| 物理性能 | 值/单位(登录后可见) | 测试标准 | 测试条件 |
密度/比重 |
*** g/cm³
| ASTM D792 | |
吸水率 |
*** %
| ASTM D570 | 24 hr |
| 机械性能 | 值/单位(登录后可见) | 测试标准 | 测试条件 |
拉伸模量 |
*** Mpa
| ASTM D638 | |
拉伸强度 | | | |
- |
*** Mpa | ASTM D 638 | |
拉伸延伸率 | | | |
断裂(brk) |
*** % | ASTM D638 | |
弯曲模量 |
*** Mpa
| ASTM D790 | |
弯曲强度 | | | |
- |
*** Mpa | ASTM D790 | |
摩擦系数 |
*** -
| ASTM 1894 | Lubricated: 0.25 m/s, 6.9 MPa |
摩擦系数 |
*** -
| ASTM 1894 | Lubricated: 4 m/s, 5.2 MPa |
摩擦系数 |
*** -
| ASTM D 3702 | Dry: 0.25 m/s, 3.4 MPa |
摩擦系数 |
*** -
| ASTM D 3702 | Dry: 4 m/s, 0.2 MPa |
磨损因数 |
*** E-10 in3·min/ft·lb·hr
| ASTM D 3702 | Dry: 0.25 m/s, 3.4 MPa |
磨损因数 |
*** E-10 in3·min/ft·lb·hr
| ASTM D 3702 | Dry: 4 m/s, 0.2 MPa |
磨损因数 |
*** E-10 in3·min/ft·lb·hr
| ASTM D 3702 | Lubricated: 0.25 m/s, 6.9 MPa |
磨损因数 |
*** E-10 in3·min/ft·lb·hr
| ASTM D 3702 | Lubricated: 4 m/s, 5.2 MPa |
抗压强度 |
*** Mpa
| ASTM D 695 | |
| 冲击性能 | 值/单位(登录后可见) | 测试标准 | 测试条件 |
悬臂梁缺口(Izod Notched) | | | |
- |
*** J/m | ASTM D 256 | |
悬臂梁无缺口(Izod Unnotched) | | | |
- |
*** J/m | ASTM D 256 | |
| 热学性能 | 值/单位(登录后可见) | 测试标准 | 测试条件 |
热变形温度(HDT) | | | |
1.8 Mpa (264 psi)（18.6kg/cm²） |
*** °C | ASTM D648 | Unannealed |
线性膨胀系数(CLTE) | | | |
- |
*** E-6 cm/cm/℃ | ASTM D 696 | |