KetaSpire® KT-880 CF30 is a high flow, 30% carbon fiber reinforced grade of polyetheretherketone (PEEK). Carbon-fiber reinforcement of KetaSpire® PEEK provides the maximum levels of mechanical properties at temperatures approaching 300°C and the lowest coefficient of linear thermal expansion within the KetaSpire® product family.
KetaSpire® PEEK is produced to the highest industry standards and is characterized by a distinct combination of properties, which include excellent wear resistance, best-in-class fatigue resistance, ease of melt processing, high purity and excellent chemical resistance to organics, acids and bases.
These properties make it well-suited for applications in healthcare, transportation, electronics, chemical processing and other industrial uses.
| 原厂资料 | 物性表(英文) | |||
| 产品特性 | 高强度高挺度耐疲劳耐热阻燃尺寸稳定电子束灭菌耐伽马射线环氧乙烷灭菌(EtO)耐蒸煮耐化学性高流动填充增强 | |||
| 颜色形状 | 粒状黑色 | |||
| 成型方式 | 注塑型材挤出机加工 | |||
| 法规认证 | FAA FAR(美国航空管理局)ISO10993(生物相容性)MIL P-46183(美国军用标准) | |||
| 增强填充 | 30% 碳纤 | |||
| 物理性能 | 值/单位 | 测试标准 | 测试条件 |
|---|---|---|---|
比重 | 1.41 - | ASTM D792 | |
熔体质量流动速率(MFR) | |||
400℃/2.16 kg | 11 g/10 min | ASTM D 1238 | |
收缩率 | |||
纵向(Flow) | 0~0.2 % | ASTM D 955 | 3.18 mm |
横向(Across Flow) | 1.4~1.6 % | ASTM D 955 | 3.18 mm |
吸水率 | 0.1 % | ASTM D570 | 24 hr |
粘度 | 450 Pa-s | ASTM D 3835 | 400℃,1000 sec-1 |
| 机械性能 | 值/单位 | 测试标准 | 测试条件 |
拉伸强度 | |||
屈服(yld) | 218 Mpa | ISO 527-2/1A/5 | |
- | 223 Mpa | ASTM D 638 | |
拉伸延伸率 | |||
断裂(brk) | 1.7 % | ASTM D638 | 5.0 mm/min |
断裂(brk) | 1.7 % | ISO 527-2/1A/5 | |
弯曲强度 | |||
- | 321 Mpa | ASTM D790 | |
- | 319 Mpa | ISO 178 | |
弯曲模量 | 17900 Mpa | ASTM D790 | |
弯曲模量 | 21500 Mpa | ISO 178 | |
拉伸模量 | 20900 Mpa | ASTM D638 | |
拉伸模量 | 25400 Mpa | ISO 527-2/1A/1 | |
剪切强度 | 103 Mpa | ASTM D 732 | |
抗压强度 | 188 Mpa | ASTM D 695 | |
| 冲击性能 | 值/单位 | 测试标准 | 测试条件 |
悬臂梁缺口(Izod Notched) | |||
- | 64 J/m | ASTM D 256 | |
- | 8.5 kJ/m² | ISO 180 | |
悬臂梁无缺口(Izod Unnotched) | |||
- | 43 kJ/m² | ISO 180 | |
- | 640 J/m | ASTM D 4812 | |
| 硬度性能 | 值/单位 | 测试标准 | 测试条件 |
洛氏硬度 M | 106 M | ASTM D 785 | |
| 热学性能 | 值/单位 | 测试标准 | 测试条件 |
热变形温度(HDT) | |||
1.8 Mpa (264 psi)（18.6kg/cm²） | 315 °C | ASTM D648 | Annealed |
比热容 | 1810 J/kg/℃ | DSC | 200℃ |
比热容 | 1310 J/kg/℃ | DSC | 50℃ |
线性膨胀系数(CLTE) | |||
纵向(Flow) | 6.7 E-6 cm/cm/℃ | ASTM E831 | -50 to 50℃ |
熔融温度(Tm) | 343 °C | ASTM D3418 | |
玻璃化温度(Tg) | 147 °C | ASTM D 3418 | |
导热系数 | 0.37 W/(m K) | ASTM E 1530 | |
| 燃烧性能 | 值/单位 | 测试标准 | 测试条件 |
UL 防火等级 | |||
V-0 | 0.8 mm | UL94 | |
V-0 | 1.6 mm | UL94 |
此物性表中的信息由阿技材料库从该材料的生产商处获得。阿技材料库尽最大努力确保此数据的准确性。 但是阿技材料库对这些数据值不承担任何责任，并强烈建议在最终选择材料前，就数据值与材料供应商进行验证。