物性表(英文) 

SAN

耐热

良好表面

尺寸稳定

耐化学性

卫浴洁具

电池外壳

储物箱

马桶座便盖

厨房电器

透明

注塑

挤出

N粘度-剪切速度 220|1/s|Pa s|Shear rate in 1/s|Viscosity in Pa s|2.525:8792.709999999999@4.758:7358.09@8.968:5760.3@16.901:4241.22@31.853:2952.81@60.033:1955.91@113.143:1240.85@213.237:759.409@401.882:451.842@757.4160000000001:263.549{n}245|1/s|Pa s|Shear rate in 1/s|Viscosity in Pa s|7.996:2776.59@15.07:2323.15@28.401:1818.89@53.527:1339.15@100.88:932.355@190.127:617.582@358.326:391.802@675.327:239.786@1272.77:142.671@2398.75:83.2167{n}270|1/s|Pa s|Shear rate in 1/s|Viscosity in Pa s|18.836:1178.68@35.5:986.194@66.905:772.116@126.094:568.472@237.646:395.782@447.886:262.163@844.117:166.319@1590.88:101.789@2998.29:60.5635@5650.8:35.3253

剪切应力-剪切速率 220|1/s|Pa|Shear rate in 1/s|Shearstress in Pa|2.525:22201.6@4.758:35009.8@8.968:51658.4@16.901:71680.89999999999@31.853:94056@60.033:117419@113.143:140393@213.237:161934@401.882:181587@757.4160000000001:199616{n}245|1/s|Pa|Shear rate in 1/s|Shearstress in Pa|7.996:22201.6@15.07:35009.8@28.401:51658.4@53.527:71680.89999999999@100.88:94056@190.127:117419@358.326:140393@675.327:161934@1272.77:181587@2398.75:199616{n}270|1/s|Pa|Shear rate in 1/s|Shearstress in Pa|18.836:22201.6@35.5:35009.9@66.905:51658.4@126.094:71680.89999999999@237.646:94056@447.886:117419@844.117:140393@1590.88:161934@2998.29:181587@5650.8:199616

应力-应变 -40|%|Mpa|Strain in %|Stress in MPa|0:0@0.36:21.08@0.72:39.24@1.08:54.78@1.44:68.01000000000001@1.8:79.26000000000001@2.16:88.81@2.52:96.98999999999999@2.88:104.11@3.24:110.47@3.6:116.39{n}-20|%|Mpa|Strain in %|Stress in MPa|0:0@0.31:15.56@0.62:29.99@0.93:43.26@1.24:55.37@1.55:66.3@1.86:76.04000000000001@2.17:84.56@2.48:91.86@2.79:97.92@3.1:102.73{n}0|%|Mpa|Strain in %|Stress in MPa|0:0@0.29:12.95@0.58:25.28@0.87:36.92@1.16:47.83@1.45:57.92@1.74:67.13@2.03:75.41@2.32:82.68000000000001@2.61:88.88@2.9:93.95{n}23|%|Mpa|Strain in %|Stress in MPa|0:0@0.33:14.34@0.66:27.45@0.99:39.3@1.32:49.83@1.65:59.02@1.98:66.8@2.31:73.15000000000001@2.64:78.01000000000001@2.97:81.34999999999999@3.3:83.11{n}40|%|Mpa|Strain in %|Stress in MPa|0:0@0.28:11.01@0.5600000000000001:21.69@0.84:31.84@1.12:41.25@1.4:49.71@1.68:57@1.96:62.92@2.24:67.25@2.52:69.78@2.8:70.31{n}60|%|Mpa|Strain in %|Stress in MPa|0:0@0.48:16.01@0.72:23.95@0.96:31.12@1.2:37.18@1.44:41.95@1.68:45.38@1.92:47.5@2.16:48.46@2.4:48.46{n}80|%|Mpa|Strain in %|Stress in MPa|0:0@0.4:11.45@0.6:17.02@0.8:22@1:26.17@1.2:29.42@1.4:31.74@1.6:33.2@1.8:33.91@2:34.04

正割模量-应变 -40|%|MPa|Strain in %|Secant modulus in MPa|0.36:5855.56@0.72:5450@1.08:5072.22@1.44:4722.92@1.8:4403.33@2.16:4111.57@2.52:3848.81@2.88:3614.93@3.24:3409.57@3.6:3233.06{n}-20|%|MPa|Strain in %|Secant modulus in MPa|0.31:5019.35@0.62:4837.1@0.93:4651.61@1.24:4465.32@1.55:4277.42@1.86:4088.17@2.17:3896.77@2.48:3704.03@2.79:3509.68@3.1:3313.87{n}0|%|MPa|Strain in %|Secant modulus in MPa|0.29:4465.52@0.58:4358.62@0.87:4243.68@1.16:4123.28@1.45:3994.48@1.74:3858.05@2.03:3714.78@2.32:3563.79@2.61:3405.36@2.9:3239.66{n}23|%|MPa|Strain in %|Secant modulus in MPa|0.33:4345.45@0.66:4159.09@0.99:3969.7@1.32:3775@1.65:3576.97@1.98:3373.74@2.31:3166.67@2.64:2954.92@2.97:2739.06@3.3:2518.48{n}40|%|MPa|Strain in %|Secant modulus in MPa|0.28:3932.14@0.5600000000000001:3873.21@0.84:3790.48@1.12:3683.04@1.4:3550.71@1.68:3392.86@1.96:3210.2@2.24:3002.23@2.52:2769.05@2.8:2511.07{n}60|%|MPa|Strain in %|Secant modulus in MPa|0.48:3335.42@0.72:3326.39@0.96:3241.67@1.2:3098.33@1.44:2913.19@1.68:2701.19@1.92:2473.96@2.16:2243.52@2.4:2019.17{n}80|%|MPa|Strain in %|Secant modulus in MPa|0.4:2862.5@0.6:2836.67@0.8:2750@1:2617@1.2:2451.67@1.4:2267.14@1.6:2075@1.8:1883.89@2:1702

应力-应变 (等时的)(蠕变) 23°C 10|%|MPa|Strain in %|Stress in MPa|0:0@0.1515:5@0.2381:7.8@0.3259:10.6@0.4146:13.4@0.5044999999999999:16.2@0.5955:19@0.6876:21.8@0.7808:24.6@0.8752:27.4@0.964:30{n}100|%|MPa|Strain in %|Stress in MPa|0:0@0.1662:5@0.2637:7.8@0.3642:10.6@0.4679:13.4@0.575:16.2@0.6857:19@0.8002:21.8@0.9188:24.6@1.0417:27.4@1.16:30{n}1000|%|MPa|Strain in %|Stress in MPa|0:0@0.188:5@0.3024:7.8@0.4237:10.6@0.5526:13.4@0.6897:16.2@0.8359:19@0.9922:21.8@1.1595:24.6@1.339:27.4@1.5177:30{n}10000|%|MPa|Strain in %|Stress in MPa|0:0@0.2204:5@0.3613:7.8@0.5163:10.6@0.6872:13.4@0.8764:16.2@1.0862:19@1.3195:21.8@1.5796:24.6@1.8701:27.4@2.1705:30{n}100000|%|MPa|Strain in %|Stress in MPa|0:0@0.2685:5@0.4507:7.8@0.6601:10.6@0.9014:13.4@1.1803:16.2@1.5031:19@1.8777:21.8@2.3127:24.6@2.8185:27.4@3.3618:30

应力-应变 (等时的)(蠕变) 40°C 10|%|MPa|Strain in %|Stress in MPa|0:0@0.1435:5@0.2146:7.2@0.2904:9.4@0.371:11.6@0.456:13.8@0.5455:16@0.6392:18.2@0.7371:20.4@0.8391:22.6@0.9548:25{n}100|%|MPa|Strain in %|Stress in MPa|0:0@0.1588:5@0.2459:7.2@0.3427:9.4@0.4486:11.6@0.5633:13.8@0.6861:16@0.8164:18.2@0.9539:20.4@1.0979:22.6@1.262:25{n}1000|%|MPa|Strain in %|Stress in MPa|0:0@0.193:5@0.3147:7.2@0.4563:9.4@0.616:11.6@0.7921:13.8@0.9828:16@1.1865:18.2@1.4019:20.4@1.6274:22.6@1.8834:25{n}10000|%|MPa|Strain in %|Stress in MPa|0:0@0.2689:5@0.4661:7.2@0.7038:9.4@0.9767:11.6@1.2799:13.8@1.6089:16@1.9596:18.2@2.3279:20.4@2.7105:22.6@3.1402:25{n}100000|%|MPa|Strain in %|Stress in MPa|0:0@0.4376:5@0.7992:7.2@1.2424:9.4@1.7536:11.6@2.32:13.8@2.9303:16@3.574:18.2@4.2421:20.4@4.9263:22.6@5.6826:25

应力-应变 (等时的)(蠕变) 60°C 10|%|MPa|Strain in %|Stress in MPa|0:0@0.2658:5@0.3637:6.7@0.4679:8.4@0.5800999999999999:10.1@0.7019:11.8@0.8346:13.5@0.9799:15.2@1.1394:16.9@1.3146:18.6@1.4717:20{n}100|%|MPa|Strain in %|Stress in MPa|0:0@0.3549:5@0.4888:6.7@0.634:8.4@0.7932:10.1@0.9692:11.8@1.1646:13.5@1.3822:15.2@1.6247:16.9@1.8949:18.6@2.14:20{n}1000|%|MPa|Strain in %|Stress in MPa|0:0@0.513:5@0.7108:6.7@0.9285:8.4@1.1709:10.1@1.4428:11.8@1.749:13.5@2.0944:15.2@2.4837:16.9@2.9217:18.6@3.3222:20{n}10000|%|MPa|Strain in %|Stress in MPa|0:0@0.7936:5@1.1045:6.7@1.4505:8.4@1.8401:10.1@2.2818:11.8@2.7841:13.5@3.3554:15.2@4.004:16.9@4.7384:18.6@5.4133:20{n}100000|%|MPa|Strain in %|Stress in MPa|0:0@1.2912:5@1.8027:6.7@2.376:8.4@3.0262:10.1@3.7684:11.8@4.6174:13.5@5.588:15.2@6.6949:16.9@7.9527:18.6@9.1121:20

应力-应变 (等时的)(蠕变) 80°C 10|%|MPa|Strain in %|Stress in MPa|0:0@0.3973:5@0.4939:5.9@0.5963000000000001:6.8@0.704:7.7@0.8168:8.6@0.9345:9.5@1.0568:10.4@1.1836:11.3@1.3146:12.2@1.4346:13{n}100|%|MPa|Strain in %|Stress in MPa|0:0@0.6039:5@0.7612:5.9@0.9295:6.8@1.1083:7.7@1.2969:8.6@1.4949:9.5@1.7018:10.4@1.9173:11.3@2.141:12.2@2.3466:13{n}1000|%|MPa|Strain in %|Stress in MPa|0:0@1.0045:5@1.2793:5.9@1.5755:6.8@1.8919:7.7@2.2272:8.6@2.5806:9.5@2.9513:10.4@3.3385:11.3@3.7417:12.2@4.1129:13{n}10000|%|MPa|Strain in %|Stress in MPa|0:0@1.7811:5@2.2836:5.9@2.8277:6.8@3.4106:7.7@4.0301:8.6@4.6846:9.5@5.3723:10.4@6.0918:11.3@6.8421:12.2@7.5338:13{n}100000|%|MPa|Strain in %|Stress in MPa|0:0@3.2869:5@4.2308:5.9@5.2549:6.8@6.354:7.7@7.524:8.6@8.7613:9.5@10.0627:10.4@11.4255:11.3@12.8474:12.2@14.1592:13

蠕变模量-时间 23°C 5|h|MPa|Time in h|Creep modulus in MPa|10:3300.33@100:3008.42@1000:2659.57@10000:2268.6@100000:1862.2{n}10|h|MPa|Time in h|Creep modulus in MPa|10:3257.23@100:2920.48@1000:2518.24@10000:2075.38@100000:1631.98{n}15|h|MPa|Time in h|Creep modulus in MPa|10:3220.09@100:2837.3@1000:2381.38@10000:1891.72@100000:1420.74{n}20|h|MPa|Time in h|Creep modulus in MPa|10:3183.37@100:2754.3@1000:2245.91@10000:1714.33@100000:1226.65{n}25|h|MPa|Time in h|Creep modulus in MPa|10:3147.8@100:2670.74@1000:2110.92@10000:1544.14@100000:1050.4{n}30|h|MPa|Time in h|Creep modulus in MPa|10:3112.03@100:2586.21@1000:1976.68@10000:1382.17@100000:892.379

蠕变模量-时间 40°C 5|h|MPa|Time in h|Creep modulus in MPa|10:3484.32@100:3148.61@1000:2590.67@10000:1859.43@100000:1142.6{n}10|h|MPa|Time in h|Creep modulus in MPa|10:3206.01@100:2697.75@1000:2007.63@10000:1290.52@100000:727.023{n}15|h|MPa|Time in h|Creep modulus in MPa|10:2974.55@100:2383.5@1000:1677.07@10000:1029.93@100000:566.437{n}20|h|MPa|Time in h|Creep modulus in MPa|10:2781.64@100:2154.21@1000:1468.47@10000:885.034@100000:485.531{n}25|h|MPa|Time in h|Creep modulus in MPa|10:2618.35@100:1980.98@1000:1327.39@10000:796.128@100000:439.939

蠕变模量-时间 60°C 5|h|MPa|Time in h|Creep modulus in MPa|10:1881.11@100:1408.85@1000:974.659@10000:630.04@100000:387.237{n}10|h|MPa|Time in h|Creep modulus in MPa|10:1744.45@100:1276.49@1000:865.148@10000:550.7140000000001@100000:334.946{n}15|h|MPa|Time in h|Creep modulus in MPa|10:1559.11@100:1106.73@1000:731.154@10000:456.72@100000:274.377{n}20|h|MPa|Time in h|Creep modulus in MPa|10:1358.97@100:934.579@1000:602.011@10000:369.46@100000:219.488

蠕变模量-时间 80°C 2|h|MPa| Time in h|Creep modulus in MPa|10:1431.9@100:979.379@1000:606.798@10000:349.184@100000:191.533{n}4|h|MPa| Time in h|Creep modulus in MPa|10:1327.39@100:886.708@1000:539.292@10000:306.476@100000:166.832{n}6|h|MPa| Time in h|Creep modulus in MPa|10:1188.04@100:769.787@1000:457.558@10000:256.157@100000:138.21{n}8|h|MPa| Time in h|Creep modulus in MPa|10:1079.56@100:683.696@1000:399.674@10000:221.414@100000:118.758{n}10|h|MPa| Time in h|Creep modulus in MPa|10:998.125@100:621.597@1000:359.137@10000:197.526@100000:105.524{n}12|h|MPa| Time in h|Creep modulus in MPa|10:933.793@100:574.024@1000:328.713@10000:179.843@100000:95.8019{n}13|h|MPa| Time in h|Creep modulus in MPa|10:906.176@100:553.9930000000001@1000:316.079@10000:172.556@100000:91.81310000000001

比容-温度(pvT) 0.1|°C|E-3 m³/kg|Spec. volume in °C|Temperature in E-3 m³/kg|20:0.93305@30:0.93491@40:0.93677@50:0.93863@60:0.94049@70:0.94235@80:0.94421@90:0.94607@100:0.9479300000000001@100.38:0.948@110:0.95362@120:0.95946@130:0.9653@140:0.97114@150:0.97698@160:0.98282@170:0.98866@180:0.9945000000000001@190:1.00034@200:1.00618@210:1.01202@220:1.01786@230:1.0237@240:1.02954@250:1.03538@260:1.04122@270:1.04706{n}40|°C|E-3 m³/kg|Spec. volume in °C|Temperature in E-3 m³/kg|20:0.92392@30:0.9255100000000001@40:0.9271@50:0.9286799999999999@60:0.93026@70:0.93182@80:0.93338@90:0.93493@100:0.93647@110:0.9379999999999999@111.78:0.93703@120:0.94125@130:0.94635@140:0.95142@150:0.95647@160:0.96148@170:0.9664700000000001@180:0.97143@190:0.97636@200:0.98125@210:0.98611@220:0.99094@230:0.99574@240:1.0005@250:1.00522@260:1.0099@270:1.01455{n}80|°C|E-3 m³/kg|Spec. volume in °C|Temperature in E-3 m³/kg|20:0.91568@30:0.91706@40:0.91843@50:0.91979@60:0.92113@70:0.9224599999999999@80:0.92378@90:0.92509@100:0.92638@110:0.92766@120:0.92892@123.18:0.92769@130:0.93082@140:0.93536@150:0.93987@160:0.94433@170:0.94875@180:0.95313@190:0.95746@200:0.96175@210:0.966@220:0.9702@230:0.97435@240:0.97845@250:0.98251@260:0.98651@270:0.99047{n}120|°C|E-3 m³/kg|Spec. volume in °C|Temperature in E-3 m³/kg|20:0.9081900000000001@30:0.90939@40:0.9105799999999999@50:0.9117499999999999@60:0.9129@70:0.91404@80:0.91517@90:0.91627@100:0.91736@110:0.91844@120:0.91949@130:0.92053@134.58:0.91957@140:0.92181@150:0.92592@160:0.92998@170:0.9340000000000001@180:0.93796@190:0.94187@200:0.94574@210:0.94955@220:0.95331@230:0.95702@240:0.96068@250:0.96429@260:0.96784@270:0.97134{n}160|°C|E-3 m³/kg|Spec. volume in °C|Temperature in E-3 m³/kg|20:0.90132@30:0.90237@40:0.9034@50:0.90441@60:0.90541@70:0.90639@80:0.90735@90:0.90829@100:0.90921@110:0.91012@120:0.911@130:0.91187@140:0.91272@145.98:0.91238@150:0.9139@160:0.91765@170:0.92136@180:0.92501@190:0.9286@200:0.93215@210:0.93564@220:0.93908@230:0.94246@240:0.94579@250:0.94907@260:0.95229@270:0.95546{n}200|°C|E-3 m³/kg|Spec. volume in °C|Temperature in E-3 m³/kg|20:0.89497@30:0.89589@40:0.89679@50:0.89767@60:0.8985300000000001@70:0.89937@80:0.90019@90:0.901@100:0.90178@110:0.90254@120:0.90329@130:0.90401@140:0.90471@150:0.90539@157.38:0.90593@160:0.90684@170:0.9103@180:0.9137@190:0.91705@200:0.92034@210:0.92359@220:0.92677@230:0.9298999999999999@240:0.93298@250:0.9360000000000001@260:0.93897@270:0.9418800000000001

拉伸模量-温度 |°C|MPa|Temperature in °C|Tensile modulus in MPa|-40:5030@-20:4430@0:4030@23:3900@40:3590@60:3090@80:2590