Terblend® N NG-02 EF is an 8% glass fiber reinforced UV-stabilized ABS/PA blend with enhanced dimensional stability, rigidity and high flowability.
FEATURES
High dimensional stability
Excellent flow for high surface quality appearance
Enhanced softening temperature
Enhanced rigidity
UV-stabilized
APPLICATIONS
Automotive parts
Motorcycle fairings
Truck cabin parts
| Original Document | Technical Datasheet-ISO(English) | |||
| Resin ID | (ABS+PA6)-GF8 | |||
| Features | High Stiffness/RigidityHeat ResistanceDimensional StabilityUV StabiltiyHigh FlowFilled & Reinforced | |||
| Additive | UV-Stabilizer | |||
| Applications | Automotive PartsHeavy Truck PartsCabin partsMotorcycle fairings | |||
| Diagrams | Stress-strainSecant modulus-strainTensile modulus-temperature | |||
| Reinforced | 8% Glass Fiber | |||
| Physical | Value/Unit(Sign in to View) | Test Standard | Test Condition |
|---|---|---|---|
Density/Specific Gravity | *** g/cm³ | ISO 1183 | |
Melt Volume Flow Rate(MVR) | |||
240°C/10 kg | *** cm³/10 min | ISO 1133 | |
Mold Shrinkage | |||
- | *** % | ISO 294-4 | |
Moisture /Humidity Absorption | *** % | ISO 62 | Equilibrium 23 °C/50% RH |
| Mechanical | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Tensile Modulus | *** Mpa | ISO 527 | |
Tensile Strength | |||
Yield | *** Mpa | ISO 527 | 23 °C |
Tensile Elongation | |||
Yield | *** % | ISO 527 | 23 °C |
Flexural Modulus | *** Mpa | ISO 178 | 23 °C |
Flexural Strength | |||
- | *** Mpa | ISO 178 | 23 °C |
| Impact | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Charpy Notched Impact Strengh | |||
-30℃ (-22℉) | *** kJ/m² | ISO 179/1eA | |
23℃ (73℉) | *** kJ/m² | ISO 179/1eA | |
Charpy Unnotched Impact Strengh | |||
-30℃ (-22℉) | *** kJ/m² | ISO 179/1eU | |
23℃ (73℉) | *** kJ/m² | ISO 179/1eU | |
Izod Notched Impact Strengh | |||
-30℃ (-22℉) | *** kJ/m² | ISO 180/A | |
23℃ (73℉) | *** kJ/m² | ISO 180/A | |
| Thermal | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Heat Deflection Temperature(HDT) | |||
0.45 Mpa (66 psi)（4.6kg/cm²） | *** °C | ISO 75 | annealed 4 h/80 °C |
1.8 Mpa (264 psi)（18.6kg/cm²） | *** °C | ISO 75 | annealed 4 h/80 °C |
Vicat Softening Temperature(VST) | *** °C | ISO 306 | VST/A/50 (10N, 50 °C/h) |
Vicat Softening Temperature(VST) | *** °C | ISO 306 | VST/B/50 (50N, 50 °C/h) |
Coefficient of Linear Thermal Expansion | |||
- | *** E-6/°C | ISO 11359 | |
Processing Temperature | ***~*** °C | - | |
Mould temperature | ***~*** °C | - | |
| Electrical | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Volume Resistivity | *** Ohm-m | IEC 60093 | |
Surface Resistivity | *** Ohm | IEC 60093 | |
Dielectric Constant(Permittivity) | |||
1MHz | *** - | IEC 60250 | |
Dissipation Factor | |||
1MHz | *** E-4 | IEC 60250 | |
| Film | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Tensile Elongation | |||
Break | *** % | ISO 527 | MD |
The information presented on this datasheet was acquired by AjiEng.com from the producer of the material. AjiEng.com makes substantial efforts to assure the accuracy of this data. However, AjiEng.com assumes no responsibility for the data values and strongly encourages that upon final material selection, data points are validated with the material supplier.