High Heat, Low Gloss, Medium Impact ABS resin for injection molded automotive interior trim applications
| Original Document | Technical Datasheet(English) | |||
| Features | Medium Impact ResistanceHeat ResistanceLow Gloss | |||
| Applications | Automotive Interior Trims | |||
| Processing | Injection | |||
| Automotive Specs | VAG(Volkswagen Group) TL 527VAG(Volkswagen Group) TL 527 AVAG(Volkswagen Group) TL 527 BFORD WSS-M4D690-B1GM(General Motors) GMW15572P-ABS-T2FCA (Fiat Chrysler Automobiles) MS-DB 191-CPN1734FCA (Fiat Chrysler Automobiles) MS-DB 191-CPN3826FCA (Fiat Chrysler Automobiles) MS-DB 300-CPN4412FCA (Fiat Chrysler Automobiles) MS-DB 300-CPN4537Toyota TSM 5512G-2B | |||
| Physical | Value/Unit(Sign in to View) | Test Standard | Test Condition |
|---|---|---|---|
Density/Specific Gravity | *** g/cm³ | ISO 1183 | |
Density/Specific Gravity | *** g/cm³ | ASTM D792 | |
Melt Mass Flow Rate(MFR) | |||
230°C/3.8 kg | *** g/10 min | ASTM D 1238 | |
230°C/3.8 kg | *** g/10 min | ISO 1133 | |
Mold Shrinkage | |||
Flow | *** % | ISO 294-4 | |
Across Flow | *** % | ISO 294-4 | |
Bulk(Apparent ) Density | *** g/cm³ | ASTM D 1895 | |
| Mechanical | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Tensile Modulus | *** Mpa | ASTM D638 | 51 mm/min |
Tensile Modulus | *** Mpa | ISO 527-2 | |
Tensile Strength | |||
Yield | *** Mpa | ASTM D638 | 51 mm/min |
Yield | *** Mpa | ISO 527-2/50 | |
Tensile Elongation | |||
Yield | *** % | ASTM D638 | 51 mm/min |
Yield | *** % | ISO 527-2/50 | |
Break | *** % | ASTM D638 | 51 mm/min |
Break | *** % | ISO 527-2/50 | |
Flexural Modulus | *** Mpa | ASTM D790 | 1.3 mm/min |
Flexural Modulus | *** Mpa | ISO 178 | 2.0 mm/min |
Flexural Strength | |||
- | *** Mpa | ASTM D790 | 1.3 mm/min |
- | *** Mpa | ISO 178 | 2.0 mm/min |
| Impact | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Charpy Notched Impact Strengh | |||
-30℃ (-22℉) | *** kJ/m² | ISO 179/1eA | |
23℃ (73℉) | *** kJ/m² | ISO 179/1eA | |
Izod Notched Impact Strengh | |||
-30℃ (-22℉) | *** J/m | ASTM D256 | |
-30℃ (-22℉) | *** kJ/m² | ISO 180/A | |
23℃ (73℉) | *** J/m | ASTM D256 | |
23℃ (73℉) | *** kJ/m² | ISO 180/A | |
Instrumented Impact Energy | |||
-30℃ (-22℉)peak | *** J | ASTM D3763 | |
23℃ (73℉)peak | *** J | ASTM D3763 | |
| Thermal | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Heat Deflection Temperature(HDT) | |||
0.45 Mpa (66 psi)（4.6kg/cm²） | *** °C | ASTM D648 | Unannealed |
0.45 Mpa (66 psi)（4.6kg/cm²） | *** °C | ISO 75-2/B | Unannealed |
1.8 Mpa (264 psi)（18.6kg/cm²） | *** °C | ASTM D648 | Unannealed |
1.8 Mpa (264 psi)（18.6kg/cm²） | *** °C | ISO 75-2/A | Unannealed |
Vicat Softening Temperature(VST) | *** °C | ASTM D1525 | Rate A (50°C/h), Loading 2 (50 N) |
Vicat Softening Temperature(VST) | *** °C | ISO 306/B50 | |
Coefficient of Linear Thermal Expansion | |||
Flow | *** E-6 cm/cm/℃ | ASTM E831 | -40 to 100°C |
Across Flow | *** E-6 cm/cm/℃ | ASTM E831 | -40 to 100°C |
| Flammability | Value/Unit(Sign in to View) | Test Standard | Test Condition |
FMVSS | *** mm/min | FMVSS 302 |
The information presented on this datasheet was acquired by AjiEng.com from the producer of the material. AjiEng.com makes substantial efforts to assure the accuracy of this data. However, AjiEng.com assumes no responsibility for the data values and strongly encourages that upon final material selection, data points are validated with the material supplier.