MAGNUM* 3513 is a grade which combines high impact with good flowability. It is suitable for injection moulding and extrusion applications.
The mass (continuous process) ABS technology ensures an ABS resin that combines excellent processability with a stable light base colour that is ideal for self-colouring.
Applications:
Extruded sheet
Profiles
General injection moulding
| Original Document | Technical Datasheet(English) | |||
| Features | High ImpactHigh Flow | |||
| Processing | InjectionExtrusionSheet ExtrusionProfile Extrusion | |||
| Automotive Specs | BMW GS 93016 Color: BlackChery CMP.ABS.A2Geely MAD PI0248-BGreat Wall MP03-02 | |||
| Physical | Value/Unit(Sign in to View) | Test Standard | Test Condition |
|---|---|---|---|
Density/Specific Gravity | *** g/cm³ | ISO 1183 | |
Density/Specific Gravity | *** g/cm³ | ASTM D792 | |
Melt Mass Flow Rate(MFR) | |||
220°C/5.0 kg | *** g/10 min | ASTM D 1238 | |
220℃/10 kg | *** g/10 min | ASTM D 1238 | |
230°C/3.8 kg | *** g/10 min | ASTM D 1238 | |
Mold Shrinkage | |||
Flow | ***~*** % | ISO 294-4 | |
Bulk(Apparent ) Density | *** g/cm³ | ISO 60 | |
| Mechanical | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Tensile Modulus | *** Mpa | ASTM D638 | |
Tensile Modulus | *** Mpa | ISO 527-2 | 3.20 mm,Injection Molded |
Tensile Strength | |||
Yield | *** Mpa | ASTM D638 | |
Yield | *** Mpa | ISO 527-2/50 | 3.20 mm,Injection Molded |
Tensile Elongation | |||
Yield | *** % | ASTM D638 | |
Yield | *** % | ISO 527-2/50 | 3.20 mm,Injection Molded |
Flexural Modulus | *** Mpa | ASTM D790 | |
Flexural Modulus | *** Mpa | ISO 178 | 3.20 mm,Injection Molded |
Flexural Strength | |||
- | *** Mpa | ASTM D790 | |
- | *** Mpa | ISO 178 | 3.20 mm,Injection Molded |
| Impact | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Charpy Notched Impact Strengh | |||
-30℃ (-22℉) | *** kJ/m² | ISO 179/1eA | Injection Molded |
-30℃ (-22℉) | *** kJ/m² | ISO 179/2C | Injection Molded |
23℃ (73℉) | *** kJ/m² | ISO 179/1eA | Injection Molded |
23℃ (73℉) | *** kJ/m² | ISO 179/2C | Injection Molded |
Izod Notched Impact Strengh | |||
-30℃ (-22℉) | *** kJ/m² | ISO 180/1A | Injection Molded |
23℃ (73℉) | *** J/m | ASTM D256 | |
23℃ (73℉) | *** kJ/m² | ISO 180/1A | Injection Molded |
| Thermal | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Heat Deflection Temperature(HDT) | |||
1.8 Mpa (264 psi)（18.6kg/cm²） | *** °C | ISO 75-2/A | Annealed |
Vicat Softening Temperature(VST) | *** °C | ASTM D1525 | |
Vicat Softening Temperature(VST) | *** °C | ISO 306/B50 | |
| Flammability | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Flame Rating | |||
HB | *** mm | UL94 | |
HB | *** mm | UL94 | |
Burning Rate | *** mm/min | ISO 3795 | 2.0 mm |
| Optical | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Gloss | *** - | ASTM D 523 | 60° |
The information presented on this datasheet was acquired by AjiEng.com from the producer of the material. AjiEng.com makes substantial efforts to assure the accuracy of this data. However, AjiEng.com assumes no responsibility for the data values and strongly encourages that upon final material selection, data points are validated with the material supplier.