Luran® S KR2866C is a blend of ASA and PC with a reduced content of PC. It is characterized by a medium impact toughness and heat resistance.
FEATURES
Good heat resistance
Medium impact strength
APPLICATIONS
Radiator grills
| Original Document | Technical Datasheet-ISO(English) | |||
| Resin ID | ASA+PC | |||
| Features | High ImpactHeat Resistance | |||
| Applications | Radiator Grills | |||
| Diagrams | Stress-strain -40|%|Mpa|Strain in %|Stress in MPa|0:0@0.5600000000000001:16.73@1.12:31.51@1.68:44.37@2.24:55.3@2.8:64.28@3.36:71.28@3.92:76.34999999999999@4.48:79.65000000000001@5.04:81.48@5.6:82.33{n}-20|%|Mpa|Strain in %|Stress in MPa|0:0@0.48:14.09@0.96:26.65@1.44:37.78@1.92:47.45@2.4:55.55@2.88:62@3.36:66.73999999999999@3.84:69.83@4.32:71.52@4.8:72.23999999999999{n}0|%|Mpa|Strain in %|Stress in MPa|0:0@0.43:12.15@0.86:23.17@1.29:33@1.72:41.55@2.15:48.72@2.58:54.42@3.01:58.63@3.44:61.4@3.87:62.89@4.3:63.41{n}23|%|Mpa|Strain in %|Stress in MPa|0:0@0.41:11@0.82:21.07@1.23:29.95@1.64:37.46@2.05:43.5@2.46:48.05@2.87:51.17@3.28:53.04@3.69:53.93@4.1:54.23{n}40|%|Mpa|Strain in %|Stress in MPa|0:0@0.37:9.390000000000001@0.74:18.01@1.11:25.56@1.48:31.88@1.85:36.89@2.22:40.63@2.59:43.2@2.96:44.79@3.33:45.65@3.7:46.06{n}60|%|Mpa|Strain in %|Stress in MPa|0:0@0.35:8.199999999999999@0.7:15.74@1.05:22.24@1.4:27.5@1.75:31.49@2.1:34.28@2.45:36.05@2.8:37.04@3.15:37.52@3.5:37.74{n}80|%|Mpa|Strain in %|Stress in MPa|0:0@0.28:6.13@0.5600000000000001:11.75@0.84:16.69@1.12:20.84@1.4:24.12@1.68:26.54@1.96:28.14@2.24:29.06@2.52:29.5@2.8:29.72{n}100|%|Mpa|Strain in %|Stress in MPa|0:0@0.26:4.82@0.52:8.92@0.78:12.37@1.04:15.19@1.3:17.43@1.56:19.1@1.82:20.25@2.08:20.94@2.34:21.29@2.6:21.43Secant modulus-strain -40|%|MPa|Strain in %|Secant modulus in MPa|0.5600000000000001:2987.5@1.12:2813.39@1.68:2641.07@2.24:2468.75@2.8:2295.71@3.36:2121.43@3.92:1947.7@4.48:1777.9@5.04:1616.67@5.6:1470.18{n}-20|%|MPa|Strain in %|Secant modulus in MPa|0.48:2935.42@0.96:2776.04@1.44:2623.61@1.92:2471.35@2.4:2314.58@2.88:2152.78@3.36:1986.31@3.84:1818.49@4.32:1655.56@4.8:1505{n}0|%|MPa|Strain in %|Secant modulus in MPa|0.43:2825.58@0.86:2694.19@1.29:2558.14@1.72:2415.7@2.15:2266.05@2.58:2109.3@3.01:1947.84@3.44:1784.88@3.87:1625.06@4.3:1474.65{n}23|%|MPa|Strain in %|Secant modulus in MPa|0.41:2682.93@0.82:2569.51@1.23:2434.96@1.64:2284.15@2.05:2121.95@2.46:1953.25@2.87:1782.93@3.28:1617.07@3.69:1461.52@4.1:1322.68{n}40|%|MPa|Strain in %|Secant modulus in MPa|0.37:2537.84@0.74:2433.78@1.11:2302.7@1.48:2154.05@1.85:1994.05@2.22:1830.18@2.59:1667.95@2.96:1513.18@3.33:1370.87@3.7:1244.86{n}60|%|MPa|Strain in %|Secant modulus in MPa|0.35:2342.86@0.7:2248.57@1.05:2118.1@1.4:1964.29@1.75:1799.43@2.1:1632.38@2.45:1471.43@2.8:1322.86@3.15:1191.11@3.5:1078.29{n}80|%|MPa|Strain in %|Secant modulus in MPa|0.28:2189.29@0.5600000000000001:2098.21@0.84:1986.9@1.12:1860.71@1.4:1722.86@1.68:1579.76@1.96:1435.71@2.24:1297.32@2.52:1170.63@2.8:1061.43{n}100|%|MPa|Strain in %|Secant modulus in MPa|0.26:1853.85@0.52:1715.38@0.78:1585.9@1.04:1460.58@1.3:1340.77@1.56:1224.36@1.82:1112.64@2.08:1006.73@2.34:909.829@2.6:824.231Tensile modulus-temperature |°C|MPa|Temperature in °C|Tensile modulus in MPa|-40:3018@-30:2948@-20:2945@-10:2857@0:2803@10:2751@20:2666@30:2587@40:2466@50:2323@60:2201@70:2057@80:1919@90:1716@100:1334 | |||
| Physical | Value/Unit(Sign in to View) | Test Standard | Test Condition |
|---|---|---|---|
Density/Specific Gravity | *** g/cm³ | ISO 1183 | |
Melt Volume Flow Rate(MVR) | |||
220°C/10.0 kg | *** cm³/10 min | ISO 1133 | |
260°C/5.0 kg | *** cm³/10 min | ISO 1133 | |
Mold Shrinkage | |||
- | ***~*** % | ISO 294-4 | |
Water Absorption | *** % | ISO 62 | Saturated at 23°C |
Moisture /Humidity Absorption | *** % | ISO 62 | Equilibrium 23 °C/50% RH |
| Mechanical | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Tensile Modulus | *** Mpa | ISO 527 | |
Tensile Strength | |||
Yield | *** Mpa | ISO 527 | 23 °C |
Tensile Elongation | |||
Yield | *** % | ISO 527 | 23 °C |
Flexural Strength | |||
- | *** Mpa | ISO 178 | 23 °C |
| Impact | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Charpy Notched Impact Strengh | |||
-30℃ (-22℉) | *** kJ/m² | ISO 179/1eA | |
23℃ (73℉) | *** kJ/m² | ISO 179/1eA | |
Izod Notched Impact Strengh | |||
-30℃ (-22℉) | *** kJ/m² | ISO 180/A | |
23℃ (73℉) | *** kJ/m² | ISO 180/A | |
| Hardness | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Ball Indentation Hardness | *** Mpa | ISO 2039-1 | |
| Thermal | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Heat Deflection Temperature(HDT) | |||
0.45 Mpa (66 psi)（4.6kg/cm²） | *** °C | ISO 75 | annealed 4 h/80 °C |
1.8 Mpa (264 psi)（18.6kg/cm²） | *** °C | ISO 75 | annealed 4 h/80 °C |
Vicat Softening Temperature(VST) | *** °C | ISO 306 | VST/B/50 (50N, 50 °C/h) |
Coefficient of Linear Thermal Expansion | |||
- | ***~*** E-6/°C | ISO 11359 | |
Thermal Conductivity | *** W/(m K) | DIN 52612-1 | |
Processing Temperature | ***~*** °C | - | |
Mould temperature | *** °C | - | |
| Electrical | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Volume Resistivity | *** Ohm-m | IEC 60093 | |
Surface Resistivity | *** Ohm | IEC 60093 | |
| Film | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Tensile Elongation | |||
Break | *** % | ISO 527 | MD |
The information presented on this datasheet was acquired by AjiEng.com from the producer of the material. AjiEng.com makes substantial efforts to assure the accuracy of this data. However, AjiEng.com assumes no responsibility for the data values and strongly encourages that upon final material selection, data points are validated with the material supplier.