DESCRIPTION Terluran® GP-22 is an easy-flow, general purpose injection molding grade with high resistance to impact and heat distortion; intended for a wide range of applications, particularly in the housings sector.
FEATURES
- Excellent colorability
- Medium flow
- Good impact resistance
- Good heat distortion resistance
- High quality surface finish and gloss
- Great mechanical strength and rigidity
APPLICATIONS
- Injection molding
- Appliance housings
- Household and sanitary appliances
- Toys
- Automotive components
- Consumer products
| 原厂资料 | 物性表-ISO(英文) 物性表-ASTM(英文) | |||
| 产品特性 | 高冲击耐热良好表面高光泽易着色高流动 | |||
| 应用产品 | 玩具家居用品外壳家用电器汽车零部件卫浴洁具 | |||
| 成型方式 | 注塑 | |||
| 曲线坐标点 | N粘度-剪切速度剪切应力-剪切速率动态剪切模量-温度应力-应变正割模量-应变应力-应变 (等时的) 23°C应力-应变 (等时的) 60°C蠕变模量-时间 23°C蠕变模量-时间 60°C比容-温度(pvT)拉伸模量-温度 | |||
| 物理性能 | 值/单位 | 测试标准 | 测试条件 |
|---|---|---|---|
密度 | 1.04 g/cm³ | ISO 1183 | |
密度 | 1.04 - | ASTM D792 | |
熔体体积流动速率(MVR) | |||
220°C/10.0 kg | 19 cm³/10 min | ISO 1133 | |
230℃/3.8 kg | 4.8 cm³/10 min | ASTM D 1238 | |
熔体质量流动速率(MFR) | |||
200 ℃/5 Kg | 1.5 g/10 min | ASTM D 1238 | |
220℃/10 kg | 19 g/10 min | ASTM D 1238 | |
收缩率 | |||
- | 0.004~0.007 in/in | ASTM D 955 | |
- | 0.4~0.7 % | ISO 294-4 | |
吸水率 | 1 % | ASTM D570 | Saturated at 23 °C |
吸水率 | 1 % | ISO 62 | Saturated at 23 °C |
吸湿率 | 0.22 % | ISO 62 | Equilibrium 23 °C/50% RH |
| 机械性能 | 值/单位 | 测试标准 | 测试条件 |
拉伸强度 | |||
屈服(yld) | 6520 psi | ASTM D638 | 23 °C |
屈服(yld) | 45 Mpa | ISO 527 | |
拉伸延伸率 | |||
屈服(yld) | 2.6 % | ISO 527 | |
标称断裂伸长率 | 10 % | ISO 527 | |
- | 2.6 % | ASTM D 638 | |
弯曲强度 | |||
- | 9430 psi | ASTM D790 | 23 °C |
- | 65 Mpa | ISO 178 | |
弯曲模量 | 334000 psi | ASTM D790 | 23 °C |
拉伸模量 | 334000 psi | ASTM D638 | |
拉伸模量 | 2300 Mpa | ISO 527 | |
| 冲击性能 | 值/单位 | 测试标准 | 测试条件 |
简支梁缺口(Charpy Notched) | |||
-30℃ (-22℉) | 8 kJ/m² | ISO 179/1eA | |
23℃ (73℉) | 22 kJ/m² | ISO 179/1eA | |
简支梁无缺口(Charpy Unnotched) | |||
-30℃ (-22℉) | 100 kJ/m² | ISO 179/1eU | |
23℃ (73℉) | 180 kJ/m² | ISO 179/1eU | |
悬臂梁缺口(Izod Notched) | |||
-30℃ (-22℉) | 1.1 ft·lb/in | ASTM D256 | |
-30℃ (-22℉) | 8 kJ/m² | ISO 180/A | |
-18℃ (0℉) | 1.9 ft·lb/in | ASTM D 256 | |
23℃ (73℉) | 5.6 ft·lb/in | ASTM D256 | |
23℃ (73℉) | 26 kJ/m² | ISO 180/A | |
| 硬度性能 | 值/单位 | 测试标准 | 测试条件 |
洛氏硬度R | 103 R | ASTM D785 | |
球压硬度 | 97 Mpa | ISO 2039-1 | |
| 热学性能 | 值/单位 | 测试标准 | 测试条件 |
热变形温度(HDT) | |||
0.45 Mpa (66 psi)（4.6kg/cm²） | 219 °F | ASTM D648 | Annealed |
0.45 Mpa (66 psi)（4.6kg/cm²） | 195 °F | ASTM D648 | Unannealed |
0.45 Mpa (66 psi)（4.6kg/cm²） | 99 °C | ISO 75 | annealed 4 h/80 °C |
1.8 Mpa (264 psi)（18.6kg/cm²） | 210 °F | ASTM D648 | Annealed |
1.8 Mpa (264 psi)（18.6kg/cm²） | 172 °F | ASTM D648 | Unannealed |
1.8 Mpa (264 psi)（18.6kg/cm²） | 94 °C | ISO 75 | annealed 4 h/80 °C |
维卡软化温度(Vicat) | 204 °F | ISO 306 | VST/A/50 (10N, 50 °C/h) |
维卡软化温度(Vicat) | 105 °C | ISO 306 | VST/A/50 (10N, 50 °C/h) |
维卡软化温度(Vicat) | 96 °C | ISO 306 | VST/B/50 (50N, 50 °C/h) |
线性膨胀系数(CLTE) | |||
- | 80~110 E-6/°C | ISO 11359 | |
导热系数 | 0.17 W/(m K) | DIN 52612-1 | |
加工温度 | 220~260 °C | - | |
模具温度 | 30~80 °C | - | |
| 电学性能 | 值/单位 | 测试标准 | 测试条件 |
体积电阻率 | 1.0E+13 Ohm-m | ASTM D257 | min. |
体积电阻率 | 1.0E+13 Ohm-m | IEC 60093 | min. |
表面电阻率 | 1.0E+13 Ohm | IEC 60093 | min. |
介电常数(DK) | |||
100Hz | 2.9 - | IEC 60250 | |
1MHz | 2.8 - | IEC 60250 | |
1MHz | 2.8 - | ASTM D 150 | 0,0394 in |
耗散因数(DF) | |||
100Hz | 48 E-4 | IEC 60250 | |
1MHz | 79 E-4 | IEC 60250 | |
| 其他性能 | 值/单位 | 测试标准 | 测试条件 |
黄色指数(YI) | 13 - | DIN 6167 |