Ube Nylon 5034B is a PA6/6.6 Copolyamide, produced by continuous polymerization process. It is a high viscosity grade suitable for numerous applications. The grade can be used for cast film and blown film (air cooled). This material has following featur
| Original Document | Technical Datasheet(English) | |||
| Features | Food ContactHigh Viscosity | |||
| Processing | Extrusion | |||
| Compliance | EU 2011/10/EC | |||
| Physical | Value/Unit(Sign in to View) | Test Standard | Test Condition |
|---|---|---|---|
Density/Specific Gravity | *** g/cm³ | ISO 1183 | |
Viscosity | *** - | Internal | 96%H2SO4,1,0g/100ml |
| Mechanical | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Coefficient of Friction | *** - | ASTM 1894 | Dynamic |
Coefficient of Friction | *** - | ASTM 1894 | Static |
| Thermal | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Melt Temperature(Tm) | *** °C | ISO 11357 | |
| Electrical | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Surface Resistivity | *** Ohm | Internal | |
| Optical | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Haze | *** % | ASTM D1003 | |
Gloss | *** % | ASTM D 523 | |
| Film | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Tensile Strength | |||
Yield | *** Mpa | ASTM D 882 | |
Break | *** Mpa | ASTM D 882 | |
Tensile Elongation | |||
Break | *** % | ASTM D 882 | |
Tensile Modulus | *** Mpa | ASTM D 882 | |
Piercing strength | *** N | JAS P 1019 | |
Piercing elongation | *** mm | JAS P 1019 | |
Flex crack resistance | *** hole/0,04m2 | MIL B 131B | 23 °C,1000 cycle |
Gelbo Flex Testing | *** hole/0,04m2 | MIL B 131B | 5 °C,100 cycle |
Water Vapor Transmission Rate | *** g.mm/m².24hr | JIS Z 0208 | |
Oxygen permeability | *** ml/m2 day | ASTM D 3985 |
The information presented on this datasheet was acquired by AjiEng.com from the producer of the material. AjiEng.com makes substantial efforts to assure the accuracy of this data. However, AjiEng.com assumes no responsibility for the data values and strongly encourages that upon final material selection, data points are validated with the material supplier.