Amodel® AS-4133 HS is a 33% glass reinforced, lubricated, heat stabilized grade of polyphthalamide (PPA) that offers fast cycle times and moldability in hot water molds. Testing conducted on samples dry as molded and samples conditioned to 50% relative humidity in accordance with ISO-1110, Accelerated Method. Typical applications include electrical and electronic components especially for automotive systems.
Black: AS-4133 HS BK 324
Natural: AS-4133 HS NT
| 原厂资料 | 物性表(英文) | |||
| 产品特性 | 高强度高刚性耐热热稳定尺寸稳定抗蠕变短周期成型易焊接耐化学性填充增强 | |||
| 添加助剂 | 热稳定剂脱模剂润滑剂 | |||
| 颜色形状 | 本色黑色 | |||
| 成型方式 | 注塑 | |||
| 法规认证 | RoHS(欧盟电子电气设备中有害物质) | |||
| 增强填充 | 33% 玻纤 | |||
| 物理性能 | 值/单位 | 测试标准 | 测试条件 |
|---|---|---|---|
密度 | 1.45 g/cm³ | ISO 1183 | Dry |
收缩率 | |||
纵向(Flow) | 0.5 % | ASTM D 955 | Dry |
横向(Across Flow) | 1 % | ASTM D 955 | Dry |
吸水率 | 0.29 % | ASTM D570 | 24 hr |
| 机械性能 | 值/单位 | 测试标准 | 测试条件 |
拉伸强度 | |||
断裂(brk) | 125 Mpa | ISO 527-2 | Dry,100℃ |
断裂(brk) | 87.6 Mpa | ISO 527-2 | Dry,150℃ |
断裂(brk) | 79.3 Mpa | ISO 527-2 | Dry,175℃ |
断裂(brk) | 211 Mpa | ISO 527-2 | Dry,23℃ |
- | 172 Mpa | ASTM D 638 | Conditioned |
- | 200 Mpa | ASTM D 638 | Dry |
拉伸延伸率 | |||
断裂(brk) | 2.2 % | ASTM D638 | Conditioned |
断裂(brk) | 2.5 % | ASTM D638 | Dry |
断裂(brk) | 4.3 % | ISO 527-2 | Dry,100℃ |
断裂(brk) | 6.6 % | ISO 527-2 | Dry,150℃ |
断裂(brk) | 6.6 % | ISO 527-2 | Dry,175℃ |
断裂(brk) | 2.6 % | ISO 527-2 | Dry,23℃ |
弯曲强度 | |||
- | 241 Mpa | ASTM D790 | Conditioned |
- | 290 Mpa | ASTM D790 | Dry |
- | 177 Mpa | ISO 178 | Dry,100℃ |
- | 11 Mpa | ISO 178 | Dry,150℃ |
- | 99.3 Mpa | ISO 178 | Dry,175℃ |
- | 296 Mpa | ISO 178 | Dry,23℃ |
弯曲模量 | 11000 Mpa | ASTM D790 | Conditioned |
弯曲模量 | 11000 Mpa | ASTM D790 | Dry |
弯曲模量 | 7170 Mpa | ISO 178 | Dry,100℃ |
弯曲模量 | 4620 Mpa | ISO 178 | Dry,150℃ |
弯曲模量 | 4210 Mpa | ISO 178 | Dry,175℃ |
弯曲模量 | 10400 Mpa | ISO 178 | Dry,23℃ |
拉伸模量 | 11700 Mpa | ASTM D638 | Conditioned |
拉伸模量 | 11700 Mpa | ASTM D638 | Dry |
拉伸模量 | 6830 Mpa | ISO 527-2 | Dry,100℃ |
拉伸模量 | 5310 Mpa | ISO 527-2 | Dry,150℃ |
拉伸模量 | 4830 Mpa | ISO 527-2 | Dry,175℃ |
拉伸模量 | 12600 Mpa | ISO 527-2 | Dry,23℃ |
泊松比 | 0.41 - | ASTM E 132 | Dry |
剪切强度 | 75.8 Mpa | ASTM D 732 | Conditioned |
剪切强度 | 89.6 Mpa | ASTM D 732 | Dry |
抗压强度 | 172 Mpa | ASTM D 695 | Conditioned |
抗压强度 | 179 Mpa | ASTM D 695 | Dry |
| 冲击性能 | 值/单位 | 测试标准 | 测试条件 |
简支梁缺口(Charpy Notched) | |||
23℃ (73℉) | 11 kJ/m² | ISO 179/1eA | Dry |
简支梁无缺口(Charpy Unnotched) | |||
23℃ (73℉) | 67 kJ/m² | ISO 179/1eU | Dry |
悬臂梁缺口(Izod Notched) | |||
23℃ (73℉) | 9.7 kJ/m² | ISO 180/1A | Dry |
- | 69 J/m | ASTM D 256 | Conditioned |
- | 80 J/m | ASTM D 256 | Dry |
悬臂梁无缺口(Izod Unnotched) | |||
23℃ (73℉) | 59 kJ/m² | ISO 180/1U | Dry |
- | 960 J/m | ASTM D 256 | Dry |
| 热学性能 | 值/单位 | 测试标准 | 测试条件 |
热变形温度(HDT) | |||
0.45 Mpa (66 psi)（4.6kg/cm²） | 320 °C | ASTM D648 | Annealed, 3.2 mm |
1.8 Mpa (264 psi)（18.6kg/cm²） | 300 °C | ASTM D648 | Annealed, 3.2 mm |
1.8 Mpa (264 psi)（18.6kg/cm²） | 294 °C | ISO 75-2/A | Unannealed |
线性膨胀系数(CLTE) | |||
纵向(Flow) | 20 E-6 cm/cm/℃ | ASTM E831 | 0 to 100℃ |
纵向(Flow) | 15 E-6 cm/cm/℃ | ASTM E831 | 100 to 200℃ |
横向(Across Flow) | 76 E-6 cm/cm/℃ | ASTM E831 | 0 to 100℃ |
横向(Across Flow) | 120 E-6 cm/cm/℃ | ASTM E831 | 100 to 200℃ |
熔融温度(Tm) | 320 °C | ISO 11357-3 | Dry |
熔融温度(Tm) | 320 °C | ASTM D 570 | Dry |
连续使用温度 | |||
1500 hr | 210 °C | ASTM D 3045 | Dry |
| 燃烧性能 | 值/单位 | 测试标准 | 测试条件 |
UL 防火等级 | |||
HB | 3.2 mm | UL94 | Dry |
| 电学性能 | 值/单位 | 测试标准 | 测试条件 |
体积电阻率 | 5.0E+14 Ohm-cm | ASTM D257 | Conditioned |
体积电阻率 | 2.0E+16 Ohm-cm | ASTM D257 | Dry |
介电常数(DK) | |||
60 Hz | 4.3 - | ASTM D 150 | Conditioned |
60 Hz | 3.8 - | ASTM D 150 | Dry |
1MHz | 3.4 - | ASTM D 150 | Conditioned |
1MHz | 3.6 - | ASTM D 150 | Dry |
耗散因数(DF) | |||
60 Hz | 200 E-4 | ASTM D 150 | Conditioned |
60 Hz | 40 E-4 | ASTM D 150 | Dry |
1MHz | 190 E-4 | ASTM D150 | Conditioned |
1MHz | 120 E-4 | ASTM D150 | Dry |
相对漏电起痕指数(CTI ) | |||
- | 600 V | UL 746 | Conditioned |
- | 600 V | UL 746 | Dry |
绝缘强度 | 20 kV/mm | ASTM D149 | Conditioned,1.6mm |
绝缘强度 | 20 kV/mm | ASTM D149 | Dry,1.6mm |
高电压电弧起痕速率(HVTR) | 18 mm/min | UL 746A | Conditioned |
高电压电弧起痕速率(HVTR) | 14 mm/min | UL 746A | Dry |
| 光学性能 | 值/单位 | 测试标准 | 测试条件 |
透光率 | 20 % | ASTM D1003 | 1070nm : 1.60mm |
透光率 | 20 % | ASTM D1003 | 940nm : 1.60mm |
此物性表中的信息由阿技材料库从该材料的生产商处获得。阿技材料库尽最大努力确保此数据的准确性。 但是阿技材料库对这些数据值不承担任何责任，并强烈建议在最终选择材料前，就数据值与材料供应商进行验证。