EMERGE™ PC 8130 Advanced Resin is an ignition-resistant polycarbonate resin with improved UV stability. It is designed for thin-wall applications and has a UL94 V-0 rating at 1.0 mm. EMERGE PC 8130 is also f1 rated according to UL 746C. This resin does not contain chlorine or bromine additives.
Main Characteristics:
Ignition resistant
UV resistant
Applications:
Powered Device Housings
Information technology equipment
Electrical parts
| Original Document | Technical Datasheet-ASTM(English) | |||
| Features | Flame RetardantCl- FreeBr- FreeUV Stabiltiy | |||
| Additive | Flame RetardantUV-Stabilizer | |||
| Physical | Value/Unit(Sign in to View) | Test Standard | Test Condition |
|---|---|---|---|
Density/Specific Gravity | *** g/cm³ | ASTM D792 | |
Melt Mass Flow Rate(MFR) | |||
300℃/1.2 kg | *** g/10min | ASTM D1238 | |
Mold Shrinkage | |||
Flow | ***~*** % | ASTM D955 | |
Outdoor Suitability UL F1/F2 | |||
F1 | *** - | UL 746C | |
Water Absorption | *** % | ASTM D570 | 24 hr, 23°C |
| Mechanical | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Tensile Modulus | *** Mpa | ASTM D638 | |
Tensile Strength | |||
Yield | *** Mpa | ASTM D638 | |
Yield | *** Mpa | ISO 527-2/50 | |
Break | *** Mpa | ASTM D638 | |
Break | *** Mpa | ISO 527-2/50 | |
Tensile Elongation | |||
Yield | *** % | ASTM D638 | |
Break | *** % | ASTM D638 | |
Flexural Modulus | *** Mpa | ASTM D790 | |
Flexural Strength | |||
- | *** Mpa | ASTM D790 | |
| Impact | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Izod Notched Impact Strengh | |||
23℃ (73℉) | *** J/m | ASTM D256 | |
Instrumented Impact Energy | |||
23℃ (73℉)Total Energy | *** J | ASTM D3763 | |
Tensile Impact | *** kJ/m² | ASTM D 1822 | |
| Thermal | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Heat Deflection Temperature(HDT) | |||
0.45 Mpa (66 psi)（4.6kg/cm²） | *** °C | ASTM D648 | Unannealed, 6.40 mm |
1.8 Mpa (264 psi)（18.6kg/cm²） | *** °C | ASTM D648 | Unannealed, 6.40 mm |
Vicat Softening Temperature(VST) | *** °C | ASTM D1525 | |
Relative Temperature Index(RTI), Imp | |||
- | *** °C | UL 746 | |
Relative Temperature Index(RTI), Elec | |||
- | *** °C | UL 746 | |
Relative Temperature Index(RTI), Str | |||
- | *** °C | UL 746 | |
Coefficient of Linear Thermal Expansion | |||
Flow | *** E-6 cm/cm/℃ | ASTM D 696 | |
| Flammability | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Flame Rating | |||
V-1 | *** mm | UL94 | all |
V-0 | *** mm | Internal | all |
V-0 | *** mm | Internal | wt, black |
5VB | *** mm | UL94 | all |
5VA | *** mm | UL94 | all |
| Electrical | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Comparative Tracking Index (CTI) | |||
- | *** PLC | UL 746 | |
Arc Resistance | *** PLC | ASTM D495 | |
Hot Wire Ignition(HWI) | *** PLC | UL 746 | 0.9 to 3.0 mm |
High Ampere Arc Ignition(HAI) | *** PLC | UL 746 | 0.9mm |
High Ampere Arc Ignition(HAI) | *** PLC | UL 746 | 1.0 to 3.0 mm |
High Voltage Arc Resistance to Ignition(HVAR) | *** PLC | UL 746 |
The information presented on this datasheet was acquired by AjiEng.com from the producer of the material. AjiEng.com makes substantial efforts to assure the accuracy of this data. However, AjiEng.com assumes no responsibility for the data values and strongly encourages that upon final material selection, data points are validated with the material supplier.