Injection molding grade with 30% glass fibers for industrial parts with excellent surface quality, for example external door handles in vehicles, visible sunroof frames, oven door handles, toaster casings, external mirrors, rear screen wiper arms in vehicles and sunroof wind deflectors. Formerly called KR 4040 G6.
| Original Document | Technical Datasheet-ISO(English) | |||
| Resin ID | (PBT+PET)-GF30 | |||
| Features | Good SurfaceFilled & Reinforced | |||
| Processing | Injection | |||
| Diagrams | Viscosity-shear rateShearstress-shear rateDynamic Shear modulus-temperatureDynamic Shear modulus (G storage)-temperatureStress-strainSecant modulus-strainSpecific volume-temperature (pvT)Coefficient of Linear Thermal Expansion(CTE)-TemperatureTensile modulus-temperature | |||
| Reinforced | 30% Glass Fiber | |||
| Physical | Value/Unit(Sign in to View) | Test Standard | Test Condition |
|---|---|---|---|
Density/Specific Gravity | *** g/cm³ | ISO 1183 | |
Melt Volume Flow Rate(MVR) | |||
275°C/2.16 kg | *** cm³/10 min | ISO 1133 | |
Mold Shrinkage | |||
Flow | *** % | ISO 294-4 | |
Across Flow | *** % | ISO 294-4 | |
Molding Shrinkage | |||
Flow | *** % | Internal | plate with film gate 150*150*3 mm³ |
Across Flow | *** % | Internal | plate with film gate 150*150*3 mm³ |
Water Absorption | *** % | ISO 62 | equilibrium in water at 23°C |
Moisture /Humidity Absorption | *** % | ISO 62 | equilibrium 23°C/50% r.h. |
Viscosity | *** cm³/g | ISO 307, 1157, 1628 | solution 0,005 g/ml Phenole/1,2 Dichlorbenzol 1:1 |
| Mechanical | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Tensile Modulus | *** Mpa | ISO 527-1/-2 | |
Tensile Strength | |||
Break | *** Mpa | ISO 527-1/-2 | |
Break | *** Mpa | ISO 527-1/-2 | |
| Impact | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Charpy Notched Impact Strengh | |||
23℃ (73℉) | *** kJ/m² | ISO 179/1eA | |
Charpy Unnotched Impact Strengh | |||
-30℃ (-22℉) | *** kJ/m² | ISO 179/1eU | |
23℃ (73℉) | *** kJ/m² | ISO 179/1eU | |
| Thermal | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Heat Deflection Temperature(HDT) | |||
0.45 Mpa (66 psi)（4.6kg/cm²） | *** °C | ISO 75-1/-2 | |
1.8 Mpa (264 psi)（18.6kg/cm²） | *** °C | ISO 75-1/-2 | |
Specific Heat | *** J/kg-K | - | |
Coefficient of Linear Thermal Expansion | |||
Flow | ***~*** E-6/K | ISO 11359-1/-2 | 23-80℃ |
Melt Temperature(Tm) | *** °C | ISO 11357-1/-3 | DSC |
Temperature at Short Circle Operation | *** °C | - | |
Processing Temperature | ***~*** °C | - | |
Mould temperature | ***~*** °C | - | |
Temperature index (TI)-Tensile Strength | |||
5000 h | *** °C | IEC 60216 | |
20000 h | *** °C | IEC 60216 | |
| Flammability | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Flame Rating | |||
HB | *** mm | IEC 60695-11-10 | |
HB | *** mm | IEC 60695-11-10 | |
FMVSS | *** pass | FMVSS 302 | thickness d>= 1mm |
| Electrical | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Volume Resistivity | *** Ohm-m | IEC 60093 | |
Surface Resistivity | *** Ohm | IEC 60093 | |
Dielectric Constant(Permittivity) | |||
100Hz | *** - | IEC 60250 | |
1MHz | *** - | IEC 60250 | |
Dissipation Factor | |||
100Hz | *** E-4 | IEC 60250 | |
1MHz | *** E-4 | IEC 60250 | |
Comparative Tracking Index (CTI) | |||
Solution A | *** V | IEC 60112 |
The information presented on this datasheet was acquired by AjiEng.com from the producer of the material. AjiEng.com makes substantial efforts to assure the accuracy of this data. However, AjiEng.com assumes no responsibility for the data values and strongly encourages that upon final material selection, data points are validated with the material supplier.