MAGNUM™ 3416SLG is a high-heat ABS. Its very low gloss properties combined with a high flow makes it specifically suitable for unpainted interior automotive applications. MAGNUM™ 3416SLG can thereby help you to save up to 50% of the part costs. It is globally available, locally produced in major car production regions.
Benefits:
Lot to lot consistency allowing for optimal machine parameters settings from the start
Self-coloring enabling improvement of costs by using less pigments and lowering your logistic costs
Low VOC allowing a better interior air quality facing increasing regulatory and OEMs constraints.
Heat stability during wide range of processing temperatures: enhanced part design freedom
High scratch and mar resistance for an improved aesthetic durability of the parts
Easier recyclability of unpainted part
Applications:
Unpainted interior automotive applications
Mid-consoles
Door panels
Door handles
Door armrests
Pillars
| Original Document | Technical Datasheet-ISO(English) | |||
| Features | Heat StabilizedLow GlossAnti-ScratchLow EmissionHigh Flow | |||
| Applications | Car pillarsAutomotive Door HandlesAutomotive ConsolesAutomotive Interior PartsAutomotive Door panelsAutomotive Door armrests | |||
| Markets | Automotive | |||
| Processing | Injection | |||
| Automotive Specs | Audi TL 527 AAudi TL 527 BVAG(Volkswagen Group) TL 527 AVAG(Volkswagen Group) TL 527 BGM(General Motors) GMW15572P-ABS-T2 Color: Jet BlackGM(General Motors) GMW15572P-ABS-T1 Color: Jet Black | |||
| Physical | Value/Unit(Sign in to View) | Test Standard | Test Condition |
|---|---|---|---|
Density/Specific Gravity | *** g/cm³ | ISO 1183 | |
Melt Mass Flow Rate(MFR) | |||
220℃/10 kg | *** g/10 min | ISO 1133 | |
Mold Shrinkage | |||
Flow | ***~*** % | ISO 294-4 | |
Bulk(Apparent ) Density | *** g/cm³ | ISO 60 | |
| Mechanical | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Tensile Modulus | *** Mpa | ISO 527-2 | |
Tensile Strength | |||
Yield | *** Mpa | ISO 527-2/50 | |
Tensile Elongation | |||
Break | *** % | ISO 527-2/50 | |
Flexural Modulus | *** Mpa | ISO 178 | 2.0 mm/min |
Flexural Strength | |||
- | *** Mpa | ISO 178 | 2.0 mm/min |
| Impact | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Charpy Notched Impact Strengh | |||
-30℃ (-22℉) | *** kJ/m² | ISO 179/1eA | |
23℃ (73℉) | *** kJ/m² | ISO 179/1eA | |
| Thermal | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Heat Deflection Temperature(HDT) | |||
1.8 Mpa (264 psi)（18.6kg/cm²） | *** °C | ISO 75-2/A | Unannealed |
Vicat Softening Temperature(VST) | *** °C | ISO 306/B50 |
The information presented on this datasheet was acquired by AjiEng.com from the producer of the material. AjiEng.com makes substantial efforts to assure the accuracy of this data. However, AjiEng.com assumes no responsibility for the data values and strongly encourages that upon final material selection, data points are validated with the material supplier.