Amodel® AT-6115 HS is a 15% glass-fiber reinforced, toughened grade of polyphthalamide (PPA) resin designed to possess more elongation than other 15% glass-fiber reinforced grades of Amodel resin. This grade was developed for automotive snap-fit electronic connectors. It offers high flow and short molding cycles.
Black: AT-6115 HS BK 324
Natural: AT-6115 HS NT
| Original Document | Technical Datasheet(English) | |||
| Features | High ImpactHeat StabilizedFast Cycle TimeMold ReleaseHigh FlowFilled & Reinforced | |||
| Additive | Impact ModifierHeat StabilizerRelease AgentLubricant | |||
| Appearance | Natural ColorBlack | |||
| Processing | Injection | |||
| Compliance | RoHS | |||
| Reinforced | 15% Glass Fiber | |||
| Physical | Value/Unit(Sign in to View) | Test Standard | Test Condition |
|---|---|---|---|
Density/Specific Gravity | *** g/cm³ | ISO 1183 | Dry |
Mold Shrinkage | |||
Flow | *** % | ASTM D955 | Dry |
Across Flow | *** % | ASTM D955 | Dry |
Water Absorption | *** % | ASTM D570 | 24 hr |
| Mechanical | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Tensile Modulus | *** Mpa | ASTM D638 | Conditioned |
Tensile Modulus | *** Mpa | ASTM D638 | Dry |
Tensile Modulus | *** Mpa | ISO 527-2 | Dry,100℃ |
Tensile Modulus | *** Mpa | ISO 527-2 | Dry,23℃ |
Tensile Strength | |||
Break | *** Mpa | ISO 527-2 | Dry,100℃ |
Break | *** Mpa | ISO 527-2 | Dry,23℃ |
- | *** Mpa | ASTM D 638 | Conditioned |
- | *** Mpa | ASTM D 638 | Dry |
Tensile Elongation | |||
Break | *** % | ASTM D638 | Conditioned |
Break | *** % | ASTM D638 | Dry |
Break | *** % | ISO 527-2 | Dry,100℃ |
Break | *** % | ISO 527-2 | Dry,23℃ |
Flexural Modulus | *** Mpa | ASTM D790 | Conditioned |
Flexural Modulus | *** Mpa | ASTM D790 | Dry |
Flexural Modulus | *** Mpa | ISO 178 | Dry,100℃ |
Flexural Modulus | *** Mpa | ISO 178 | Dry,23℃ |
Flexural Strength | |||
- | *** Mpa | ASTM D790 | Conditioned |
- | *** Mpa | ASTM D790 | Dry |
- | *** Mpa | ISO 178 | Dry,100℃ |
- | *** Mpa | ISO 178 | Dry,23℃ |
Shear Strength | *** Mpa | ASTM D 732 | Conditioned |
Shear Strength | *** Mpa | ASTM D 732 | Dry |
Compressive Strength | *** Mpa | ASTM D 695 | Dry |
| Impact | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Charpy Notched Impact Strengh | |||
23℃ (73℉) | *** kJ/m² | ISO 179/1eA | Dry |
Charpy Unnotched Impact Strengh | |||
23℃ (73℉) | *** kJ/m² | ISO 179/1eU | Dry |
Izod Notched Impact Strengh | |||
23℃ (73℉) | *** kJ/m² | ISO 180/1A | Dry |
- | *** J/m | ASTM D 256 | Conditioned |
- | *** J/m | ASTM D 256 | Dry |
Izod Unnotched Impact Strengh | |||
23℃ (73℉) | *** kJ/m² | ISO 180/1U | Dry |
- | *** J/m | ASTM D 256 | Dry |
| Thermal | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Heat Deflection Temperature(HDT) | |||
0.45 Mpa (66 psi)（4.6kg/cm²） | *** °C | ISO 75-2/B | Unannealed |
1.8 Mpa (264 psi)（18.6kg/cm²） | *** °C | ASTM D648 | Annealed |
1.8 Mpa (264 psi)（18.6kg/cm²） | *** °C | ISO 75-2/A | Unannealed |
Coefficient of Linear Thermal Expansion | |||
Flow | *** E-6 cm/cm/℃ | ASTM E831 | 0 to 100℃ |
Flow | *** E-6 cm/cm/℃ | ASTM E831 | 100 to 200℃ |
Across Flow | *** E-6 cm/cm/℃ | ASTM E831 | 0 to 100℃ |
Across Flow | *** E-6 cm/cm/℃ | ASTM E831 | 100 to 200℃ |
Melt Temperature(Tm) | *** °C | ASTM D3418 | Dry |
Melt Temperature(Tm) | *** °C | ISO 11357-3 | Dry |
The information presented on this datasheet was acquired by AjiEng.com from the producer of the material. AjiEng.com makes substantial efforts to assure the accuracy of this data. However, AjiEng.com assumes no responsibility for the data values and strongly encourages that upon final material selection, data points are validated with the material supplier.