Amodel® AS-1935 HS is a 35% glass reinforced grade of polyphthalamide (PPA) resin developed specifically for improved performance in a 50/50 ethylene glycol and water environment. This material exceeds the performance required by the automotive industry for polymeric materials exposed to antifreeze at 226°F (108°C), even when tested at 275°F (135°C).
Former PXM-12091
Black: AS-1935 HS BK 328
| 原厂资料 | 物性表(英文) | |||
| 产品特性 | 高强度高刚性耐热热稳定尺寸稳定抗蠕变耐化学性耐乙二醇耐防冻剂填充增强 | |||
| 添加助剂 | 热稳定剂 | |||
| 颜色形状 | 黑色 | |||
| 成型方式 | 注塑 | |||
| 法规认证 | RoHS(欧盟电子电气设备中有害物质) | |||
| 增强填充 | 35% 玻纤 | |||
| 物理性能 | 值/单位 | 测试标准 | 测试条件 |
|---|---|---|---|
密度 | 1.49 g/cm³ | ISO 1183 | |
收缩率 | |||
纵向(Flow) | 0.2 % | ASTM D 955 | |
横向(Across Flow) | 0.6 % | ASTM D 955 | |
| 机械性能 | 值/单位 | 测试标准 | 测试条件 |
拉伸强度 | |||
断裂(brk) | 205 Mpa | ASTM D638 | |
断裂(brk) | 210 Mpa | ISO 527-2 | |
拉伸延伸率 | |||
断裂(brk) | 2.2 % | ASTM D638 | |
断裂(brk) | 2.2 % | ISO 527-2 | |
弯曲强度 | |||
断裂(brk) | 275 Mpa | ASTM D790 | |
- | 300 Mpa | ISO 178 | |
弯曲模量 | 11300 Mpa | ASTM D790 | |
弯曲模量 | 11500 Mpa | ISO 178 | |
拉伸模量 | 12500 Mpa | ASTM D638 | |
拉伸模量 | 12600 Mpa | ISO 527-2 | |
| 冲击性能 | 值/单位 | 测试标准 | 测试条件 |
简支梁缺口(Charpy Notched) | |||
- | 8 kJ/m² | ISO 179/1eA | |
简支梁无缺口(Charpy Unnotched) | |||
- | 66 kJ/m² | ISO 179/1eU | |
悬臂梁缺口(Izod Notched) | |||
- | 8.5 kJ/m² | ISO 180/1A | |
- | 65 J/m | ASTM D 256 | |
| 热学性能 | 值/单位 | 测试标准 | 测试条件 |
热变形温度(HDT) | |||
1.8 Mpa (264 psi)（18.6kg/cm²） | 290 °C | ISO 75-2/A | Unannealed |
熔融温度(Tm) | 323 °C | ISO 11357-3 |
此物性表中的信息由阿技材料库从该材料的生产商处获得。阿技材料库尽最大努力确保此数据的准确性。 但是阿技材料库对这些数据值不承担任何责任，并强烈建议在最终选择材料前，就数据值与材料供应商进行验证。