40% GR, provides improved mechanical properties and UL94V-1 rated at 0.058". Internal mold release added
| Original Document | ||||
| Features | Filled & Reinforced | |||
| Additive | Release Agent | |||
| Reinforced | 40% Glass Fiber | |||
| Physical | Value/Unit(Sign in to View) | Test Standard | Test Condition |
|---|---|---|---|
Density/Specific Gravity | *** g/cm³ | ASTM D792 | |
Density/Specific Gravity | *** g/cm³ | ASTM D792 | |
Melt Mass Flow Rate(MFR) | |||
300°C/5.0 kg | *** g/10 min | ASTM D 1238 | |
Mold Shrinkage | |||
Flow | ***~*** % | Internal | |
Water Absorption | *** % | ASTM D570 | |
Water Absorption | *** % | ASTM D570 | |
Specific Volume | *** cm³/g | ASTM D792 | |
Abrasion resistance | *** mg/1000cy | ASTM D 1044 | CS-17, 1 kg |
| Mechanical | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Tensile Strength | |||
Break | *** Mpa | ASTM D638 | Type I, 5 mm/min |
Tensile Elongation | |||
Break | *** % | ASTM D638 | Type I, 5 mm/min |
Flexural Modulus | *** Mpa | ASTM D790 | 1.3 mm/min, 50 mm span |
Flexural Strength | |||
Yield | *** Mpa | ASTM D790 | 1.3 mm/min, 50 mm span |
| Impact | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Izod Notched Impact Strengh | |||
23℃ (73℉) | *** J/m | ASTM D256 | |
Izod Unnotched Impact Strengh | |||
23℃ (73℉) | *** J/m | ASTM D4812 | |
Falling Dart Impact | *** J | ASTM D 3029 | |
Tensile Impact | *** kJ/m² | ASTM D 1822 | Type S |
| Hardness | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Rockwell M | *** M | ASTM D 785 | |
Rockwell R | *** R | ASTM D785 | |
| Thermal | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Heat Deflection Temperature(HDT) | |||
0.45 Mpa (66 psi)（4.6kg/cm²） | *** °C | ASTM D648 | 6.4 mm, unannealed |
1.8 Mpa (264 psi)（18.6kg/cm²） | *** °C | ASTM D648 | 6.4 mm, unannealed |
Vicat Softening Temperature(VST) | *** °C | ASTM D1525 | |
Relative Temperature Index(RTI), Imp | |||
- | *** °C | UL 746B | |
Relative Temperature Index(RTI), Elec | |||
- | *** °C | UL 746B | |
Relative Temperature Index(RTI), Str | |||
- | *** °C | UL 746B | |
Specific Heat | *** J/g-°C | ASTM C 351 | |
Coefficient of Linear Thermal Expansion | |||
Flow | *** E-6/°C | ASTM E831 | -40°C to 95°C, flow |
Thermal Conductivity | *** W/m-°C | ASTM C 177 | |
| Flammability | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Flame Rating | |||
V-1 | *** mm | UL94 | |
V-0 | *** mm | UL94 | |
| Electrical | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Volume Resistivity | *** Ohm-cm | ASTM D257 | |
Dielectric Constant(Permittivity) | |||
50/60 Hz | *** - | ASTM D150 | |
1MHz | *** - | ASTM D 150 | |
Dissipation Factor | |||
50/60 Hz | *** E-4 | ASTM D 150 | |
1MHz | *** E-4 | ASTM D150 | |
Comparative Tracking Index (CTI) | |||
- | *** PLC | UL 746A | |
Dielectric Strength | *** kV/mm | ASTM D149 | in air, 3.2 mm |
Arc Resistance | *** PLC | ASTM D495 | Tungsten |
High Voltage Arc Tracking Rate(HVTR) | *** PLC | UL 746A | |
Hot Wire Ignition(HWI) | PLC | UL 746A | |
High Ampere Arc Ignition(HAI) | *** PLC | UL 746A | surface |
The information presented on this datasheet was acquired by AjiEng.com from the producer of the material. AjiEng.com makes substantial efforts to assure the accuracy of this data. However, AjiEng.com assumes no responsibility for the data values and strongly encourages that upon final material selection, data points are validated with the material supplier.