Unreinforced, low viscosity injection moulding grade, flows very readily.
| Original Document | Technical Datasheet-ISO(English) | |||
| Resin ID | PESU | |||
| Availability | AsiaEuropeNorth AmericaMiddle EastAfricaSouth & Central America | |||
| Features | High FlowLow viscosity | |||
| Processing | Injection | |||
| Diagrams | Viscosity-shear rateShearstress-shear rateStress-strain (Cond.)Secant modulus-strain (Cond.)Specific volume-temperature (pvT)Tensile modulus-temperature (cond.) | |||
| Physical | Value/Unit(Sign in to View) | Test Standard | Test Condition |
|---|---|---|---|
Density/Specific Gravity | *** g/cm³ | ISO 1183 | |
Melt Volume Flow Rate(MVR) | |||
360°C/10 kg | *** cm³/10 min | ISO 1133 | |
Mold Shrinkage | |||
Flow | *** % | ISO 294-4 | |
Across Flow | *** % | ISO 294-4 | |
Water Absorption | *** % | ISO 62 | equilibrium 23°C/50% r.h. |
Water Absorption | *** % | ISO 62 | equilibrium in water at 23°C |
Viscosity | *** cm³/g | ISO 307, 1157, 1628 | in 0,01 g/ml Phenol/1,2, ortho-Dichlorbenzol, 1:1 |
| Mechanical | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Tensile Modulus | *** Mpa | ISO 527-1/-2 | |
Tensile Strength | |||
Yield | *** Mpa | ISO 527-1/-2 | 50 mm/min |
Tensile Elongation | |||
Yield | *** % | ISO 527-1/-2 | 50 mm/min |
| Impact | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Charpy Notched Impact Strengh | |||
-30℃ (-22℉) | *** kJ/m² | ISO 179/1eA | |
23℃ (73℉) | *** kJ/m² | ISO 179/1eA | |
Charpy Unnotched Impact Strengh | |||
-30℃ (-22℉) | *** kJ/m² | ISO 179/1eU | |
23℃ (73℉) | *** kJ/m² | ISO 179/1eU | |
Izod Notched Impact Strengh | |||
-30℃ (-22℉) | *** kJ/m² | ISO 180/A | |
23℃ (73℉) | *** kJ/m² | ISO 180/A | |
| Hardness | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Ball Indentation Hardness | *** Mpa | ISO 2039-1 | at 358 N and 30 s |
| Thermal | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Heat Deflection Temperature(HDT) | |||
1.8 Mpa (264 psi)（18.6kg/cm²） | *** °C | ISO 75-1/-2 | |
Coefficient of Linear Thermal Expansion | |||
Flow | *** E-6/K | ISO 11359-1/-2 | 23-80℃ |
Flow | *** E-6/K | DIN 53752 | 180℃ |
Glass Transition Temperature | *** °C | ISO 11357-1/-2 | 10°C/min |
Temperature at Short Circle Operation | *** °C | - | |
Processing Temperature | ***~*** °C | - | injection moulding |
Mould temperature | ***~*** °C | - | injection moulding |
Temperature index (TI)-Tensile Strength | |||
20000 h | *** °C | IEC 60216 | |
| Flammability | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Flame Rating | |||
V-1 | *** mm | IEC 60695-11-10 | |
V-0 | *** mm | IEC 60695-11-10 | |
| Electrical | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Volume Resistivity | *** Ohm-m | IEC 62631-3-1 | |
Surface Resistivity | *** Ohm | IEC 62631-3-2 | |
Dielectric Constant(Permittivity) | |||
100Hz | *** - | IEC 62631-2-1 | |
1MHz | *** - | IEC 62631-2-1 | |
Dissipation Factor | |||
100Hz | *** E-4 | IEC 62631-2-1 | |
1MHz | *** E-4 | IEC 62631-2-1 | |
Comparative Tracking Index (CTI) | |||
Solution A | *** V | IEC 60112 | |
Solution B | *** V | IEC 60112 | |
Dielectric Strength | *** kV/mm | IEC 60243-1 | K20/K20 |
| Optical | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Light Transmission | *** % | DIN 5036-3 | thickness = 2 mm |
Refractive Index | *** - | ISO 489 | thickness = 1 mm |
The information presented on this datasheet was acquired by AjiEng.com from the producer of the material. AjiEng.com makes substantial efforts to assure the accuracy of this data. However, AjiEng.com assumes no responsibility for the data values and strongly encourages that upon final material selection, data points are validated with the material supplier.