LEXAN 3412ECR Polycarbonate (PC) is an injection moldable non-chlorinated and non-brominated flame retardant grade that is 20% glass fiber filled. It has a UL94 V0@1.5mm rating and is available in various opaque color options. This is an alternative to LEXAN 3412R and 3412HF.
| 原厂资料 | 物性表(英文) | |||
| 产品特性 | 阻燃无氯无溴填充增强 | |||
| 添加助剂 | 阻燃剂 | |||
| 颜色形状 | 不透明色 | |||
| 成型方式 | 注塑 | |||
| 增强填充 | 20% 玻纤 | |||
| 物理性能 | 值/单位 | 测试标准 | 测试条件 |
|---|---|---|---|
密度 | 1.36 g/cm³ | ISO 1183 | |
比重 | 1.3 - | ASTM D792 | |
熔体体积流动速率(MVR) | |||
300°C/1.2 kg | 7 cm³/10 min | ISO 1133 | |
熔体质量流动速率(MFR) | |||
300℃/1.2 kg | 7 g/10min | ASTM D1238 | |
收缩率 | |||
纵向(Flow) | 0.2~0.5 % | Internal | flow, 3.2 mm |
横向(Across Flow) | 0.2~0.5 % | Internal | xflow, 3.2 mm |
吸水率 | 0.29 % | ISO 62 | (23°C/sat) |
吸湿率 | 0.12 % | ISO 62 | 23°C / 50% RH |
| 机械性能 | 值/单位 | 测试标准 | 测试条件 |
拉伸强度 | |||
屈服(yld) | 90 Mpa | ASTM D638 | Type I, 5 mm/min |
屈服(yld) | 95 Mpa | ISO 527 | 5 mm/min |
断裂(brk) | 90 Mpa | ISO 527 | 5 mm/min |
断裂(brk) | 87 Mpa | ASTM D638 | Type I, 5 mm/min |
拉伸延伸率 | |||
屈服(yld) | 3.1 % | ASTM D638 | Type I, 5 mm/min |
屈服(yld) | 2.8 % | ISO 527 | 5 mm/min |
断裂(brk) | 3.2 % | ISO 527 | 5 mm/min |
弯曲强度 | |||
屈服(yld) | 156 Mpa | ASTM D790 | 1.3 mm/min, 50 mm span |
屈服(yld) | 140 Mpa | ISO 178 | 2 mm/min |
弯曲模量 | 5000 Mpa | ASTM D790 | 1.3 mm/min, 50 mm span |
弯曲模量 | 5500 Mpa | ISO 178 | 2 mm/min |
拉伸模量 | 5500 Mpa | ASTM D638 | 5 mm/min |
拉伸模量 | 6000 Mpa | ISO 527 | 1 mm/min |
| 冲击性能 | 值/单位 | 测试标准 | 测试条件 |
简支梁缺口(Charpy Notched) | |||
-30℃ (-22℉) | 5 kJ/m² | ISO 179/1eA | V-notch Edgew 80*10*3 sp=62mm |
23℃ (73℉) | 6 kJ/m² | ISO 179/1eA | V-notch Edgew 80*10*3 sp=62mm |
简支梁无缺口(Charpy Unnotched) | |||
-30℃ (-22℉) | 40 kJ/m² | ISO 179/1eU | Edgew 80*10*3 sp=62mm |
23℃ (73℉) | 40 kJ/m² | ISO 179/1eU | Edgew 80*10*3 sp=62mm |
悬臂梁缺口(Izod Notched) | |||
-30℃ (-22℉) | 107 J/m | ASTM D256 | |
-30℃ (-22℉) | 6 kJ/m² | ISO 180/1A | 80*10*3 |
23℃ (73℉) | 110 J/m | ASTM D256 | |
23℃ (73℉) | 7 kJ/m² | ISO 180/1A | 80*10*3 |
悬臂梁无缺口(Izod Unnotched) | |||
-30℃ (-22℉) | 35 kJ/m² | ISO 180/1U | 80*10*3 |
23℃ (73℉) | 35 kJ/m² | ISO 180/1U | 80*10*3 |
仪器化落镖冲击能量 | |||
23℃ (73℉)总能量 | 20 J | ASTM D3763 | |
| 热学性能 | 值/单位 | 测试标准 | 测试条件 |
热变形温度(HDT) | |||
0.45 Mpa (66 psi)（4.6kg/cm²） | 141 °C | ISO 75/Bf | Flatw 80*10*4 sp=64mm |
1.8 Mpa (264 psi)（18.6kg/cm²） | 141 °C | ASTM D648 | 3.2mm, unannealed |
1.8 Mpa (264 psi)（18.6kg/cm²） | 136 °C | ISO 75/Af | Flatw 80*10*4 sp=64mm |
维卡软化温度(Vicat) | 147 °C | ASTM D1525 | Rate B/50 |
维卡软化温度(Vicat) | 146 °C | ISO 306 | Rate B/120 |
维卡软化温度(Vicat) | 145 °C | ISO 306 | Rate B/50 |
相对温度指数(RTI) | |||
冲击Imp,- | 130 °C | UL 746B | |
冲击Imp,- | 130 °C | UL 746B | |
强度Str,- | 130 °C | UL 746B | |
线性膨胀系数(CLTE) | |||
纵向(Flow) | 30 E-6/°C | ASTM E831 | -40°C to 40°C, flow |
纵向(Flow) | 30 E-6/°C | ISO 11359-2 | 23°C to 80°C, flow |
横向(Across Flow) | 70 E-6/°C | ASTM E831 | -40°C to 40°C, xflow |
横向(Across Flow) | 70 E-6/°C | ISO 11359-2 | 23°C to 80°C, xflow |
球压痕温度 | 125 °C | IEC 60695-10-2 | PASS |
| 燃烧性能 | 值/单位 | 测试标准 | 测试条件 |
UL 防火等级 | |||
V-0 | 1.5 mm | UL94 | |
5VA | 3 mm | UL94 | |
氧指数(LOI) | 40 % | ISO 4589 | |
灼热丝可燃性指数(GWFI) | |||
1mm | 960 °C | IEC 60695-2-12 | pass |
灼热丝点燃温度(GWIT) | |||
1.0mm | 825 °C | IEC 60695-2-13 | |
| 电学性能 | 值/单位 | 测试标准 | 测试条件 |
体积电阻率 | 1.0E+15 Ohm-cm | IEC 60093 | |
表面电阻率 | 1.0E+15 Ohm | IEC 60093 | ROA |
介电常数(DK) | |||
50/60 Hz | 3.3 - | IEC 60250 | |
1MHz | 3.3 - | IEC 60250 | |
耗散因数(DF) | |||
50/60 Hz | 200 E-4 | IEC 60250 | |
1MHz | 100 E-4 | IEC 60250 | |
相对漏电起痕指数(CTI ) | |||
- | 3 PLC | UL 746A | |
绝缘强度 | 34 kV/mm | IEC 60243-1 | |
耐电弧性 | 7 PLC | ASTM D495 | Tungsten |
高电压电弧起痕速率(HVTR) | 3 PLC | UL 746A | |
热线圈起燃性(HWI) | 0 PLC | UL 746A | |
高电流电弧起燃性(HAI) | 3 PLC | UL 746A |
此物性表中的信息由阿技材料库从该材料的生产商处获得。阿技材料库尽最大努力确保此数据的准确性。 但是阿技材料库对这些数据值不承担任何责任，并强烈建议在最终选择材料前，就数据值与材料供应商进行验证。