Amodel® AS-4133 L polyphthalamide (PPA) a 33% glass reinforced, lubricated, structural grade of polyphthalamide (PPA) that offers fast cycle times and is hot water moldable. Typical applications include electrical and electronic components.
Black: AS-4133 L BK 324
Natural: AS-4133 L NT
| Original Document | Technical Datasheet(English) | |||
| Features | High StrengthHigh Stiffness/RigidityDimensional StabilityCreep ResistantFast Cycle TimeChemical ResistanceFilled & Reinforced | |||
| Additive | Lubricant | |||
| Appearance | Natural ColorBlack | |||
| Processing | Injection | |||
| Compliance | RoHS | |||
| Reinforced | 33% Glass Fiber | |||
| Physical | Value/Unit(Sign in to View) | Test Standard | Test Condition |
|---|---|---|---|
Density/Specific Gravity | *** g/cm³ | ISO 1183 | Dry |
Mold Shrinkage | |||
Flow | *** % | ASTM D955 | Dry |
Across Flow | *** % | ASTM D955 | Dry |
Water Absorption | *** % | ASTM D570 | 24 hr |
| Mechanical | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Tensile Modulus | *** Mpa | ASTM D638 | Conditioned |
Tensile Modulus | *** Mpa | ASTM D638 | Dry |
Tensile Strength | |||
Break | *** Mpa | ASTM D638 | Conditioned |
Break | *** Mpa | ASTM D638 | Dry |
Tensile Elongation | |||
Break | *** % | ASTM D638 | Conditioned |
Break | *** % | ASTM D638 | Dry |
Flexural Modulus | *** Mpa | ASTM D790 | Conditioned |
Flexural Modulus | *** Mpa | ASTM D790 | Dry |
Flexural Strength | |||
Yield | *** Mpa | ASTM D790 | Conditioned |
Yield | *** Mpa | ASTM D790 | Dry |
Poisson Ratio | *** - | ASTM E 132 | Dry |
Shear Strength | *** Mpa | ASTM D 732 | Conditioned |
Shear Strength | *** Mpa | ASTM D 732 | Dry |
Compressive Strength | *** Mpa | ASTM D 695 | Conditioned |
Compressive Strength | *** Mpa | ASTM D 695 | Dry |
| Impact | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Izod Notched Impact Strengh | |||
- | *** J/m | ASTM D 256 | Conditioned |
- | *** J/m | ASTM D 256 | Dry |
Izod Unnotched Impact Strengh | |||
- | *** J/m | ASTM D 256 | Dry |
| Thermal | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Heat Deflection Temperature(HDT) | |||
0.45 Mpa (66 psi)（4.6kg/cm²） | *** °C | ASTM D648 | Dry,Annealed, 3.18 mm |
1.8 Mpa (264 psi)（18.6kg/cm²） | *** °C | ASTM D648 | Dry,Annealed, 3.18 mm |
Coefficient of Linear Thermal Expansion | |||
Flow | *** E-6 cm/cm/℃ | ASTM E831 | 0 to 90℃ |
Flow | *** E-6 cm/cm/℃ | ASTM E831 | 149 to 249℃ |
Across Flow | *** E-6 cm/cm/℃ | ASTM E831 | 0 to 90℃ |
Across Flow | *** E-6 cm/cm/℃ | ASTM E831 | 149 to 249℃ |
Melt Temperature(Tm) | *** °C | ASTM D3418 | Dry |
Melt Temperature(Tm) | *** °C | Internal | Dry |
| Flammability | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Flame Rating | |||
HB | *** mm | UL94 | Dry |
| Electrical | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Comparative Tracking Index (CTI) | |||
- | *** V | UL 746 | Conditioned |
- | *** V | UL 746 | Dry |
High Voltage Arc Tracking Rate(HVTR) | *** mm/min | UL 746A | Conditioned |
High Voltage Arc Tracking Rate(HVTR) | *** mm/min | UL 746A | Dry |
The information presented on this datasheet was acquired by AjiEng.com from the producer of the material. AjiEng.com makes substantial efforts to assure the accuracy of this data. However, AjiEng.com assumes no responsibility for the data values and strongly encourages that upon final material selection, data points are validated with the material supplier.