Injection molding grade with 30% glass fiber reinforcement and very high transmission for laser light in the wavelength range of 800 to 1100 nm. Suitable for manufacturing technical parts, e.g. covers that are welded to a housing by laser transmission welding
| Original Document | Technical Datasheet-ISO(English) | |||
| Resin ID | PBT-GF30 | |||
| Features | Good WeldFilled & Reinforced | |||
| Processing | Injection | |||
| Diagrams | Stress-strain(Break)Secant modulus-strain(Break)Tensile modulus-temperature | |||
| Reinforced | 30% Glass Fiber | |||
| Physical | Value/Unit(Sign in to View) | Test Standard | Test Condition |
|---|---|---|---|
Density/Specific Gravity | *** g/cm³ | ISO 1183 | |
Melt Volume Flow Rate(MVR) | |||
275°C/2.16 kg | *** cm³/10 min | ISO 1133 | |
Mold Shrinkage | |||
Flow | *** % | ISO 294-4 | |
Across Flow | *** % | ISO 294-4 | |
Water Absorption | *** % | ISO 62 | equilibrium 23°C/50% r.h. |
Water Absorption | *** % | ISO 62 | equilibrium in water at 23°C |
Viscosity | *** cm³/g | ISO 307, 1157, 1628 | solution 0,005 g/ml Phenole/1,2 Dichlorbenzol 1:1 |
| Mechanical | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Tensile Modulus | *** Mpa | ISO 527-1/-2 | |
Tensile Strength | |||
Break | *** Mpa | ISO 527-1/-2 | |
Tensile Elongation | |||
Break | *** % | ISO 527-1/-2 | |
Flexural Modulus | *** Mpa | ISO 178 | |
Flexural Strength | |||
- | *** Mpa | ISO 178 | |
| Impact | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Charpy Notched Impact Strengh | |||
-30℃ (-22℉) | *** kJ/m² | ISO 179/1eA | |
23℃ (73℉) | *** kJ/m² | ISO 179/1eA | |
Charpy Unnotched Impact Strengh | |||
-30℃ (-22℉) | *** kJ/m² | ISO 179/1eU | |
23℃ (73℉) | *** kJ/m² | ISO 179/1eU | |
| Thermal | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Heat Deflection Temperature(HDT) | |||
0.45 Mpa (66 psi)（4.6kg/cm²） | *** °C | ISO 75-1/-2 | |
1.8 Mpa (264 psi)（18.6kg/cm²） | *** °C | ISO 75-1/-2 | |
Coefficient of Linear Thermal Expansion | |||
Flow | ***~*** E-6/K | ISO 11359-1/-2 | 23-80℃ |
Melt Temperature(Tm) | *** °C | ISO 11357-1/-3 | DSC |
Temperature at Short Circle Operation | *** °C | - | |
Processing Temperature | ***~*** °C | - | |
Mould temperature | ***~*** °C | - | |
| Flammability | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Flame Rating | |||
HB | *** mm | IEC 60695-11-10 | |
HB | *** mm | IEC 60695-11-10 | |
| Electrical | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Volume Resistivity | *** Ohm-m | IEC 60093 | |
Surface Resistivity | *** Ohm | IEC 60093 | |
Dielectric Constant(Permittivity) | |||
100Hz | *** - | IEC 60250 | |
1MHz | *** - | IEC 60250 | |
Dissipation Factor | |||
100Hz | *** E-4 | IEC 60250 | |
1MHz | *** E-4 | IEC 60250 | |
Comparative Tracking Index (CTI) | |||
Solution A | *** V | IEC 60112 | |
| Optical | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Light Transmission | *** % | Internal | laser type Nd:YAG, 1064 nm |
The information presented on this datasheet was acquired by AjiEng.com from the producer of the material. AjiEng.com makes substantial efforts to assure the accuracy of this data. However, AjiEng.com assumes no responsibility for the data values and strongly encourages that upon final material selection, data points are validated with the material supplier.