Ultraform N 2310 P Q600 is a general-purpose injection molding POM grade containing special lubricant. Low frictional coefficient giving extremely low wear with otherwise unaltered mechanical properties.
Applications
Typical applications include spring elements, clips, gears and other applications requiring low friction and wear.
| Original Document | Technical Datasheet-ISO(English) Technical Datasheet-ASTM(English) | |||
| Features | Wear/Abrasion ResistanceLow Friction/WearCopolymer | |||
| Additive | Lubricant | |||
| Processing | Injection | |||
| Physical | Value/Unit(Sign in to View) | Test Standard | Test Condition |
|---|---|---|---|
Density/Specific Gravity | *** g/cm³ | ISO 1183 | |
Density/Specific Gravity | *** g/cm³ | ASTM D792 | |
Melt Volume Flow Rate(MVR) | |||
190℃/2.16 kg | *** cm³/10min | ISO 1133 | |
Mold Shrinkage | |||
Flow | *** % | ISO 294-4 | |
Across Flow | *** % | ISO 294-4 | |
- | *** % | Internal | |
Water Absorption | *** % | ASTM D570 | 50% RH |
Water Absorption | *** % | ASTM D570 | Saturation |
Water Absorption | *** % | ISO 62 | 50% RH |
Water Absorption | *** % | ISO 62 | Saturation |
| Mechanical | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Tensile Modulus | *** Mpa | ISO 527 | 23℃ |
Tensile Strength | |||
Yield | *** Mpa | ASTM D638 | 23℃ |
Yield | *** Mpa | ISO 527 | 23℃ |
Tensile Elongation | |||
Yield | *** % | ASTM D638 | 23℃ |
Yield | *** % | ISO 527 | 23℃ |
Nominal Tensile Strain at Break | *** % | ISO 527 | 23℃ |
Flexural Modulus | *** Mpa | ASTM D790 | 23℃ |
Tensile Creep Modulus | |||
1h | *** Mpa | ISO 899 | |
1000h | *** Mpa | ISO 899 | |
| Impact | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Charpy Notched Impact Strengh | |||
23℃ (73℉) | *** kJ/m² | ISO 179 | |
Charpy Unnotched Impact Strengh | |||
-30℃ (-22℉) | *** kJ/m² | ISO 179 | |
23℃ (73℉) | *** kJ/m² | ISO 179 | |
Izod Notched Impact Strengh | |||
-40℃ (-40℉) | *** J/m | ASTM D256 | |
23℃ (73℉) | *** J/m | ASTM D256 | |
| Hardness | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Rockwell R | *** R | ASTM D785 | |
| Thermal | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Heat Deflection Temperature(HDT) | |||
0.45 Mpa (66 psi)（4.6kg/cm²） | *** °C | ASTM D648 | |
0.45 Mpa (66 psi)（4.6kg/cm²） | *** °C | ISO 75 | |
1.8 Mpa (264 psi)（18.6kg/cm²） | *** °C | ASTM D648 | |
1.8 Mpa (264 psi)（18.6kg/cm²） | *** °C | ISO 75 | |
Coefficient of Linear Thermal Expansion | |||
Flow | *** E-6/°C | Internal | |
- | *** E-6/°C | ASTM D E831 | |
Melt Temperature(Tm) | *** °C | ASTM D3418 | |
Melt Temperature(Tm) | *** °C | ISO 3146 | |
| Electrical | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Volume Resistivity | *** Ohm-cm | ASTM D257 | 1.5 mm |
Volume Resistivity | *** Ohm-cm | IEC 60093 | |
Surface Resistivity | *** Ohm | ASTM D257 | 1.5 mm |
Surface Resistivity | *** Ohm | IEC 60093 | |
Dielectric Constant(Permittivity) | |||
100Hz | *** - | IEC 60250 | |
1MHz | *** - | IEC 60250 | |
Dissipation Factor | |||
100Hz | *** E-4 | IEC 60250 | |
1MHz | *** E-4 | IEC 60250 | |
Comparative Tracking Index (CTI) | |||
- | *** V | IEC 60112 | |
Dielectric Strength | *** kV/mm | IEC 60243-1 |
The information presented on this datasheet was acquired by AjiEng.com from the producer of the material. AjiEng.com makes substantial efforts to assure the accuracy of this data. However, AjiEng.com assumes no responsibility for the data values and strongly encourages that upon final material selection, data points are validated with the material supplier.