| Physical | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Density/Specific Gravity |
*** g/cm³
| ISO 1183 | Dry |
Mold Shrinkage | | | |
- |
***~*** % | ASTM D955 | Dry |
Water Absorption |
*** %
| ISO 62 | Dry |
| Mechanical | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Tensile Strength | | | |
- |
*** Mpa | ISO 527 | 1.6% moist. |
- |
*** Mpa | ISO 527 | Dry |
Flexural Modulus |
*** Mpa
| ISO 178 | 1.6% moist. |
Flexural Modulus |
*** Mpa
| ISO 178 | Dry |
Flexural Strength | | | |
- |
*** Mpa | ISO 178 | 1.6% moist. |
- |
*** Mpa | ISO 178 | Dry |
| Impact | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Charpy Notched Impact Strengh | | | |
-30℃ (-22℉) |
*** kJ/m² | ISO 179/1eA | Dry |
23℃ (73℉) |
*** kJ/m² | ISO 179/1eA | 1.6% moist. |
23℃ (73℉) |
*** kJ/m² | ISO 179/1eA | Dry |
Izod Notched Impact Strengh | | | |
-30℃ (-22℉) |
*** J/m | ASTM D256 | 6.4mm,Dry |
23℃ (73℉) |
*** J/m | ASTM D256 | 6.4mm,1.6% moist. |
23℃ (73℉) |
*** J/m | ASTM D256 | 6.4mm,Dry |
| Hardness | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Rockwell R |
*** R
| ISO 2039 | 1.6% moist. |
Rockwell R |
*** R
| ISO 2039 | Dry |
| Thermal | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Heat Deflection Temperature(HDT) | | | |
0.45 Mpa (66 psi)（4.6kg/cm²） |
*** °C | ASTM D648 | 6.4mm,1.6% moist. |
0.45 Mpa (66 psi)（4.6kg/cm²） |
*** °C | ASTM D648 | 6.4mm,Dry |
0.45 Mpa (66 psi)（4.6kg/cm²） |
*** °C | ISO 75 | 1.6% moist. |
0.45 Mpa (66 psi)（4.6kg/cm²） |
*** °C | ISO 75 | Dry |
1.8 Mpa (264 psi)（18.6kg/cm²） |
*** °C | ASTM D648 | 6.4mm,1.6% moist. |
1.8 Mpa (264 psi)（18.6kg/cm²） |
*** °C | ASTM D648 | 6.4mm,Dry |
1.8 Mpa (264 psi)（18.6kg/cm²） |
*** °C | ISO 75 | 1.6% moist. |
1.8 Mpa (264 psi)（18.6kg/cm²） |
*** °C | ISO 75 | Dry |
Coefficient of Linear Thermal Expansion | | | |
Flow |
*** E-6/°C | ISO 11359 | Dry |
| Flammability | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Flame Rating | | | |
HB |
*** mm | UL94 | Dry |
The information presented on this datasheet was acquired by AjiEng.com from the producer of the material. AjiEng.com makes substantial efforts to assure the accuracy of this data. However, AjiEng.com assumes no responsibility for the data values and strongly encourages that upon final material selection, data points are validated with the material supplier.