Halar® 350LC is an Ethylene Chlorotrifluoroethylene Copolymer (ECTFE) material. It is available in Africa & Middle East, Asia Pacific, Europe, Latin America, or North America for extrusion.
Important attributes of Halar® 350LC are:
Flame Rated
Medium Viscosity
| Original Document | Technical Datasheet-ASTM(English) | |||
| Features | Medium viscosity | |||
| Processing | Extrusion | |||
| Physical | Value/Unit(Sign in to View) | Test Standard | Test Condition |
|---|---|---|---|
Density/Specific Gravity | *** g/cm³ | ASTM D792 | |
Melt Mass Flow Rate(MFR) | |||
275℃/2.16 kg | ***~*** g/10min | ASTM D 1238 | |
Mold Shrinkage | |||
Flow | *** % | ASTM D955 | |
Water Absorption | *** % | ASTM D570 | Equilibrium |
Abrasion resistance | *** mg | Internal | 1000 Cycles, 500 g, CS-17 Wheel |
| Mechanical | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Tensile Modulus | *** Mpa | ASTM D638 | 23℃,50 mm/min |
Tensile Strength | |||
Yield | *** Mpa | ASTM D638 | 23℃,50 mm/min |
Break | *** Mpa | ASTM D638 | 23℃,50 mm/min |
Tensile Elongation | |||
Yield | *** % | ASTM D638 | 23℃,50 mm/min |
Break | *** % | ASTM D638 | 23℃,50 mm/min |
Flexural Modulus | *** Mpa | ASTM D790 | 23℃,2.5 mm/min |
Flexural Strength | |||
- | *** Mpa | ASTM D790 | 23℃,2.5 mm/min |
Coefficient of Friction | *** - | ASTM 1894 | vs. Itself - Dynamic |
Coefficient of Friction | *** - | ASTM 1894 | vs. Itself - Static |
| Impact | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Izod Notched Impact Strengh | |||
-40℃ (-40℉) | *** J/m | ASTM D256 | 3.20 mm |
23℃ (73℉) | *** J/m | ASTM D256 | 3.20 mm |
Brittleness Temperature | *** °C | ASTM D 746 | |
| Hardness | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Rockwell R | *** R | ASTM D785 | |
Shore D hardness | *** D | ASTM D 2240 | |
| Thermal | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Heat Deflection Temperature(HDT) | |||
0.45 Mpa (66 psi)（4.6kg/cm²） | *** °C | ASTM D648 | Unannealed |
1.8 Mpa (264 psi)（18.6kg/cm²） | *** °C | ASTM D648 | Unannealed |
Specific Heat | *** J/kg/°C | ASTM D 3418 | 23℃ |
Coefficient of Linear Thermal Expansion | |||
Flow | *** E-6 cm/cm/℃ | ASTM D 696 | |
Melt Temperature(Tm) | *** °C | ASTM D3418 | |
Glass Transition Temperature | *** °C | Internal | |
Thermal Conductivity | *** W/(m K) | ASTM C 177 | 40℃ |
Freezing temperature | *** °C | ASTM D 3418 | DSC |
Crystallization Heat | *** J/g | ASTM D 3418 | |
Heat of Fusion | *** J/g | ASTM D 3418 | |
Thermal Stability | *** °C | TGA | 1% mass loss, N2 |
| Flammability | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Flame Rating | |||
V-0 | *** mm | UL94 | |
Oxygen Index | *** % | ASTM D 2863 | |
| Electrical | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Volume Resistivity | *** Ohm-cm | ASTM D257 | 23℃,50% RH |
Dielectric Constant(Permittivity) | |||
1MHz | *** - | ASTM D 150 | 23℃ |
Dielectric Strength | *** kV/mm | ASTM D149 | 23℃,3.20 mm |
The information presented on this datasheet was acquired by AjiEng.com from the producer of the material. AjiEng.com makes substantial efforts to assure the accuracy of this data. However, AjiEng.com assumes no responsibility for the data values and strongly encourages that upon final material selection, data points are validated with the material supplier.