Omnix® LF-4050 BK 000 is a 50% Long Glass Fiber reinforced, easy-flowing, heat stabilized HPPA with a very high flexural modulus. It exhibits unique stiffness/toughness combination, an excellent retention of properties in a wide temperature range as well as outstanding creep and fatigue resistance.
Omnix® LF-4050 BK 000 has a pellet length of 9mm and can be processed on most injection-molding machines.
| 原厂资料 | 物性表(英文) | |||
| 产品特性 | 高刚性耐疲劳高冲击耐热绝缘低翘曲抗蠕变填充增强 | |||
| 颜色形状 | 粒状黑色 | |||
| 成型方式 | 注塑 | |||
| 增强填充 | 50% 长玻纤 | |||
| 物理性能 | 值/单位 | 测试标准 | 测试条件 |
|---|---|---|---|
密度 | 1.59 g/cm³ | ISO 1183 | Dry |
收缩率 | |||
纵向(Flow) | 0.1 % | Internal | Dry |
吸水率 | 1.4 % | ISO 62 | Equilibrium, 23°C, 50% RH |
| 机械性能 | 值/单位 | 测试标准 | 测试条件 |
拉伸强度 | |||
断裂(brk) | 235 Mpa | ISO 527-2 | Conditioned,23℃ |
断裂(brk) | 270 Mpa | ISO 527-2 | Dry,23℃ |
拉伸延伸率 | |||
断裂(brk) | 2 % | ISO 527-2 | Conditioned |
断裂(brk) | 2.1 % | ISO 527-2 | Dry |
弯曲强度 | |||
- | 360 Mpa | ISO 178 | Dry,23℃ |
弯曲模量 | 16000 Mpa | ISO 178 | Dry,23℃ |
拉伸模量 | 17500 Mpa | ISO 527-2 | Conditioned,23℃ |
拉伸模量 | 17500 Mpa | ISO 527-2 | Dry,23℃ |
| 冲击性能 | 值/单位 | 测试标准 | 测试条件 |
简支梁缺口(Charpy Notched) | |||
23℃ (73℉) | 35 kJ/m² | ISO 179 | Conditioned |
23℃ (73℉) | 35 kJ/m² | ISO 179 | Dry |
简支梁无缺口(Charpy Unnotched) | |||
23℃ (73℉) | 95 kJ/m² | ISO 179 | Conditioned |
23℃ (73℉) | 95 kJ/m² | ISO 179 | Dry |
| 热学性能 | 值/单位 | 测试标准 | 测试条件 |
热变形温度(HDT) | |||
0.45 Mpa (66 psi)（4.6kg/cm²） | 260 °C | ISO 75-2/B | Dry,Unannealed |
1.8 Mpa (264 psi)（18.6kg/cm²） | 255 °C | ISO 75-2/A | Dry,Unannealed |
线性膨胀系数(CLTE) | |||
纵向(Flow) | 20 E-6 cm/cm/℃ | ISO 11359-2 | Dry |
导热系数 | 0.32 W/(m K) | ISO 22007 | Dry |
| 电学性能 | 值/单位 | 测试标准 | 测试条件 |
表面电阻率 | 1.0E+13 Ohm | ASTM D257 | Dry |
相对漏电起痕指数(CTI ) | |||
- | 600 V | IEC 60112 | Dry |
绝缘强度 | 35 kV/mm | IEC 60243-1 | Dry,2.0mm |
此物性表中的信息由阿技材料库从该材料的生产商处获得。阿技材料库尽最大努力确保此数据的准确性。 但是阿技材料库对这些数据值不承担任何责任，并强烈建议在最终选择材料前，就数据值与材料供应商进行验证。