Technical Datasheet-ISO(English) 

Technical Datasheet-ASTM(English) 

Technical Datasheet(English) 

(PBT+ASA+PET)-GF20

Good Surface

Low Warpage

ESCR

Chemical Resistance

Filled & Reinforced

Housings

Connectors

Viscosity-shear rate 255|1/s|Pa s|Shear rate in 1/s|Viscosity in Pa s|11.9:788.8@27.6:587.101@63.8:430.799@147.5:309.6@341:216.2@788.3:145.2@1822.4:92.90000000000001@4213.1:55.8@9739.799999999999:31.1@22516.2:15.9{n}265|1/s|Pa s|Shear rate in 1/s|Viscosity in Pa s|18.3:514.6@42.3:383@97.8:281.1@226.1:202@522.6:141.1@1208.2:94.7997@2793.2:60.6@6457.3:36.4@14927.8:20.3@34509.9:10.3{n}275|1/s|Pa s|Shear rate in 1/s|Viscosity in Pa s|27.1:347.1@62.7:258.4@145:189.6@335.2:136.3@774.8:95.09999999999999@1791.2:63.9002@4140.9:40.9@9572.9:24.6@22130.4:13.7@51160.8:7.00001

Shearstress-shear rate 255|1/s|Pa|Shear rate in 1/s|Shearstress in Pa|11.9:9386.719999999999@27.6:16204@63.8:27485@147.5:45666@341:73724.2@788.3:114461@1822.4:169301@4213.1:235091@9739.799999999999:302908@22516.2:358008{n}265|1/s|Pa|Shear rate in 1/s|Shearstress in Pa|18.3:9417.18@42.3:16200.9@97.8:27491.6@226.1:45672.2@522.6:73738.89999999999@1208.2:114537@2793.2:169268@6457.3:235046@14927.8:303034@34509.9:355452{n}275|1/s|Pa|Shear rate in 1/s|Shearstress in Pa|27.1:9406.41@62.7:16201.7@145:27492@335.2:45687.8@774.8:73683.5@1791.2:114458@4140.9:169363@9572.9:235493@22130.4:303186@51160.8:358126

Dynamic Shear modulus-temperature G'|°C|MPa|Temperature in °C|Dyn. Shear modulus in MPa|-50:1689.2@-40:1585.5@-30:1538.3@-20:1511.3@-10:1492.6@0:1471.5@10:1449.9@20:1424.2@30:1398.3@40:1331.3@50:1066.3@60:810.2@70:664.3@80:583.5@90:532.3@100:482.1@110:389.4@120:251.9@130:211.7@140:194.7@150:179.9@160:166@170:152@180:138.4@190:124.7@200:108.7@210:88.59999999999999@220:58.8@230:10@240:0.6{n}G"|°C|MPa|Temperature in °C|Dyn. Shear modulus in MPa|-50:48.2604@-40:35.2774@-30:22.4746@-20:17.123@-10:14.5976@0:13.2876@10:12.6286@20:12.5614@30:13.5495@40:22.9516@50:66.0253@60:69.40170000000001@70:52.4996@80:39.5263@90:32.9387@100:32.7973@110:49.5317@120:34.0065@130:13.6906@140:9.779780000000001@150:8.467890000000001@160:7.80864@170:7.334@180:7.01411@190:6.73754@200:6.52961@210:6.66006@220:6.0564@230:2.992@240:0.32988{n}tan d|°C|MPa|Temperature in °C|Dyn. Shear modulus in MPa|-50:0.02857@-40:0.02225@-30:0.01461@-20:0.01133@-10:0.00978@0:0.00903@10:0.008710000000000001@20:0.00882@30:0.009690000000000001@40:0.01724@50:0.06192@60:0.08566@70:0.07903@80:0.06773999999999999@90:0.06188@100:0.06802999999999999@110:0.1272@120:0.135@130:0.06467000000000001@140:0.05023@150:0.04707@160:0.04704@170:0.04825@180:0.05068@190:0.05403@200:0.06007@210:0.07517@220:0.103@230:0.2992@240:0.5498

Stress-strain(Break) -40|%|Mpa|Strain in %|Stress in MPa|0:0@0.27:22.23@0.54:44.38@0.8100000000000001:65.38@1.08:84.63@1.35:101.84@1.62:117.02@1.89:130.3@2.16:141.85@2.43:151.81@2.7:160.14{n}-20|%|Mpa|Strain in %|Stress in MPa|0:0@0.5600000000000001:42.45@0.84:62.39@1.12:80.34@1.4:96.06@1.68:109.58@1.96:121.12@2.24:130.93@2.52:139.11@2.8:145.53{n}23|%|Mpa|Strain in %|Stress in MPa|0:0@0.26:18.61@0.52:37.12@0.78:54.08@1.04:68.77@1.3:80.98999999999999@1.56:90.90000000000001@1.82:98.81@2.08:104.99@2.34:109.54@2.6:112.15{n}40|%|Mpa|Strain in %|Stress in MPa|0:0@0.29:18.43@0.58:35.6@0.87:50.51@1.16:62.84@1.45:72.70999999999999@1.74:80.47@2.03:86.48999999999999@2.32:90.95999999999999@2.61:93.66@2.9:93.75{n}50|%|Mpa|Strain in %|Stress in MPa|0:0@0.31:17.49@0.62:33.06@0.93:46.37@1.24:57.37@1.55:66.2@1.86:73.09999999999999@2.17:78.34999999999999@2.48:82.13@2.79:84.45999999999999@3.1:85.14{n}60|%|Mpa|Strain in %|Stress in MPa|0:0@0.34:17.23@0.68:32.14@1.02:44.63@1.36:54.76@1.7:62.68@2.04:68.61@2.38:72.81@2.72:75.52@3.06:76.95@3.4:77.2{n}80|%|Mpa|Strain in %|Stress in MPa|0:0@0.42:17.98@0.84:32.16@1.26:43.11@1.68:51.37@2.1:57.42@2.52:61.68@2.94:64.53@3.36:66.3@3.78:67.23999999999999@4.2:67.58{n}120|%|Mpa|Strain in %|Stress in MPa|0:0@0.74:15.57@1.48:25.34@2.22:31.37@2.96:35.13@3.7:37.58@4.44:39.3@5.18:40.58@5.92:41.51@6.66:42.12@7.4:42.44{n}150|%|Mpa|Strain in %|Stress in MPa|0:0@0.67:10.96@1.34:18.12@2.01:22.75@2.68:25.76@3.35:27.81@4.02:29.32@4.69:30.5@5.36:31.42@6.03:32.04@6.7:32.22

Secant modulus-strain(Break) -40|%|MPa|Strain in %|Secant modulus in MPa|0.27:8233.33@0.54:8218.52@0.8100000000000001:8071.6@1.08:7836.11@1.35:7543.7@1.62:7223.46@1.89:6894.18@2.16:6567.13@2.43:6247.33@2.7:5931.11{n}-20|%|MPa|Strain in %|Secant modulus in MPa|0.5600000000000001:7580.36@0.84:7427.38@1.12:7173.21@1.4:6861.43@1.68:6522.62@1.96:6179.59@2.24:5845.09@2.52:5520.24@2.8:5197.5{n}23|%|MPa|Strain in %|Secant modulus in MPa|0.26:7157.69@0.52:7138.46@0.78:6933.33@1.04:6612.5@1.3:6230@1.56:5826.92@1.82:5429.12@2.08:5047.6@2.34:4681.2@2.6:4313.46{n}40|%|MPa|Strain in %|Secant modulus in MPa|0.29:6355.17@0.58:6137.93@0.87:5805.75@1.16:5417.24@1.45:5014.48@1.74:4624.71@2.03:4260.59@2.32:3920.69@2.61:3588.51@2.9:3232.76{n}50|%|MPa|Strain in %|Secant modulus in MPa|0.31:5641.94@0.62:5332.26@0.93:4986.02@1.24:4626.61@1.55:4270.97@1.86:3930.11@2.17:3610.6@2.48:3311.69@2.79:3027.24@3.1:2746.45{n}60|%|MPa|Strain in %|Secant modulus in MPa|0.34:5067.65@0.68:4726.47@1.02:4375.49@1.36:4026.47@1.7:3687.06@2.04:3363.24@2.38:3059.24@2.72:2776.47@3.06:2514.71@3.4:2270.59{n}80|%|MPa|Strain in %|Secant modulus in MPa|0.42:4280.95@0.84:3828.57@1.26:3421.43@1.68:3057.74@2.1:2734.29@2.52:2447.62@2.94:2194.9@3.36:1973.21@3.78:1778.84@4.2:1609.05{n}120|%|MPa|Strain in %|Secant modulus in MPa|0.74:2104.05@1.48:1712.16@2.22:1413.06@2.96:1186.82@3.7:1015.68@4.44:885.135@5.18:783.398@5.92:701.182@6.66:632.432@7.4:573.513{n}150|%|MPa|Strain in %|Secant modulus in MPa|0.67:1635.82@1.34:1352.24@2.01:1131.84@2.68:961.194@3.35:830.149@4.02:729.353@4.69:650.3200000000001@5.36:586.194@6.03:531.343@6.7:480.896

Stress-strain (isochronous)(Creep) 23°C 1|%|MPa|Strain in %|Stress in MPa|0:0@0.12797:7@0.25739:14@0.38971:21@0.5263600000000001:28@0.6688:35@0.81847:42@0.97682:49@1.1453:56@1.32535:63@1.51842:70{n}10|%|MPa|Strain in %|Stress in MPa|0:0@0.13243:7@0.26706:14@0.40561:21@0.54988:28@0.70168:35@0.86291:42@1.0355:49@1.22146:56@1.42283:63@1.64172:70{n}100|%|MPa|Strain in %|Stress in MPa|0:0@0.13753:7@0.27821:14@0.42412:21@0.57744:28@0.74052:35@0.9157999999999999:42@1.10588:49@1.31349:56@1.54152:63@1.793:70{n}1000|%|MPa|Strain in %|Stress in MPa|0:0@0.14338:7@0.29109:14@0.44565:21@0.60977:28@0.7864:35@0.97875:42@1.19028:49@1.4247:56@1.68603:63@1.97859:70{n}10000|%|MPa|Strain in %|Stress in MPa|0:0@0.15008:7@0.30597:14@0.4707:21@0.64766:28@0.8406:35@1.05369:42@1.2915:49@1.55909:56@1.862:63@2.2063:70{n}100000|%|MPa|Strain in %|Stress in MPa|0:0@0.15777:7@0.32315:14@0.49985:21@0.69209:28@0.90463:35@1.14288:42@1.4129:49@1.7215:56@2.07626:63@2.48566:70

Stress-strain (isochronous)(Creep) 40°C 10|%|MPa|Strain in %|Stress in MPa|0:0@0.2913:15@0.4036:20@0.5228:25@0.6485:30@0.7805:35@0.9187:40@1.0628:45@1.2127:50@1.3682:55@1.5292:60{n}100|%|MPa|Strain in %|Stress in MPa|0:0@0.3027:15@0.4226:20@0.551:25@0.6873:30@0.8310999999999999:35@0.9822:40@1.1401:45@1.3046:50@1.4754:55@1.6523:60{n}1000|%|MPa|Strain in %|Stress in MPa|0:0@0.3172:15@0.4468:20@0.5868:25@0.7364000000000001:30@0.8949:35@1.0619:40@1.2367:45@1.419:50@1.6084:55@1.8043:60{n}10000|%|MPa|Strain in %|Stress in MPa|0:0@0.3357:15@0.4777:20@0.6323:25@0.7984:30@0.9752:35@1.1618:40@1.3574:45@1.5614:50@1.7731:55@1.9919:60{n}100000|%|MPa|Strain in %|Stress in MPa|0:0@0.3595:15@0.5171:20@0.6901:25@0.8769:30@1.0763:35@1.2871:40@1.5081:45@1.7385:50@1.9772:55@2.2234:60

Stress-strain (isochronous)(Creep) 60°C 10|%|MPa|Strain in %|Stress in MPa|0:0@0.3648:10@0.5498:14.4@0.7429:18.8@0.9425:23.2@1.1476:27.6@1.3573:32@1.571:36.4@1.7883:40.8@2.0088:45.2@2.2525:50{n}100|%|MPa|Strain in %|Stress in MPa|0:0@0.3952:10@0.5972:14.4@0.8080000000000001:18.8@1.0255:23.2@1.2486:27.6@1.4761:32@1.7072:36.4@1.9415:40.8@2.1783:45.2@2.4391:50{n}1000|%|MPa|Strain in %|Stress in MPa|0:0@0.4315:10@0.6535:14.4@0.885:18.8@1.1235:23.2@1.3673:27.6@1.6151:32@1.8661:36.4@2.1194:40.8@2.3746:45.2@2.6543:50{n}10000|%|MPa|Strain in %|Stress in MPa|0:0@0.4748:10@0.7204:14.4@0.9762:18.8@1.239:23.2@1.5067:27.6@1.7779:32@2.0514:36.4@2.3263:40.8@2.6018:45.2@2.9026:50{n}100000|%|MPa|Strain in %|Stress in MPa|0:0@0.5264:10@0.8:14.4@1.0842:18.8@1.3753:23.2@1.6706:27.6@1.9685:32@2.2676:36.4@2.5667:40.8@2.865:45.2@3.1889:50

Creep modulus-time 23°C 10|h|MPa|Time in h|Creep modulus in MPa|1:5459.31@10:5269.99@100:5068.39@1000:4854.71@10000:4630.29@100000:4396.51{n}20|h|MPa|Time in h|Creep modulus in MPa|1:5397.01@10:5187.94@100:4964.31@1000:4727.55@10000:4479.25@100000:4221.52{n}30|h|MPa|Time in h|Creep modulus in MPa|1:5296.59@10:5064.14@100:4815.93@1000:4553.58@10000:4279.73@100000:3997.24{n}40|h|MPa|Time in h|Creep modulus in MPa|1:5162.03@10:4903.31@100:4627.85@1000:4338.4@10000:4038.35@100000:3731.83{n}50|h|MPa|Time in h|Creep modulus in MPa|1:4998.76@10:4711.57@100:4407.52@1000:4090.61@10000:3765.56@100000:3437.57{n}60|h|MPa|Time in h|Creep modulus in MPa|1:4813.52@10:4496.9@100:4164.48@1000:3821.66@10000:3474.52@100000:3129.54{n}70|h|MPa|Time in h|Creep modulus in MPa|1:4610.06@10:4263.82@100:3904.07@1000:3537.87@10000:3172.73@100000:2816.15

Creep modulus-time 40°C 10|h|MPa|Time in h|Creep modulus in MPa|10:5311.12@100:5144.15@1000:4947.06@10000:4717.1@100000:4447.98{n}20|h|MPa|Time in h|Creep modulus in MPa|10:4955.4@100:4732.61@1000:4476.28@10000:4186.73@100000:3867.72{n}30|h|MPa|Time in h|Creep modulus in MPa|10:4626.06@100:4364.91@1000:4073.87@10000:3757.52@100000:3421.14{n}40|h|MPa|Time in h|Creep modulus in MPa|10:4353.98@100:4072.49@1000:3766.83@10000:3442.93@100000:3107.76{n}50|h|MPa|Time in h|Creep modulus in MPa|10:4123.03@100:3832.59@1000:3523.61@10000:3202.25@100000:2876.04{n}60|h|MPa|Time in h|Creep modulus in MPa|10:3923.62@100:3631.3@1000:3325.39@10000:3012.2@100000:2698.57

Creep modulus-time 60°C 10|h|MPa|Time in h|Creep modulus in MPa|10:2741.23@100:2530.36@1000:2317.5@10000:2106.15@100000:1899.7{n}20|h|MPa|Time in h|Creep modulus in MPa|10:2510.35@100:2307.7@1000:2106.64@10000:1909.81@100000:1719.74{n}30|h|MPa|Time in h|Creep modulus in MPa|10:2378.21@100:2186.26@1000:1997.31@10000:1813.49@100000:1636.79{n}40|h|MPa|Time in h|Creep modulus in MPa|10:2287.61@100:2106.7@1000:1929.39@10000:1757.27@100000:1592.13{n}50|h|MPa|Time in h|Creep modulus in MPa|10:2219.76@100:2049.94@1000:1883.74@10000:1722.59@100000:1567.94

Stress-strain (isochronous)(Creep) 80°C 1|%|MPa|Strain in %|Stress in MPa|0:0@0.68294:18@1.07246:27@1.48004:36{n}10|%|MPa|Strain in %|Stress in MPa|0:0@0.74984:18@1.18599:27@1.64573:36{n}100|%|MPa|Strain in %|Stress in MPa|0:0@0.83366:18@1.32853:27@1.85412:36{n}1000|%|MPa|Strain in %|Stress in MPa|0:0@0.9387:18@1.50747:27@2.11622:36{n}10000|%|MPa|Strain in %|Stress in MPa|0:0@1.07032:18@1.73212:27@2.44588:36

Stress-strain (isochronous)(Creep) 120°C 10|%|MPa|Strain in %|Stress in MPa|0:0@0.6922:12@0.7987:13.3@0.9124:14.6@1.0332:15.9@1.1614:17.2@1.297:18.5@1.4401:19.8@1.5907:21.1@1.7489:22.4@1.9539:24{n}100|%|MPa|Strain in %|Stress in MPa|0:0@0.7479:12@0.8669:13.3@0.9937:14.6@1.1283:15.9@1.2706:17.2@1.4205:18.5@1.5778:19.8@1.7424:21.1@1.9141:22.4@2.1348:24{n}1000|%|MPa|Strain in %|Stress in MPa|0:0@0.8198:12@0.954:13.3@1.0968:14.6@1.2478:15.9@1.4066:17.2@1.5729:18.5@1.7463:19.8@1.9264:21.1@2.1127:22.4@2.35:24{n}10000|%|MPa|Strain in %|Stress in MPa|0:0@0.9125:12@1.0655:13.3@1.2275:14.6@1.3979:15.9@1.576:17.2@1.7611:18.5@1.9525:19.8@2.1496:21.1@2.3516:22.4@2.6061:24{n}100000|%|MPa|Strain in %|Stress in MPa|0:0@1.0321:12@1.208:13.3@1.3931:14.6@1.5864:15.9@1.7869:17.2@1.9934:18.5@2.2049:19.8@2.4204:21.1@2.6389:22.4@2.9107:24

Creep modulus-time 80°C 5|h|MPa| Time in h|Creep modulus in MPa|1:2748.13@10:2519.89@100:2282.84@1000:2042.46@10000:1804.77{n}10|h|MPa| Time in h|Creep modulus in MPa|1:2719.02@10:2488.84@100:2250.5@1000:2009.62@10000:1772.25{n}15|h|MPa| Time in h|Creep modulus in MPa|1:2671.87@10:2438.76@100:2198.6@1000:1957.18@10000:1720.57{n}20|h|MPa| Time in h|Creep modulus in MPa|1:2608.86@10:2372.29@100:2130.16@1000:1888.53@10000:1653.42{n}25|h|MPa| Time in h|Creep modulus in MPa|1:2541.96@10:2302.11@100:2058.37@1000:1816.97@10000:1583.88{n}30|h|MPa| Time in h|Creep modulus in MPa|1:2484.78@10:2242.25@100:1997.32@1000:1756.31@10000:1525.12{n}35|h|MPa| Time in h|Creep modulus in MPa|1:2439.93@10:2195.37@100:1949.63@1000:1709.06@10000:1479.48{n}36|h|MPa| Time in h|Creep modulus in MPa|1:2432.37@10:2187.48@100:1941.62@1000:1701.15@10000:1471.86

Creep modulus-time 120°C 5|h|MPa|Time in h|Creep modulus in MPa|10:2041.99@100:1931.69@1000:1796.59@10000:1642.9@100000:1471.38{n}10|h|MPa|Time in h|Creep modulus in MPa|10:1836.13@100:1711.7@1000:1571.41@10000:1419.82@100000:1260.46{n}15|h|MPa|Time in h|Creep modulus in MPa|10:1580.95@100:1450.29@1000:1313.03@10000:1172.75@100000:1033.26{n}20|h|MPa|Time in h|Creep modulus in MPa|10:1367.25@100:1247.93@1000:1127.66@10000:1008.84@100000:893.727{n}24|h|MPa|Time in h|Creep modulus in MPa|10:1228.31@100:1124.23@1000:1021.28@10000:920.9160000000001@100000:824.544

Specific volume-temperature (pvT) 0.1|°C|E-3 m³/kg|Spec. volume in °C|Temperature in E-3 m³/kg|20:0.73241@30:0.73508@40:0.73776@50:0.74044@60:0.74312@70:0.74581@80:0.74851@90:0.75123@100:0.75397@110:0.75675@120:0.75957@130:0.76247@140:0.76549@150:0.76867@160:0.7720900000000001@170:0.77589@180:0.78023@190:0.78539@200:0.79175@210:0.79991@220:0.81073@230:0.82551@232:0.832@240:0.8365@250:0.84212@260:0.84774@270:0.85336@280:0.85898{n}40|°C|E-3 m³/kg|Spec. volume in °C|Temperature in E-3 m³/kg|20:0.72668@30:0.7291299999999999@40:0.7315700000000001@50:0.734@60:0.73642@70:0.73885@80:0.74127@90:0.74369@100:0.7461100000000001@110:0.74855@120:0.75102@130:0.75353@140:0.7561@150:0.75879@160:0.76164@170:0.76475@180:0.76824@190:0.7723100000000001@200:0.77723@210:0.78344@220:0.79157@230:0.8025600000000001@239.04:0.81757@240:0.81801@250:0.8226@260:0.82713@270:0.83161@280:0.8360300000000001{n}80|°C|E-3 m³/kg|Spec. volume in °C|Temperature in E-3 m³/kg|20:0.72142@30:0.72367@40:0.7259100000000001@50:0.7281300000000001@60:0.73034@70:0.73254@80:0.73473@90:0.73691@100:0.73908@110:0.74125@120:0.74343@130:0.74563@140:0.74787@150:0.75018@160:0.7526@170:0.75519@180:0.75804@190:0.7613@200:0.76518@210:0.76997@220:0.7761400000000001@230:0.78437@240:0.79567@246.08:0.80559@250:0.80711@260:0.8109499999999999@270:0.8147@280:0.81839{n}120|°C|E-3 m³/kg|Spec. volume in °C|Temperature in E-3 m³/kg|20:0.71655@30:0.7186399999999999@40:0.7207@50:0.72275@60:0.72477@70:0.72678@80:0.72878@90:0.73075@100:0.73271@110:0.73467@120:0.7366200000000001@130:0.7385699999999999@140:0.74054@150:0.74255@160:0.74463@170:0.74682@180:0.7492@190:0.75186@200:0.75495@210:0.7587@220:0.7634300000000001@230:0.7696499999999999@240:0.77808@250:0.78981@253.12:0.79533@260:0.79762@270:0.80088@280:0.80405{n}160|°C|E-3 m³/kg|Spec. volume in °C|Temperature in E-3 m³/kg|20:0.71202@30:0.71396@40:0.71587@50:0.71777@60:0.7196399999999999@70:0.72149@80:0.72331@90:0.72512@100:0.7269@110:0.72867@120:0.73043@130:0.7321800000000001@140:0.73393@150:0.73571@160:0.73752@170:0.7393999999999999@180:0.74141@190:0.74361@200:0.74612@210:0.74909@220:0.75276@230:0.7575@240:0.76383@250:0.77255@260:0.78482@260.16:0.78633@270:0.78917@280:0.79197{n}200|°C|E-3 m³/kg|Spec. volume in °C|Temperature in E-3 m³/kg|20:0.70778@30:0.7095900000000001@40:0.71138@50:0.71313@60:0.71487@70:0.71658@80:0.71826@90:0.71992@100:0.72156@110:0.72317@120:0.72477@130:0.7263500000000001@140:0.72792@150:0.7295@160:0.7311@170:0.7327399999999999@180:0.73445@190:0.7363@200:0.73836@210:0.74075@220:0.74364@230:0.74729@240:0.75208@250:0.7586000000000001@260:0.76768@267.2:0.7783099999999999@270:0.77903@280:0.78154

Tensile modulus-temperature |°C|MPa|Temperature in °C|Tensile modulus in MPa|-40:7950@-20:7560@23:7180@40:5980@50:5160@60:4830@80:4290@120:2400@150:1970

20% Glass Fiber