** Mpa | ASTM D638 | 3.20 mm,Injection Molded |
Tensile Elongation | |||
Yield | *** % | ASTM D638 | 3.20 mm,Injection Molded |
Yield | *** % | ISO 527-2 | |
Break | *** % | ASTM D638 | 3.20 mm,Injection Molded |
Break | *** % | ISO 527-2 | |
Flexural Modulus | *** Mpa | ASTM D790 | 3.20 mm,Injection Molded |
Flexural Modulus | *** Mpa | ISO 178 | |
Flexural Strength | |||
- | *** Mpa | ASTM D790 | 3.20 mm,Injection Molded |
- | *** Mpa | ISO 178 | |
| Impact | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Izod Notched Impact Strengh | |||
-40℃ (-40℉) | *** kJ/m² | ISO 180 | |
-30℃ (-22℉) | *** kJ/m² | ISO 180 | |
-29℃ (-20℉) | *** J/m | ASTM D 256 | 3.20 mm,Injection Molded |
23℃ (73℉) | *** J/m | ASTM D256 | 3.20 mm,Injection Molded |
23℃ (73℉) | *** kJ/m² | ISO 180 | |
Instrumented Impact Energy | |||
-29℃ (-20℉)peak | *** J | ASTM D 3763 | 3.20 mm |
23℃ (73℉)peak | *** J | ASTM D3763 | 3.20 mm |
| Thermal | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Heat Deflection Temperature(HDT) | |||
0.45 Mpa (66 psi)（4.6kg/cm²） | *** °C | ASTM D648 | 3.20 mm,Unannealed |
0.45 Mpa (66 psi)（4.6kg/cm²） | *** °C | ISO 75-2/B | 3.20 mm,Unannealed |
1.8 Mpa (264 psi)（18.6kg/cm²） | *** °C | ASTM D648 | 3.20 mm,Unannealed |
1.8 Mpa (264 psi)（18.6kg/cm²） | *** °C | ISO 75-2/A | 3.20 mm,Unannealed |
Vicat Softening Temperature(VST) | *** °C | ASTM D1525 | Rate A (50°C/h), Loading 2 (50 N) |
Vicat Softening Temperature(VST) | *** °C | ISO 306 | A120 |
Vicat Softening Temperature(VST) | *** °C | ISO 306/B50 | |
Coefficient of Linear Thermal Expansion | |||
Flow | *** E-6 cm/cm/℃ | ASTM D 696 | -40 to 180°C |
| Optical | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Gloss | *** - | ASTM D542 | 60°, Smooth |
The information presented on this datasheet was acquired by AjiEng.com from the producer of the material. AjiEng.com makes substantial efforts to assure the accuracy of this data. However, AjiEng.com assumes no responsibility for the data values and strongly encourages that upon final material selection, data points are validated with the material supplier.