Terblend® S is a UV-stabilized ASA/PA blend with high impact strength, easy flow and pronounced color fastness. It is especially suitable for unpainted highly UV-exposed automotive interior parts.
FEATURES
Enhanced UV resistance and color fastness
Excellent flow for high surface quality appearance
High impact strength
UV-stabilized
APPLICATIONS
Unpainted automotive interior parts
Trim for convertibles
Under the windscreen interior applications
| Original Document | Technical Datasheet-ISO(English) | |||
| Resin ID | ASA+PA6 | |||
| Features | High ImpactGood SurfaceUV StabiltiyHigh Flow | |||
| Additive | UV-Stabilizer | |||
| Applications | Automotive Interior Parts | |||
| Diagrams | Stress-strainSecant modulus-strainTensile modulus-temperature | |||
| Physical | Value/Unit(Sign in to View) | Test Standard | Test Condition |
|---|---|---|---|
Density/Specific Gravity | *** g/cm³ | ISO 1183 | |
Melt Volume Flow Rate(MVR) | |||
240°C/10 kg | *** cm³/10 min | ISO 1133 | |
Mold Shrinkage | |||
- | *** % | ISO 294-4 | |
Moisture /Humidity Absorption | *** % | ISO 62 | Equilibrium 23°C/50% RH |
| Mechanical | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Tensile Modulus | *** Mpa | ISO 527 | |
Tensile Strength | |||
Yield | *** Mpa | ISO 527 | 23 °C |
Tensile Elongation | |||
Yield | *** % | ISO 527 | 23 °C |
Flexural Modulus | *** Mpa | ISO 178 | 23 °C |
Flexural Strength | |||
- | *** Mpa | ISO 178 | 23 °C |
| Impact | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Charpy Notched Impact Strengh | |||
-30℃ (-22℉) | *** kJ/m² | ISO 179/1eA | |
23℃ (73℉) | *** kJ/m² | ISO 179/1eA | |
Izod Notched Impact Strengh | |||
-30℃ (-22℉) | *** kJ/m² | ISO 180/A | |
23℃ (73℉) | *** kJ/m² | ISO 180/A | |
| Thermal | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Heat Deflection Temperature(HDT) | |||
0.45 Mpa (66 psi)（4.6kg/cm²） | *** °C | ISO 75 | annealed 4 h/80 °C |
1.8 Mpa (264 psi)（18.6kg/cm²） | *** °C | ISO 75 | annealed 4 h/80 °C |
Vicat Softening Temperature(VST) | *** °C | ISO 306 | VST/A/50 (10N, 50 °C/h) |
Vicat Softening Temperature(VST) | *** °C | ISO 306 | VST/B/50 (50N, 50 °C/h) |
Coefficient of Linear Thermal Expansion | |||
- | *** E-6/°C | ISO 11359 | |
Processing Temperature | ***~*** °C | - | |
Mould temperature | ***~*** °C | - | |
| Electrical | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Volume Resistivity | *** Ohm-m | IEC 60093 | |
Surface Resistivity | *** Ohm | IEC 60093 | |
Dielectric Constant(Permittivity) | |||
100Hz | *** - | IEC 60250 | |
Dissipation Factor | |||
1MHz | *** E-4 | IEC 60250 | |
| Film | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Tensile Elongation | |||
Break | *** % | ISO 527 | MD |
The information presented on this datasheet was acquired by AjiEng.com from the producer of the material. AjiEng.com makes substantial efforts to assure the accuracy of this data. However, AjiEng.com assumes no responsibility for the data values and strongly encourages that upon final material selection, data points are validated with the material supplier.