CALIBRE™ 603-3 is a branched polycarbonate resin specially designed for extrusion of profiles, corrugated sheet and very complex multi-wall sheet. CALIBRE™ 603-3 offers a very high melt strength to calibrate effectively the most complex multi-wall sheet structures, such as a seven wall sheet or more, and to calibrate effectively complex profiles and corrugated sheet. CALIBRE™ 603-3 contains a UV absorber additive, but note that sheets for outdoor applications also require a protective UV-absorbing cap layer. It is recommended to coextrude a 50 µm thick cap layer, using CALIBRE™ 320UV.
Main Characteristics:
Very high melt strength
Good impact resistance
Applications:
Complex multi-wall sheet
Profiles
| Original Document | Technical Datasheet-ISO(English) | |||
| Features | UV StabiltiyHigh melt strength | |||
| Additive | UV-Stabilizer | |||
| Processing | ExtrusionSheet Extrusion | |||
| Physical | Value/Unit(Sign in to View) | Test Standard | Test Condition |
|---|---|---|---|
Density/Specific Gravity | *** g/cm³ | ISO 1183 | |
Melt Mass Flow Rate(MFR) | |||
300℃/1.2 kg | *** g/10min | ISO 1133 | |
Mold Shrinkage | |||
Flow | ***~*** % | ISO 294-4 | |
Water Absorption | *** % | ISO 62 | 24 hr, 23°C |
Water Absorption | *** % | ISO 62 | Equilibrium, 23°C, 50% RH |
| Mechanical | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Tensile Modulus | *** Mpa | ISO 527-2/50 | |
Tensile Strength | |||
Yield | *** Mpa | ISO 527-2/50 | |
Break | *** Mpa | ISO 527-2/50 | |
Tensile Elongation | |||
Yield | *** % | ISO 527-2/50 | |
Break | *** % | ISO 527-2/50 | |
Flexural Modulus | *** Mpa | ISO 178 | 2.0 mm/min |
Flexural Strength | |||
- | *** Mpa | ISO 178 | 2.0 mm/min |
| Impact | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Charpy Notched Impact Strengh | |||
-30℃ (-22℉) | *** kJ/m² | ISO 179/1eA | |
23℃ (73℉) | *** kJ/m² | ISO 179/1eA | |
Izod Notched Impact Strengh | |||
-30℃ (-22℉) | *** kJ/m² | ISO 180/A | |
23℃ (73℉) | *** kJ/m² | ISO 180/A | |
| Thermal | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Heat Deflection Temperature(HDT) | |||
0.45 Mpa (66 psi)（4.6kg/cm²） | *** °C | ISO 75-2/B | Annealed |
1.8 Mpa (264 psi)（18.6kg/cm²） | *** °C | ISO 75-2/A | Annealed |
1.8 Mpa (264 psi)（18.6kg/cm²） | *** °C | ISO 75-2/A | Unannealed |
Vicat Softening Temperature(VST) | *** °C | ISO 306/B50 | |
Coefficient of Linear Thermal Expansion | |||
Flow | *** E-6 cm/cm/℃ | ISO 11359-2 | |
| Flammability | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Flame Rating | |||
HB | *** mm | UL94 | |
HB | *** mm | UL94 | |
Glow Wire Flammability Index(GWFI) | |||
1mm | *** °C | IEC 60695-2-12 | |
2mm | *** °C | IEC 60695-2-12 | |
3mm | *** °C | IEC 60695-2-12 | |
Glow Wire Ignition Test(GWIT) | |||
1.0mm | *** °C | IEC 60695-2-13 | |
2.0mm | *** °C | IEC 60695-2-13 | |
3.0mm | *** °C | IEC 60695-2-13 | |
| Electrical | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Comparative Tracking Index (CTI) | |||
Solution A | *** V | IEC 60112 | 2.0 mm |
| Optical | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Light Transmission | *** % | ASTM D1003 | |
Haze | *** % | ASTM D1003 | |
Refractive Index | *** - | ISO 489 |
The information presented on this datasheet was acquired by AjiEng.com from the producer of the material. AjiEng.com makes substantial efforts to assure the accuracy of this data. However, AjiEng.com assumes no responsibility for the data values and strongly encourages that upon final material selection, data points are validated with the material supplier.