High Heat, Low Gloss ABS resin with good practical toughness for injection molded automotive interior applications.
Applications:
Door panels, Floor consoles, Instrument Panel & Sidewall trim parts.
| Original Document | Technical Datasheet-ISO(English) | |||
| Features | Good ToughnessHeat ResistanceLow Gloss | |||
| Applications | Automotive Instrument PanelAutomotive ConsolesAutomotive Door panels | |||
| Appearance | Pellets/GranulesNatural Color | |||
| Processing | Injection | |||
| Automotive Specs | BMW GS 93016FORD WSS-M4D906-B2 | |||
| Physical | Value/Unit(Sign in to View) | Test Standard | Test Condition |
|---|---|---|---|
Density/Specific Gravity | *** g/cm³ | ISO 1183 | |
Melt Mass Flow Rate(MFR) | |||
220℃/10 kg | *** g/10 min | ISO 1133 | |
230°C/3.8 kg | *** g/10 min | ISO 1133 | |
Mold Shrinkage | |||
Flow | *** % | ISO 294-4 | |
Across Flow | *** % | ISO 294-4 | |
Bulk(Apparent ) Density | *** g/cm³ | ISO 60 | |
| Mechanical | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Tensile Modulus | *** Mpa | ISO 527-2 | |
Tensile Strength | |||
Yield | *** Mpa | ISO 527-2/50 | |
Tensile Elongation | |||
Yield | *** % | ISO 527-2/50 | |
Flexural Modulus | *** Mpa | ISO 178 | 2.0 mm/min |
Flexural Strength | |||
- | *** Mpa | ISO 178 | 2.0 mm/min |
| Impact | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Charpy Notched Impact Strengh | |||
-30℃ (-22℉) | *** kJ/m² | ISO 179/1eA | |
23℃ (73℉) | *** kJ/m² | ISO 179/1eA | |
Izod Notched Impact Strengh | |||
-30℃ (-22℉) | *** kJ/m² | ISO 180/A | |
23℃ (73℉) | *** kJ/m² | ISO 180/A | |
| Thermal | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Heat Deflection Temperature(HDT) | |||
1.8 Mpa (264 psi)（18.6kg/cm²） | *** °C | ISO 75-2/A | Unannealed |
Vicat Softening Temperature(VST) | *** °C | ISO 306/B50 | |
| Flammability | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Burning Rate | *** mm/min | ISO 3795 | 2 mm |
| Additional Information | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Fogging | |||
- | *** % | ISO 6452 | 100°C |
Volatile Organic Compounds | *** µg/g | VDA 277 |
The information presented on this datasheet was acquired by AjiEng.com from the producer of the material. AjiEng.com makes substantial efforts to assure the accuracy of this data. However, AjiEng.com assumes no responsibility for the data values and strongly encourages that upon final material selection, data points are validated with the material supplier.