UL rated HB as of 10/97. 200 series recommended when V-2 rating required. Automotive lens applications. Medium viscosity. UV-stabilized. Transparent colors only.
| 原厂资料 | 物性表(英文) | |||
| 产品特性 | 抗紫外线中粘度 | |||
| 添加助剂 | 紫外线稳定剂 | |||
| 颜色形状 | 透明 | |||
| 物理性能 | 值/单位 | 测试标准 | 测试条件 |
|---|---|---|---|
密度 | 1.2 g/cm³ | ASTM D792 | |
熔体质量流动速率(MFR) | |||
300℃/1.2 kg | 11 g/10min | ASTM D1238 | |
收缩率 | |||
纵向(Flow) | 0.5~0.7 % | Internal | flow, 3.2 mm |
吸水率 | 0.15 % | ASTM D570 | 24 hours |
| 机械性能 | 值/单位 | 测试标准 | 测试条件 |
拉伸强度 | |||
屈服(yld) | 62 Mpa | ASTM D638 | Type I, 50 mm/min |
拉伸延伸率 | |||
断裂(brk) | 130 % | ASTM D638 | Type I, 50 mm/min |
弯曲强度 | |||
屈服(yld) | 96 Mpa | ASTM D790 | 1.3 mm/min, 50 mm span |
弯曲模量 | 2340 Mpa | ASTM D790 | 1.3 mm/min, 50 mm span |
| 冲击性能 | 值/单位 | 测试标准 | 测试条件 |
悬臂梁缺口(Izod Notched) | |||
23℃ (73℉) | 801 J/m | ASTM D256 | |
仪器化落镖冲击能量 | |||
23℃ (73℉)峰值 | 63 J | ASTM D3763 | |
落锤冲击 | 169 J | ASTM D 3029 | |
拉伸冲击 | 577 kJ/m² | ASTM D 1822 | Type S |
| 热学性能 | 值/单位 | 测试标准 | 测试条件 |
热变形温度(HDT) | |||
1.8 Mpa (264 psi)（18.6kg/cm²） | 132 °C | ASTM D648 | 6.4 mm, unannealed |
相对温度指数(RTI) | |||
冲击Imp,- | 130 °C | UL 746B | |
电气Elec,- | 130 °C | UL 746B | |
强度Str,- | 130 °C | UL 746B | |
| 燃烧性能 | 值/单位 | 测试标准 | 测试条件 |
UL 防火等级 | |||
HB | 1.47 mm | UL94 | |
紫外线暴露,水暴露试验和浸渍 | F1 - | UL 746C | |
| 电学性能 | 值/单位 | 测试标准 | 测试条件 |
相对漏电起痕指数(CTI ) | |||
- | 2 PLC | UL 746A | |
高电压电弧起痕速率(HVTR) | 2 PLC | UL 746A | |
热线圈起燃性(HWI) | 4 PLC | UL 746A | |
高电流电弧起燃性(HAI) | 1 PLC | UL 746A | surface |
| 光学性能 | 值/单位 | 测试标准 | 测试条件 |
透光率 | 88 % | ASTM D1003 | 2.54 mm |
此物性表中的信息由阿技材料库从该材料的生产商处获得。阿技材料库尽最大努力确保此数据的准确性。 但是阿技材料库对这些数据值不承担任何责任，并强烈建议在最终选择材料前，就数据值与材料供应商进行验证。