CALIBRE™ 603-6 Polycarbonate Resin is a branched polycarbonate resin specially designed for multi-wall sheet extrusion. CALIBRE 603-6 offers a high melt strength to calibrate effectively a wide range of multi-wall sheet structures from low to high complexity, such as seven wall sheet. CALIBRE 603-6 offers a wider processing window than CALIBRE 503-5 and is likewise specially designed to give excellent sheet surface quality at high line speeds with a reduced tendency to display chatter marks. CALIBRE 603-6 contains a UV absorber additive, but sheets for outdoor applications require a protective UV-absorbing cap layer. It is recommended to coextrude a 50 micron thick cap layer from CALIBRE 320UV.
Main Characteristics:
Wide processing window
High surface quality
Minimizes chatter marks
Applications:
Low to high complexity multi-wall sheets
| Original Document | Technical Datasheet-ISO(English) | |||
| Features | Good SurfaceUV StabiltiyHigh melt strength | |||
| Additive | UV-Stabilizer | |||
| Processing | ExtrusionSheet Extrusion | |||
| Physical | Value/Unit(Sign in to View) | Test Standard | Test Condition |
|---|---|---|---|
Density/Specific Gravity | *** g/cm³ | ISO 1183 | |
Melt Mass Flow Rate(MFR) | |||
300℃/1.2 kg | *** g/10min | ISO 1133 | |
Mold Shrinkage | |||
Flow | ***~*** % | ISO 294-4 | |
Water Absorption | *** % | ISO 62 | 24 hr, 23°C |
Water Absorption | *** % | ISO 62 | Equilibrium, 23°C, 50% RH |
| Mechanical | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Tensile Modulus | *** Mpa | ISO 527-2/50 | |
Tensile Strength | |||
Yield | *** Mpa | ISO 527-2/50 | |
Break | *** Mpa | ISO 527-2/50 | |
Tensile Elongation | |||
Yield | *** % | ISO 527-2/50 | |
Flexural Modulus | *** Mpa | ISO 178 | 2.0 mm/min |
Flexural Strength | |||
- | *** Mpa | ISO 178 | 2.0 mm/min |
| Impact | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Charpy Notched Impact Strengh | |||
-30℃ (-22℉) | *** kJ/m² | ISO 179/1eA | |
23℃ (73℉) | *** kJ/m² | ISO 179/1eA | |
Izod Notched Impact Strengh | |||
-30℃ (-22℉) | *** kJ/m² | ISO 180/A | |
23℃ (73℉) | *** kJ/m² | ISO 180/A | |
| Thermal | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Heat Deflection Temperature(HDT) | |||
0.45 Mpa (66 psi)（4.6kg/cm²） | *** °C | ISO 75-2/B | Annealed |
1.8 Mpa (264 psi)（18.6kg/cm²） | *** °C | ISO 75-2/A | Annealed |
1.8 Mpa (264 psi)（18.6kg/cm²） | *** °C | ISO 75-2/A | Unannealed |
Vicat Softening Temperature(VST) | *** °C | ISO 306/B50 | |
Coefficient of Linear Thermal Expansion | |||
Flow | *** E-6 cm/cm/℃ | ISO 11359-2 | |
| Flammability | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Flame Rating | |||
HB | *** mm | UL94 | |
HB | *** mm | UL94 | |
Glow Wire Flammability Index(GWFI) | |||
1mm | *** °C | IEC 60695-2-12 | |
2mm | *** °C | IEC 60695-2-12 | |
3mm | *** °C | IEC 60695-2-12 | |
Glow Wire Ignition Test(GWIT) | |||
1.0mm | *** °C | IEC 60695-2-13 | |
2.0mm | *** °C | IEC 60695-2-13 | |
3.0mm | *** °C | IEC 60695-2-13 | |
| Electrical | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Comparative Tracking Index (CTI) | |||
Solution A | *** V | IEC 60112 | 2.0 mm |
| Optical | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Light Transmission | ***~*** % | ASTM D1003 | |
Haze | *** % | ASTM D1003 | |
Refractive Index | *** - | ISO 489 |
The information presented on this datasheet was acquired by AjiEng.com from the producer of the material. AjiEng.com makes substantial efforts to assure the accuracy of this data. However, AjiEng.com assumes no responsibility for the data values and strongly encourages that upon final material selection, data points are validated with the material supplier.