AvaSpire® AV-651 is an unreinforced polyaryletherketone (PAEK) that offers more ductility and impact strength than PEEK, with higher chemical and environmental stress cracking resistance than AvaSpire® AV-650. It has been specifically formulated for applications requiring a balance of chemical resistance and mechanical strength along with good part aesthetics, bridging the performance gaps within the ultra polymers space.
These properties make it well-suited for applications in healthcare, transportation, electronics, chemical processing and other industrial uses.
AvaSpire® AV-651 can be easily processed by typical injection molding and extrusion methods using conventional processing equipment.
Natural: AvaSpire AV-651 NT
Beige: AvaSpire AV-651 BG 15
| Original Document | Technical Datasheet(English) | |||
| Features | Fatigue ResistantHigh ImpactGood ToughnessHeat ResistanceFlame RetardantDimensional StabilityBiocompatibleE-beam SterilizableGamma ResistanceEtO sterilizableSteam ResistantChemical Resistance | |||
| Appearance | Natural ColorYellow | |||
| Processing | InjectionExtrusionSheet ExtrusionProfile ExtrusionBlow MoldingSpinning/MonofilamentMachining | |||
| Physical | Value/Unit(Sign in to View) | Test Standard | Test Condition |
|---|---|---|---|
Density/Specific Gravity | *** g/cm³ | ASTM D792 | |
Melt Mass Flow Rate(MFR) | |||
400℃/2.16 kg | *** g/10 min | ASTM D 1238 | |
Mold Shrinkage | |||
Flow | ***~*** % | ASTM D955 | 3.18 mm |
Across Flow | ***~*** % | ASTM D955 | 3.18 mm |
Water Absorption | *** % | ASTM D570 | 24 hr |
Viscosity | *** Pa-s | ASTM D 3835 | 400°C, 1000 sec^-1 |
| Mechanical | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Tensile Modulus | *** Mpa | ASTM D638 | 50 mm/min |
Tensile Modulus | *** Mpa | ISO 527-2/1A/1 | |
Tensile Strength | |||
Yield | *** Mpa | ISO 527-2/1A/5 | |
- | *** Mpa | ASTM D 638 | 50 mm/min |
Tensile Elongation | |||
Yield | *** % | ASTM D638 | 50 mm/min |
Yield | *** % | ISO 527-2/50 | |
Break | *** % | ASTM D638 | 50 mm/min |
Break | *** % | ISO 527-2/1A/5 | |
Flexural Modulus | *** Mpa | ASTM D790 | |
Flexural Modulus | *** Mpa | ISO 178 | |
Flexural Strength | |||
- | *** Mpa | ASTM D790 | |
- | *** Mpa | ISO 178 | |
Shear Strength | *** Mpa | ASTM D 732 | |
Compressive Strength | *** Mpa | ASTM D 695 | |
| Impact | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Izod Notched Impact Strengh | |||
- | *** J/m | ASTM D 256 | |
- | *** kJ/m² | ISO 180 | |
Izod Unnotched Impact Strengh | |||
- | *** kJ/m² | ISO 180 | |
- | *** J/m | ASTM D 4812 | |
| Hardness | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Rockwell M | *** M | ASTM D 785 | |
| Thermal | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Heat Deflection Temperature(HDT) | |||
1.8 Mpa (264 psi)（18.6kg/cm²） | *** °C | ASTM D648 | Annealed |
Specific Heat | *** J/kg-K | - | 200℃ |
Specific Heat | *** J/kg-K | - | 50℃ |
Coefficient of Linear Thermal Expansion | |||
Flow | *** E-6 cm/cm/℃ | ASTM E831 | -50 to 50℃ |
Melt Temperature(Tm) | *** °C | ASTM D3418 | |
Glass Transition Temperature | *** °C | ASTM D 3418 | |
Thermal Conductivity | *** W/(m K) | ASTM E 1530 | |
| Flammability | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Flame Rating | |||
V-0 | *** mm | UL94 | |
V-0 | *** mm | UL94 | |
| Electrical | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Volume Resistivity | *** Ohm-cm | ASTM D257 | |
Surface Resistivity | *** Ohm | ASTM D257 | |
Dielectric Constant(Permittivity) | |||
60 Hz | *** - | ASTM D 150 | |
1 kHz | *** - | ASTM D 150 | |
1MHz | *** - | ASTM D 150 | |
Dissipation Factor | |||
60 Hz | *** E-4 | ASTM D 150 | |
1 kHz | *** E-4 | ASTM D 150 | |
1MHz | *** E-4 | ASTM D150 | |
Dielectric Strength | *** kV/mm | ASTM D149 | 3.00mm |
The information presented on this datasheet was acquired by AjiEng.com from the producer of the material. AjiEng.com makes substantial efforts to assure the accuracy of this data. However, AjiEng.com assumes no responsibility for the data values and strongly encourages that upon final material selection, data points are validated with the material supplier.