Terblend® N 3158 is an 9% mineral-filled ABS/PA blend with good dimensional stability, enhanced rigidity and excellent heat resistance, so that this grade can be applied for online-painting.
FEATURES
High dimensional stability
High rigidity
Excellent heat resistance for online-painting
Mineral filled (9%)
APPLICATIONS
Automotive exterior parts
Fenders
| 原厂资料 | 物性表-ISO(英文) | |||
| 产品特性 | 高刚性耐热尺寸稳定易涂装填充增强 | |||
| 增强填充 | 9% 矿物 | |||
| 物理性能 | 值/单位 | 测试标准 | 测试条件 |
|---|---|---|---|
密度 | 1.15 g/cm³ | ISO 1183 | |
熔体体积流动速率(MVR) | |||
280°C/10.0 kg | 10 cm³/10 min | ISO 1133 | |
收缩率 | |||
- | 1.1~1.4 % | ISO 294-4 | |
吸湿率 | 1.3 % | ISO 62 | Equilibrium 23°C/50% RH |
| 机械性能 | 值/单位 | 测试标准 | 测试条件 |
拉伸强度 | |||
屈服(yld) | 50 Mpa | ISO 527 | 23 °C |
拉伸延伸率 | |||
屈服(yld) | 3 % | ISO 527 | 23 °C |
断裂(brk) | 10 % | ISO 527 | 23 °C |
弯曲强度 | |||
- | 88 Mpa | ISO 178 | 23 °C |
弯曲模量 | 3000 Mpa | ISO 178 | 23 °C |
拉伸模量 | 2900 Mpa | ISO 527 | |
| 冲击性能 | 值/单位 | 测试标准 | 测试条件 |
简支梁无缺口(Charpy Unnotched) | |||
23℃ (73℉) | 160 kJ/m² | ISO 179 | |
悬臂梁缺口(Izod Notched) | |||
-30℃ (-22℉) | 8 kJ/m² | ISO 180/A | |
23℃ (73℉) | 160 kJ/m² | ASTM D256 | 1/4” bar, 0.010” Notch Radius |
23℃ (73℉) | 10 kJ/m² | ISO 180/A | |
| 热学性能 | 值/单位 | 测试标准 | 测试条件 |
热变形温度(HDT) | |||
0.45 Mpa (66 psi)（4.6kg/cm²） | 132 °C | ISO 75 | annealed 4 h/80 °C |
1.8 Mpa (264 psi)（18.6kg/cm²） | 92 °C | ISO 75 | annealed 4 h/80 °C |
维卡软化温度(Vicat) | 245 °C | ISO 306 | VST/A/50 (10N, 50 °C/h) |
维卡软化温度(Vicat) | 160 °C | ISO 306 | VST/B/50 (50N, 50 °C/h) |
线性膨胀系数(CLTE) | |||
- | 80 E-6/°C | ISO 11359 | |
加工温度 | 270~290 °C | - | |
模具温度 | 80 °C | - | |
| 电学性能 | 值/单位 | 测试标准 | 测试条件 |
体积电阻率 | 1.0E+13 Ohm-m | IEC 60093 | |
表面电阻率 | 1.0E+15 Ohm | IEC 60093 | |
耗散因数(DF) | |||
100Hz | 75 E-4 | IEC 60250 | |
1MHz | 150 E-4 | IEC 60250 | |
| 薄膜性能 | 值/单位 | 测试标准 | 测试条件 |
拉伸延伸率 | |||
断裂(brk) | 10 % | ISO 527 | MD |
此物性表中的信息由阿技材料库从该材料的生产商处获得。阿技材料库尽最大努力确保此数据的准确性。 但是阿技材料库对这些数据值不承担任何责任，并强烈建议在最终选择材料前，就数据值与材料供应商进行验证。