CALIBRE™ 5101 Polycarbonate resin is 10% glass-reinforced and provides increased modulus and improved heat distortion resistance with minimal shrinkage. This resin offers outstanding UL94 flammability ratings and contains mold release. CALIBRE 5101 is available in 8 and 15 melt flow rates. CALIBRE 5101 resin has undergone biocompatibility testing based on ISO 10993 (Biological Evaluation of Medical Devices) and is suitable for use in approved medical applications.
Main Characteristics:
Glass reinforced
Ignition resistant
Tested under ISO 10993
Applications
Information Technology Equipment
Telecommunications
Medical applications
| Original Document | Technical Datasheet(English) | |||
| Features | Flame RetardantMold ReleaseMedical Application/Health CareBiocompatibleFilled & Reinforced | |||
| Additive | Release Agent | |||
| Compliance | ISO10993 | |||
| Reinforced | 10% Glass Fiber | |||
| Physical | Value/Unit(Sign in to View) | Test Standard | Test Condition |
|---|---|---|---|
Density/Specific Gravity | *** g/cm³ | ISO 1183 | |
Density/Specific Gravity | *** g/cm³ | ASTM D792 | |
Melt Mass Flow Rate(MFR) | |||
300℃/1.2 kg | *** g/10min | ASTM D1238 | |
300℃/1.2 kg | *** g/10min | ISO 1133 | |
Mold Shrinkage | |||
Flow | ***~*** % | ASTM D955 | |
Flow | ***~*** % | ISO 294-4 | |
Water Absorption | *** % | ASTM D570 | 24 hr, 23°C |
Water Absorption | *** % | ASTM D570 | Equilibrium, 23°C, 50% RH |
Water Absorption | *** % | ISO 62 | 24 hr, 23°C |
Water Absorption | *** % | ISO 62 | Equilibrium, 23°C, 50% RH |
| Mechanical | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Tensile Modulus | *** Mpa | ASTM D638 | 50 mm/min |
Tensile Modulus | *** Mpa | ISO 527-2/50 | |
Tensile Strength | |||
Yield | *** Mpa | ASTM D638 | 50 mm/min |
Yield | *** Mpa | ISO 527-2/50 | |
Break | *** Mpa | ASTM D638 | 50 mm/min |
Break | *** Mpa | ISO 527-2/50 | |
Tensile Elongation | |||
Break | *** % | ASTM D638 | 50 mm/min |
Break | *** % | ISO 527-2/50 | |
Flexural Modulus | *** Mpa | ASTM D790 | 2.0 mm/min |
Flexural Modulus | *** Mpa | ISO 178 | 2.0 mm/min |
Flexural Strength | |||
- | *** Mpa | ASTM D790 | 2.0 mm/min |
- | *** Mpa | ISO 178 | 2.0 mm/min |
| Impact | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Izod Notched Impact Strengh | |||
23℃ (73℉) | *** J/m | ASTM D256 | |
Instrumented Impact Energy | |||
23℃ (73℉)Total Energy | *** J | ASTM D3763 | 3.39 m/sec |
Tensile Impact | *** kJ/m² | ASTM D 1822 | |
| Hardness | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Rockwell M | *** M | ASTM D 785 | |
Rockwell R | *** R | ASTM D785 | |
| Thermal | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Heat Deflection Temperature(HDT) | |||
0.45 Mpa (66 psi)（4.6kg/cm²） | *** °C | ASTM D648 | Annealed |
0.45 Mpa (66 psi)（4.6kg/cm²） | *** °C | ISO 75-2/B | Annealed |
1.8 Mpa (264 psi)（18.6kg/cm²） | *** °C | ASTM D648 | Unannealed |
1.8 Mpa (264 psi)（18.6kg/cm²） | *** °C | ISO 75-2/A | Unannealed |
Vicat Softening Temperature(VST) | *** °C | ASTM D1525 | Rate A (50°C/h), Loading 2 (50 N) |
Vicat Softening Temperature(VST) | *** °C | ISO 306/B50 | |
Coefficient of Linear Thermal Expansion | |||
Flow | *** E-6 cm/cm/℃ | ASTM D 696 | -40 to 82°C |
| Flammability | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Flame Rating | |||
V-2 | *** mm | UL94 | |
V-0 | *** mm | UL94 | |
Oxygen Index | *** % | ISO 4589 | |
Burning Rate | *** mm | ASTM D 635 |
The information presented on this datasheet was acquired by AjiEng.com from the producer of the material. AjiEng.com makes substantial efforts to assure the accuracy of this data. However, AjiEng.com assumes no responsibility for the data values and strongly encourages that upon final material selection, data points are validated with the material supplier.