AvaSpire® AV-621 CF30 is a 30% carbon fiber reinforced version of AvaSpire® AV-621. It offers better dimensional stability and warp resistance than 30% carbon fiber reinforced PEEK. The AV-621 CF30 grade offers the highest strength, stiffness, and fatigue resistance of any AV-621 based grade. Furthermore, this resin generally retains most of the desirable ultra-performance attributes of carbon fiber reinforced PEEK including chemical resistance, fatigue resistance, and long term thermal oxidative stability.
The excellent balance of properties of AV-621 CF30 makes this grade well suited for a broad range of applications across a number of industries, including healthcare, transportation, electronics, and chemical processing.
This resin can be easily melt processed by injection molding using standard equipment. The melt processing behavior of AV-621 CF30 is very similar to that of 30% CF reinforced PEEK. The lower melt flow of AV-621 CF30 is well suited for extrusion applications while offering a similar property profile to AV-651 CF30.
| Original Document | Technical Datasheet(English) | |||
| Features | High StrengthHigh Stiffness/RigidityFatigue ResistantHeat ResistanceFlame RetardantDimensional StabilityChemical ResistanceFilled & Reinforced | |||
| Appearance | Black | |||
| Processing | InjectionProfile ExtrusionMachining | |||
| Compliance | ISO10993 | |||
| Reinforced | 30% Carbon Fiber | |||
| Physical | Value/Unit(Sign in to View) | Test Standard | Test Condition |
|---|---|---|---|
Density/Specific Gravity | *** g/cm³ | ASTM D792 | |
Melt Mass Flow Rate(MFR) | |||
400℃/2.16 kg | *** g/10 min | ASTM D 1238 | |
Mold Shrinkage | |||
Flow | ~*** % | ASTM D955 | 3.18 mm |
Across Flow | ***~*** % | ASTM D955 | 3.18 mm |
Water Absorption | *** % | ASTM D570 | 24 hr |
Viscosity | *** Pa-s | ASTM D 3835 | 400℃,1000 sec^-1 |
| Mechanical | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Tensile Modulus | *** Mpa | ASTM D638 | 5.0 mm/min |
Tensile Modulus | *** Mpa | ISO 527-2/1A/1 | |
Tensile Strength | |||
Yield | *** Mpa | ISO 527-2/1A/5 | |
- | *** Mpa | ASTM D 638 | 5.0 mm/min |
Tensile Elongation | |||
Break | *** % | ASTM D638 | 5.0 mm/min |
Break | *** % | ISO 527-2/1A/5 | |
Flexural Modulus | *** Mpa | ASTM D790 | |
Flexural Modulus | *** Mpa | ISO 178 | |
Flexural Strength | |||
- | *** Mpa | ASTM D790 | |
- | *** Mpa | ISO 178 | |
Shear Strength | *** Mpa | ASTM D 732 | |
Compressive Strength | *** Mpa | ASTM D 695 | |
| Impact | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Izod Notched Impact Strengh | |||
- | *** J/m | ASTM D 256 | |
- | *** kJ/m² | ISO 180 | |
Izod Unnotched Impact Strengh | |||
- | *** kJ/m² | ISO 180 | |
- | *** J/m | ASTM D 4812 | |
| Hardness | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Rockwell M | *** M | ASTM D 785 | |
| Thermal | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Heat Deflection Temperature(HDT) | |||
1.8 Mpa (264 psi)（18.6kg/cm²） | *** °C | ASTM D648 | Annealed |
Specific Heat | *** J/kg-K | - | 200℃ |
Specific Heat | *** J/kg-K | - | 50℃ |
Coefficient of Linear Thermal Expansion | |||
Flow | *** E-6 cm/cm/℃ | ASTM E831 | -50 to 50℃ |
Melt Temperature(Tm) | *** °C | ASTM D3418 | |
Glass Transition Temperature | *** °C | ASTM D 3418 | |
Thermal Conductivity | *** W/(m K) | ASTM E 1530 |
The information presented on this datasheet was acquired by AjiEng.com from the producer of the material. AjiEng.com makes substantial efforts to assure the accuracy of this data. However, AjiEng.com assumes no responsibility for the data values and strongly encourages that upon final material selection, data points are validated with the material supplier.