EMERGE™ PC 8600 is translucent, ignition-resistant polycarbonate resin. This resin contains no bromine, chlorine or phosphate additives and is intended to comply with global environmental standards. It is an easy flow PC resin suitable for use in injection molded applications in the computer, electronics, electrical, and information technology equipment markets.
Applications:
Information technology equipment
Electronics and electrical appliances
Battery chargers and adaptors
| Original Document | Technical Datasheet(English) | |||
| Features | Flame RetardantCl- FreeBr- FreeNon Red PhosphorusHigh Flow | |||
| Processing | Injection | |||
| Physical | Value/Unit(Sign in to View) | Test Standard | Test Condition |
|---|---|---|---|
Density/Specific Gravity | *** g/cm³ | ISO 1183 | |
Density/Specific Gravity | *** g/cm³ | ASTM D792 | |
Melt Mass Flow Rate(MFR) | |||
300℃/1.2 kg | *** g/10min | ASTM D1238 | |
300℃/1.2 kg | *** g/10min | ISO 1133 | |
Mold Shrinkage | |||
Flow | ***~*** % | ASTM D955 | |
Flow | ***~*** % | ISO 294-4 | |
| Mechanical | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Tensile Modulus | *** Mpa | ASTM D638 | 3.20 mm,Injection Molded |
Tensile Modulus | *** Mpa | ISO 527-2/50 | 4.00 mm,Injection Molded |
Tensile Strength | |||
Yield | *** Mpa | ASTM D638 | 3.20 mm,Injection Molded |
Yield | *** Mpa | ISO 527-2/50 | 4.00 mm,Injection Molded |
Break | *** Mpa | ASTM D638 | 3.20 mm,Injection Molded |
Break | *** Mpa | ISO 527-2/50 | 4.00 mm,Injection Molded |
Tensile Elongation | |||
Yield | *** % | ASTM D638 | 3.20 mm,Injection Molded |
Yield | *** % | ISO 527-2/50 | 4.00 mm,Injection Molded |
Break | *** % | ASTM D638 | 3.20 mm,Injection Molded |
Break | *** % | ISO 527-2/50 | 4.00 mm,Injection Molded |
Flexural Modulus | *** Mpa | ASTM D790 | 3.20 mm,Injection Molded |
Flexural Modulus | *** Mpa | ISO 178 | 4.00 mm,Injection Molded |
Flexural Strength | |||
- | *** Mpa | ASTM D790 | 3.20 mm,Injection Molded |
- | *** Mpa | ISO 178 | 4.00 mm,Injection Molded |
| Impact | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Izod Notched Impact Strengh | |||
23℃ (73℉) | *** J/m | ASTM D256 | 3.20 mm,Injection Molded |
23℃ (73℉) | *** kJ/m² | ISO 180/A | |
Instrumented Impact Energy | |||
23℃ (73℉)Total Energy | *** J | ASTM D3763 | 3.20 mm |
| Hardness | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Rockwell R | *** R | ASTM D785 | 3.20 mm,Injection Molded |
Rockwell R | *** R | ISO 2039-2 | 4.00 mm |
| Thermal | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Heat Deflection Temperature(HDT) | |||
0.45 Mpa (66 psi)（4.6kg/cm²） | *** °C | ASTM D648 | Unannealed |
0.45 Mpa (66 psi)（4.6kg/cm²） | *** °C | ISO 75-2/B | Unannealed |
1.8 Mpa (264 psi)（18.6kg/cm²） | *** °C | ASTM D648 | Unannealed |
1.8 Mpa (264 psi)（18.6kg/cm²） | *** °C | ISO 75-2/A | Unannealed |
Vicat Softening Temperature(VST) | *** °C | ASTM D1525 | Rate B (120°C/h), Loading 1 (10 N) |
Vicat Softening Temperature(VST) | *** °C | ISO 306 | A120 |
Vicat Softening Temperature(VST) | *** °C | ISO 306/B50 | |
Relative Temperature Index(RTI), Imp | |||
- | *** °C | UL 746 | |
Relative Temperature Index(RTI), Elec | |||
- | *** °C | UL 746 | |
Relative Temperature Index(RTI), Str | |||
- | *** °C | UL 746 | |
Coefficient of Linear Thermal Expansion | |||
Flow | *** E-6 cm/cm/℃ | ASTM D 696 | -22 to 85°C |
Ball Pressure Test | *** °C | IEC 60335-1 | |
| Flammability | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Flame Rating | |||
V-0 | *** mm | UL94 | |
Oxygen Index | *** % | ASTM D 2863 | |
Oxygen Index | *** % | ISO 4589 | |
Glow Wire Ignition Test(GWIT) | |||
2.0mm | *** °C | IEC 60695-2-13 |
The information presented on this datasheet was acquired by AjiEng.com from the producer of the material. AjiEng.com makes substantial efforts to assure the accuracy of this data. However, AjiEng.com assumes no responsibility for the data values and strongly encourages that upon final material selection, data points are validated with the material supplier.