物性表(英文) 

SAN-GF35

高刚性

耐热

尺寸稳定

耐候性

耐化学性

填充增强

精密部件

窗户框架

机器构造部件

注塑

挤出

N粘度-剪切速度 220|1/s|Pa s|Shear rate in 1/s|Viscosity in Pa s|0.722:12855.3@2.349:9192.51@7.639:5748.89@24.846:3176.3@80.812:1571.66@262.845:707.843@854.919:295.732@2780.68:117.135@9044.32:45.0758@29417.2:17.3183{n}245|1/s|Pa s|Shear rate in 1/s|Viscosity in Pa s|2.808:3305.4@9.134:2364.05@29.71:1478.15@96.633:816.682@314.303:404.097@1022.29:181.996@3325.06:76.0368@10815:30.117@35176.3:11.5896@114413:4.45279{n}270|1/s|Pa s|Shear rate in 1/s|Viscosity in Pa s|7.952:1167.2@25.863:834.907@84.12:522.061@273.606:288.438@889.919:142.72@2894.51:64.2779@9414.58:26.8548@30621.5:10.6368@99598.2:4.09325@323949:1.57265

剪切应力-剪切速率 220|1/s|Pa|Shear rate in 1/s|Shearstress in Pa|0.722:9281.559999999999@2.349:21593.2@7.639:43915.8@24.846:78918.3@80.812:127009@262.845:186053@854.919:252827@2780.68:325715@9044.32:407680@29417.2:509457{n}245|1/s|Pa|Shear rate in 1/s|Shearstress in Pa|2.808:9281.559999999999@9.134:21593.2@29.71:43915.8@96.633:78918.39999999999@314.303:127009@1022.29:186053@3325.06:252827@10815:325715@35176.3:407680@114413:509457{n}270|1/s|Pa|Shear rate in 1/s|Shearstress in Pa|7.952:9281.559999999999@25.863:21593.2@84.12:43915.8@273.606:78918.3@889.919:127009@2894.51:186053@9414.58:252827@30621.5:325715@99598.2:407680@323949:509457

动态剪切模量 (G 储能)-温度 G'|°C|MPa|Temperature in °C|G' in MPa|-60:2875@-50:2750@-40:2650@-30:2613@-20:2563@-10:2525@0:2505@10:2495@20:2475@30:2400@40:2350@50:2250@60:2188@70:2125@80:2000@90:1926@100:1778@110:1333@120:281.3@130:50@140:17@150:10

应力-应变 -40|%|Mpa|Strain in %|Stress in MPa|0:0@0.15:23.67@0.3:45.44@0.45:65.39@0.6:83.58@0.75:100.1@0.9:115.03@1.05:128.44@1.2:140.41@1.35:151.01@1.5:160.33{n}-20|%|Mpa|Strain in %|Stress in MPa|0:0@0.14:20.5@0.28:40.05@0.42:58.51@0.5600000000000001:75.73999999999999@0.7:91.59@0.84:105.92@0.98:118.58@1.12:129.43@1.26:138.33@1.4:145.13{n}0|%|Mpa|Strain in %|Stress in MPa|0:0@0.42:52.74@0.5600000000000001:69.76000000000001@0.7:85.73@0.84:100.19@0.98:112.67@1.12:122.71@1.26:129.84@1.4:133.61{n}23|%|Mpa|Strain in %|Stress in MPa|0:0@0.52:63.32@0.65:75.37@0.78:85.91@0.91:94.94@1.04:102.47@1.17:108.5@1.3:113.01{n}40|%|Mpa|Strain in %|Stress in MPa|0:0@0.24:29.92@0.36:43.68@0.48:56.42@0.6:67.98@0.72:78.2@0.84:86.92@0.96:93.98@1.08:99.23@1.2:102.49{n}60|%|Mpa|Strain in %|Stress in MPa|0:0@0.22:26.4@0.33:37.79@0.44:48@0.55:57.07@0.66:65.03@0.77:71.90000000000001@0.88:77.72@0.99:82.52@1.1:86.31999999999999{n}80|%|Mpa|Strain in %|Stress in MPa|0:0@0.1:12.49@0.2:23.4@0.3:32.86@0.4:40.99@0.5:47.9@0.6:53.72@0.7:58.56@0.8:62.56@0.9:65.83@1:68.48999999999999{n}100|%|Mpa|Strain in %|Stress in MPa|0:0@0.14:6.49@0.28:10.85@0.42:13.85@0.5600000000000001:15.97@0.7:17.49@0.84:18.57@0.98:19.26@1.12:19.64@1.26:19.84@1.4:20.09

正割模量-应变 -40|%|MPa|Strain in %|Secant modulus in MPa|0.15:15780@0.3:15146.7@0.45:14531.1@0.6:13930@0.75:13346.7@0.9:12781.1@1.05:12232.4@1.2:11700.8@1.35:11185.9@1.5:10688.7{n}-20|%|MPa|Strain in %|Secant modulus in MPa|0.14:14642.9@0.28:14303.6@0.42:13931@0.5600000000000001:13525@0.7:13084.3@0.84:12609.5@0.98:12100@1.12:11556.2@1.26:10978.6@1.4:10366.4{n}0|%|MPa|Strain in %|Secant modulus in MPa|0.42:12557.1@0.5600000000000001:12457.1@0.7:12247.1@0.84:11927.4@0.98:11496.9@1.12:10956.2@1.26:10304.8@1.4:9543.57{n}23|%|MPa|Strain in %|Secant modulus in MPa|0.52:12176.9@0.65:11595.4@0.78:11014.1@0.91:10433@1.04:9852.879999999999@1.17:9273.5@1.3:8693.08{n}40|%|MPa|Strain in %|Secant modulus in MPa|0.24:12466.7@0.36:12133.3@0.48:11754.2@0.6:11330@0.72:10861.1@0.84:10347.6@0.96:9789.58@1.08:9187.959999999999@1.2:8540.83{n}60|%|MPa|Strain in %|Secant modulus in MPa|0.22:12000@0.33:11451.5@0.44:10909.1@0.55:10376.4@0.66:9853.030000000001@0.77:9337.66@0.88:8831.82@0.99:8335.35@1.1:7847.27{n}80|%|MPa|Strain in %|Secant modulus in MPa|0.1:12490@0.2:11700@0.3:10953.3@0.4:10247.5@0.5:9580@0.6:8953.33@0.7:8365.709999999999@0.8:7820@0.9:7314.44@1:6849{n}100|%|MPa|Strain in %|Secant modulus in MPa|0.14:4635.71@0.28:3875@0.42:3297.62@0.5600000000000001:2851.79@0.7:2498.57@0.84:2210.71@0.98:1965.31@1.12:1753.57@1.26:1574.6@1.4:1435

应力-应变 (等时的)(蠕变) 23°C 10|%|MPa|Strain in %|Stress in MPa|0:0@0.0727:7.5@0.1325:13.3@0.1951:19.1@0.2604:24.9@0.3282:30.7@0.3983:36.5@0.4705:42.3@0.5447:48.1@0.6207:53.9@0.7024:60{n}100|%|MPa|Strain in %|Stress in MPa|0:0@0.07729999999999999:7.5@0.1419:13.3@0.2103:19.1@0.2822:24.9@0.3572:30.7@0.4351:36.5@0.5155999999999999:42.3@0.5983000000000001:48.1@0.6830000000000001:53.9@0.774:60{n}1000|%|MPa|Strain in %|Stress in MPa|0:0@0.0838:7.5@0.1552:13.3@0.2318:19.1@0.3129:24.9@0.398:30.7@0.4865:36.5@0.578:42.3@0.672:48.1@0.768:53.9@0.8708:60{n}10000|%|MPa|Strain in %|Stress in MPa|0:0@0.09320000000000001:7.5@0.1744:13.3@0.2624:19.1@0.3562:24.9@0.4551:30.7@0.5580000000000001:36.5@0.6642:42.3@0.7731:48.1@0.8839:53.9@1.002:60{n}100000|%|MPa|Strain in %|Stress in MPa|0:0@0.1067:7.5@0.2017:13.3@0.3058:19.1@0.4174:24.9@0.5351:30.7@0.6575:36.5@0.7834:42.3@0.9119:48.1@1.0419:53.9@1.1794:60

应力-应变 (等时的)(蠕变) 40°C 10|%|MPa|Strain in %|Stress in MPa|0:0@0.0801:7.5@0.1332:12.2@0.1876:16.9@0.2431:21.6@0.2994:26.3@0.3564:31@0.4141:35.7@0.4724:40.4@0.5313:45.1@0.5931999999999999:50{n}100|%|MPa|Strain in %|Stress in MPa|0:0@0.0862:7.5@0.1448:12.2@0.2053:16.9@0.2675:21.6@0.3309:26.3@0.3955:31@0.4611:35.7@0.5276:40.4@0.595:45.1@0.666:50{n}1000|%|MPa|Strain in %|Stress in MPa|0:0@0.09569999999999999:7.5@0.1627:12.2@0.2327:16.9@0.3052:21.6@0.3796:26.3@0.4558:31@0.5336:35.7@0.6128:40.4@0.6932:45.1@0.7783:50{n}10000|%|MPa|Strain in %|Stress in MPa|0:0@0.1103:7.5@0.1903:12.2@0.275:16.9@0.3633:21.6@0.4548:26.3@0.5489000000000001:31@0.6454:35.7@0.7441:40.4@0.8447:45.1@0.9515:50{n}100000|%|MPa|Strain in %|Stress in MPa|0:0@0.1329:7.5@0.2329:12.2@0.3402:16.9@0.4531:21.6@0.5708:26.3@0.6926:31@0.8179999999999999:35.7@0.9467:40.4@1.0783:45.1@1.2185:50

应力-应变 (等时的)(蠕变) 60°C 10|%|MPa|Strain in %|Stress in MPa|0:0@0.1692:8@0.2607:12.1@0.3545:16.2@0.4503:20.3@0.5479000000000001:24.4@0.6474:28.5@0.7493:32.6@0.8542999999999999:36.7@0.9635:40.8@1.0811:45{n}100|%|MPa|Strain in %|Stress in MPa|0:0@0.1907:8@0.2962:12.1@0.406:16.2@0.5196:20.3@0.637:24.4@0.7586000000000001:28.5@0.8848:32.6@1.0169:36.7@1.1564:40.8@1.3092:45{n}1000|%|MPa|Strain in %|Stress in MPa|0:0@0.2175:8@0.3407:12.1@0.4711:16.2@0.6082:20.3@0.7522:24.4@0.9036:28.5@1.0634:32.6@1.2334:36.7@1.4159:40.8@1.6191:45{n}10000|%|MPa|Strain in %|Stress in MPa|0:0@0.2506:8@0.3965:12.1@0.5535:16.2@0.7215:20.3@0.9009:24.4@1.0927:28.5@1.2987:32.6@1.5215:36.7@1.7648:40.8@2.0403:45{n}100000|%|MPa|Strain in %|Stress in MPa|0:0@0.2917:8@0.4663:12.1@0.6577:16.2@0.8662:20.3@1.0928:24.4@1.3394:28.5@1.6088:32.6@1.9051:36.7@2.234:40.8@2.6127:45

应力-应变 (等时的)(蠕变) 80°C 10|%|MPa|Strain in %|Stress in MPa|0:0@0.1229:5@0.1941:7.8@0.2674:10.6@0.3431:13.4@0.4215:16.2@0.5028:19@0.5874:21.8@0.6756:24.6@0.7678:27.4@0.8572:30{n}100|%|MPa|Strain in %|Stress in MPa|0:0@0.1498:5@0.2393:7.8@0.3334:10.6@0.4327:13.4@0.5379:16.2@0.6496:19@0.7685999999999999:21.8@0.8957000000000001:24.6@1.0317:27.4@1.1668:30{n}1000|%|MPa|Strain in %|Stress in MPa|0:0@0.1884:5@0.3049:7.8@0.4305:10.6@0.5666:13.4@0.7143:16.2@0.8754:19@1.0513:21.8@1.2439:24.6@1.4553:27.4@1.6703:30{n}10000|%|MPa|Strain in %|Stress in MPa|0:0@0.2438:5@0.4002:7.8@0.5737:10.6@0.7667:13.4@0.9819:16.2@1.2226:19@1.4923:21.8@1.7951:24.6@2.1353:27.4@2.4893:30{n}100000|%|MPa|Strain in %|Stress in MPa|0:0@0.323:5@0.5387:7.8@0.7847:10.6@1.0658:13.4@1.3877:16.2@1.7568:19@2.1805:21.8@2.6673:24.6@3.227:27.4@3.8216:30

蠕变模量-时间 23°C 10|h|MPa|Time in h|Creep modulus in MPa|10:10197.2@100:9561.219999999999@1000:8786.540000000001@10000:7863.87@100000:6838.02{n}20|h|MPa|Time in h|Creep modulus in MPa|10:9753.389999999999@100:9040.200000000001@1000:8193.389999999999@10000:7231.01@100000:6198.6{n}30|h|MPa|Time in h|Creep modulus in MPa|10:9378.190000000001@100:8620.92@1000:7741.16@10000:6773.05@100000:5762.37{n}40|h|MPa|Time in h|Creep modulus in MPa|10:9057.51@100:8274.84@1000:7388.46@10000:6433.72@100000:5456.19{n}50|h|MPa|Time in h|Creep modulus in MPa|10:8781.27@100:7989.49@1000:7110.02@10000:6178.9@100000:5239.09{n}60|h|MPa|Time in h|Creep modulus in MPa|10:8542.139999999999@100:7751.94@1000:6890.22@10000:5988.02@100000:5087.33

蠕变模量-时间 40°C 10|h|MPa|Time in h|Creep modulus in MPa|10:9250.959999999999@100:8547.57@1000:7648.29@10000:6582.13@100000:5415.26{n}20|h|MPa|Time in h|Creep modulus in MPa|10:8924.639999999999@100:8124.68@1000:7135.93@10000:6008.74@100000:4830.05{n}30|h|MPa|Time in h|Creep modulus in MPa|10:8715.549999999999@100:7860.33@1000:6826.79@10000:5674.57@100000:4502{n}40|h|MPa|Time in h|Creep modulus in MPa|10:8557.709999999999@100:7664.23@1000:6600.52@10000:5437.55@100000:4275.18{n}50|h|MPa|Time in h|Creep modulus in MPa|10:8428.860000000001@100:7507.51@1000:6424.26@10000:5254.86@100000:4103.41

蠕变模量-时间 60°C 10|h|MPa|Time in h|Creep modulus in MPa|10:4685.23@100:4141.16@1000:3616.4@10000:3123.54@100000:2670.3{n}20|h|MPa|Time in h|Creep modulus in MPa|10:4512.36@100:3912.66@1000:3344.83@10000:2821.56@100000:2351.99{n}30|h|MPa|Time in h|Creep modulus in MPa|10:4383.62@100:3730.54@1000:3121.77@10000:2572.29@100000:2090.46{n}40|h|MPa|Time in h|Creep modulus in MPa|10:4247.51@100:3544.91@1000:2900.72@10000:2332.12@100000:1846.38{n}45|h|MPa|Time in h|Creep modulus in MPa|10:4162.43@100:3437.21@1000:2779.32@10000:2205.56@100000:1722.36

蠕变模量-时间 80°C 5|h|MPa| Time in h|Creep modulus in MPa|10:4068.35@100:3337.78@1000:2653.93@10000:2050.86@100000:1547.99{n}10|h|MPa| Time in h|Creep modulus in MPa|10:3976.08@100:3196.65@1000:2482.88@10000:1869.21@100000:1371.29{n}15|h|MPa| Time in h|Creep modulus in MPa|10:3870.38@100:3048.44@1000:2309.59@10000:1691.57@100000:1205.45{n}20|h|MPa| Time in h|Creep modulus in MPa|10:3755.05@100:2893.47@1000:2135.79@10000:1520.5@100000:1051.87{n}25|h|MPa| Time in h|Creep modulus in MPa|10:3631.06@100:2733.66@1000:1964.14@10000:1357.86@100000:911.668{n}30|h|MPa| Time in h|Creep modulus in MPa|10:3499.77@100:2571.13@1000:1796.08@10000:1205.16@100000:785.0119999999999

比容-温度(pvT) 0.1|°C|E-3 m³/kg|Spec. volume in °C|Temperature in E-3 m³/kg|20:0.73951@30:0.74071@40:0.74191@50:0.74311@60:0.74431@70:0.74551@80:0.74671@90:0.74791@99.08:0.749@100:0.74934@110:0.75306@120:0.75678@130:0.7605@140:0.76422@150:0.76794@160:0.77166@170:0.77538@180:0.7791@190:0.78282@200:0.78654@210:0.79026@220:0.79398@230:0.7977@240:0.80142@250:0.80514@260:0.80886@270:0.81258{n}40|°C|E-3 m³/kg|Spec. volume in °C|Temperature in E-3 m³/kg|20:0.73385@30:0.73488@40:0.73591@50:0.73694@60:0.7379599999999999@70:0.73898@80:0.73999@90:0.741@100:0.742@110:0.743@111.24:0.74243@120:0.74533@130:0.74863@140:0.75191@150:0.75517@160:0.75842@170:0.76166@180:0.76488@190:0.76808@200:0.7712599999999999@210:0.77443@220:0.77758@230:0.78071@240:0.78383@250:0.78692@260:0.78999@270:0.79305{n}80|°C|E-3 m³/kg|Spec. volume in °C|Temperature in E-3 m³/kg|20:0.72863@30:0.7295199999999999@40:0.73041@50:0.73129@60:0.73217@70:0.73303@80:0.73389@90:0.73473@100:0.7355699999999999@110:0.7364000000000001@120:0.73722@123.4:0.73655@130:0.73852@140:0.74147@150:0.74441@160:0.74732@170:0.75021@180:0.75307@190:0.75591@200:0.75872@210:0.76151@220:0.76427@230:0.767@240:0.76971@250:0.77239@260:0.77504@270:0.77767{n}120|°C|E-3 m³/kg|Spec. volume in °C|Temperature in E-3 m³/kg|20:0.72379@30:0.72457@40:0.72533@50:0.72609@60:0.72684@70:0.7275700000000001@80:0.72829@90:0.72901@100:0.72971@110:0.7304@120:0.73108@130:0.7317399999999999@135.56:0.73123@140:0.73243@150:0.73511@160:0.73776@170:0.74038@180:0.74298@190:0.74554@200:0.74808@210:0.75059@220:0.75306@230:0.75551@240:0.75792@250:0.76031@260:0.76266@270:0.76498{n}160|°C|E-3 m³/kg|Spec. volume in °C|Temperature in E-3 m³/kg|20:0.71929@30:0.71996@40:0.72062@50:0.72126@60:0.7219@70:0.7225200000000001@80:0.7231300000000001@90:0.72373@100:0.72432@110:0.72489@120:0.72544@130:0.72599@140:0.7265200000000001@147.72:0.7263500000000001@150:0.7269099999999999@160:0.72936@170:0.73178@180:0.73416@190:0.73652@200:0.7388400000000001@210:0.74113@220:0.74339@230:0.74561@240:0.74781@250:0.74997@260:0.75209@270:0.75419{n}200|°C|E-3 m³/kg|Spec. volume in °C|Temperature in E-3 m³/kg|20:0.71507@30:0.71565@40:0.71621@50:0.71677@60:0.71731@70:0.71783@80:0.71834@90:0.71884@100:0.71933@110:0.71979@120:0.7202499999999999@130:0.7206900000000001@140:0.72112@150:0.72153@159.88:0.72185@160:0.72188@170:0.72412@180:0.72634@190:0.7285199999999999@200:0.73067@210:0.7327900000000001@220:0.73487@230:0.73692@240:0.73894@250:0.74092@260:0.74287@270:0.74479

拉伸模量-温度 |°C|MPa|Temperature in °C|Tensile modulus in MPa|-40:13050@-20:12360@0:11060@23:11000@40:10360@60:9360@80:8860@100:2790

35% 玻纤