MAGNUM™ 8391 MED ABS combines an excellent glossy appearance with high flow and medium impact performance. The mass (continuous process) ABS technology ensures an ABS resin that combines excellent processability with a stable light base color that is ideal for self-coloring. MAGNUM 8391 MED natural resin has undergone biocompatibility testing based on ISO 10993 (Biological Evaluation of Medical Devices) and is suitable for use in approved medical applications.
Applications:
Medical Applications
| Original Document | Technical Datasheet(English) | |||
| Features | High GlossMedical Application/Health CareBiocompatibleHigh Flow | |||
| Appearance | Pellets/GranulesNatural Color | |||
| Compliance | ISO10993 | |||
| Physical | Value/Unit(Sign in to View) | Test Standard | Test Condition |
|---|---|---|---|
Density/Specific Gravity | *** g/cm³ | ISO 1183 | |
Density/Specific Gravity | *** g/cm³ | ASTM D792 | |
Melt Mass Flow Rate(MFR) | |||
220℃/10 kg | *** g/10 min | ISO 1133 | |
220℃/10 kg | *** g/10 min | ASTM D 1238 | |
230°C/3.8 kg | *** g/10 min | ASTM D 1238 | |
Mold Shrinkage | |||
Flow | ***~*** % | ASTM D955 | |
Flow | ***~*** % | ISO 294-4 | |
Bulk(Apparent ) Density | *** g/cm³ | ISO 60 | |
| Mechanical | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Tensile Modulus | *** Mpa | ISO 527-2 | |
Tensile Strength | |||
Yield | *** Mpa | ASTM D638 | 50 mm/min |
Yield | *** Mpa | ISO 527 | 3.20 mm,Injection Molded |
Yield | *** Mpa | ISO 527-2/50 | 3.20 mm,Injection Molded |
Break | *** Mpa | ASTM D638 | 50 mm/min |
Tensile Elongation | |||
Yield | *** % | ASTM D638 | 50 mm/min |
Yield | *** % | ISO 527 | 3.20 mm,Injection Molded |
Yield | *** % | ISO 527-2/50 | 3.20 mm,Injection Molded |
Break | *** % | ASTM D638 | 50 mm/min |
Flexural Modulus | *** Mpa | ASTM D790 | 1.3 mm/min |
Flexural Modulus | *** Mpa | ISO 178 | 2.0 mm/min |
Flexural Strength | |||
- | *** Mpa | ASTM D790 | 1.3 mm/min |
- | *** Mpa | ISO 178 | 2.0 mm/min |
| Impact | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Charpy Notched Impact Strengh | |||
-30℃ (-22℉) | *** kJ/m² | ISO 179/1eA | Injection Molded |
23℃ (73℉) | *** kJ/m² | ISO 179/1eA | Injection Molded |
Izod Notched Impact Strengh | |||
-30℃ (-22℉) | *** kJ/m² | ISO 180/A | Injection Molded |
23℃ (73℉) | *** J/m | ASTM D256 | |
23℃ (73℉) | *** kJ/m² | ISO 180/A | Injection Molded |
| Hardness | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Rockwell R | *** R | ASTM D785 | |
| Thermal | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Heat Deflection Temperature(HDT) | |||
0.45 Mpa (66 psi)（4.6kg/cm²） | *** °C | ASTM D648 | Unannealed |
1.8 Mpa (264 psi)（18.6kg/cm²） | *** °C | ASTM D648 | Unannealed |
1.8 Mpa (264 psi)（18.6kg/cm²） | *** °C | ISO 75-2/A | Annealed |
Vicat Softening Temperature(VST) | *** °C | ASTM D1525 | Rate B (120°C/h), Loading 1 (10 N) |
Vicat Softening Temperature(VST) | *** °C | ISO 306/B50 | |
| Flammability | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Flame Rating | |||
HB | *** mm | UL94 | |
HB | *** mm | UL94 | |
Burning Rate | *** mm/min | ISO 3795 |
The information presented on this datasheet was acquired by AjiEng.com from the producer of the material. AjiEng.com makes substantial efforts to assure the accuracy of this data. However, AjiEng.com assumes no responsibility for the data values and strongly encourages that upon final material selection, data points are validated with the material supplier.