Amodel® A-1625 HS is a carbon and glass-reinforced, heat-stabilized grade of polyphthalamide (PPA). It is formulated for applications requiring the dissipation of static charge. This material is well suited for fuel systems applications requiring low permeation, low swell, and high thermal resistance. It can also be used for components of electrical/electronic systems requiring high strength and stiffness, as well as static charge dissipation.
Amodel® A-1625 HS provides low moisture absorption, excellent dimensional stability and has creep resistance superior to other electrostatic dissipative materials.
Black: A-1625 HS BK 324
| 原厂资料 | 物性表(英文) | |||
| 产品特性 | 高刚性耐热抗静电尺寸稳定抗蠕变耐化学性填充增强 | |||
| 添加助剂 | 热稳定剂 | |||
| 颜色形状 | 黑色 | |||
| 成型方式 | 注塑 | |||
| 增强填充 | 玻纤碳纤玻纤+碳纤 | |||
| 物理性能 | 值/单位 | 测试标准 | 测试条件 |
|---|---|---|---|
密度 | 1.32 g/cm³ | ISO 1183 | |
收缩率 | |||
纵向(Flow) | 0.4 % | ISO 294-4 | |
横向(Across Flow) | 0.6 % | ISO 294-4 | |
吸水率 | 0.32 % | ASTM D570 | 24 hr, 50.8 mm |
| 机械性能 | 值/单位 | 测试标准 | 测试条件 |
拉伸强度 | |||
- | 205 Mpa | ASTM D 638 | |
- | 205 Mpa | ISO 527-2 | |
拉伸延伸率 | |||
断裂(brk) | 2.5 % | ASTM D638 | |
断裂(brk) | 2.4 % | ISO 527-2 | |
弯曲强度 | |||
- | 300 Mpa | ISO 178 | |
弯曲模量 | 13500 Mpa | ISO 178 | |
拉伸模量 | 15200 Mpa | ASTM D638 | |
拉伸模量 | 15000 Mpa | ISO 527-2 | |
| 冲击性能 | 值/单位 | 测试标准 | 测试条件 |
悬臂梁缺口(Izod Notched) | |||
-40℃ (-40℉) | 8 kJ/m² | ISO 180 | |
23℃ (73℉) | 11 kJ/m² | ISO 180 | |
- | 120 J/m | ASTM D 256 | |
悬臂梁无缺口(Izod Unnotched) | |||
-40℃ (-40℉) | 50 kJ/m² | ISO 180 | |
23℃ (73℉) | 50 kJ/m² | ISO 180 | |
| 热学性能 | 值/单位 | 测试标准 | 测试条件 |
热变形温度(HDT) | |||
0.45 Mpa (66 psi)（4.6kg/cm²） | 285 °C | ISO 75-2/B | Unannealed |
1.8 Mpa (264 psi)（18.6kg/cm²） | 270 °C | ASTM D648 | Unannealed |
1.8 Mpa (264 psi)（18.6kg/cm²） | 275 °C | ISO 75-2/A | Unannealed |
| 电学性能 | 值/单位 | 测试标准 | 测试条件 |
体积电阻率 | 2.4E+3 Ohm-cm | SAE J1645 | 50V |
此物性表中的信息由阿技材料库从该材料的生产商处获得。阿技材料库尽最大努力确保此数据的准确性。 但是阿技材料库对这些数据值不承担任何责任，并强烈建议在最终选择材料前，就数据值与材料供应商进行验证。