| Physical | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Density/Specific Gravity |
*** g/cm³
| ISO 1183 | |
Density/Specific Gravity |
*** g/cm³
| ASTM D792 | |
Melt Volume Flow Rate(MVR) | | | |
220°C/10.0 kg |
*** cm³/10 min | ISO 1133 | |
260°C/5.0 kg |
*** cm³/10 min | ISO 1133 | |
Melt Mass Flow Rate(MFR) | | | |
220℃/10 kg |
*** g/10 min | ISO 1133 | |
220℃/10 kg |
*** g/10 min | ASTM D 1238 | |
260°C/5.0 kg |
*** g/10min | ASTM D1238 | |
| Mechanical | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Tensile Modulus |
*** Mpa
| ASTM D638 | Type I, 5 mm/min |
Tensile Modulus |
*** Mpa
| ISO 527 | 1 mm/min |
Tensile Strength | | | |
Yield |
*** Mpa | ASTM D638 | Type I, 5 mm/min |
Yield |
*** Mpa | ASTM D638 | Type I, 50 mm/min |
Yield |
*** Mpa | ISO 527 | 50 mm/min |
Yield |
*** Mpa | ISO 527 | Type I, 5 mm/min |
Break |
*** Mpa | ISO 527 | 50 mm/min |
Break |
*** Mpa | ISO 527 | Type I, 5 mm/min |
Break |
*** Mpa | ASTM D638 | Type I, 5 mm/min |
Break |
*** Mpa | ASTM D638 | Type I, 50 mm/min |
Tensile Elongation | | | |
Yield |
*** % | ASTM D638 | Type I, 5 mm/min |
Yield |
*** % | ASTM D638 | Type I, 50 mm/min |
Yield |
*** % | ISO 527 | 5 mm/min |
Yield |
*** % | ISO 527 | 50 mm/min |
Break |
*** % | ASTM D638 | Type I, 5 mm/min |
Break |
*** % | ASTM D638 | Type I, 50 mm/min |
Break |
*** % | ISO 527 | 50 mm/min |
Flexural Modulus |
*** Mpa
| ISO 178 | 2 mm/min |
Flexural Strength | | | |
Yield |
*** Mpa | ISO 178 | 2 mm/min |
| Impact | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Charpy Notched Impact Strengh | | | |
-30℃ (-22℉) |
*** kJ/m² | ISO 179/1eA | V-notch Edgew 80*10*4 sp=62mm |
23℃ (73℉) |
*** kJ/m² | ISO 179/1eA | V-notch Edgew 80*10*4 sp=62mm |
Izod Notched Impact Strengh | | | |
-30℃ (-22℉) |
*** J/m | ASTM D256 | |
-30℃ (-22℉) |
*** kJ/m² | ISO 180/1A | 80*10*4 |
23℃ (73℉) |
*** J/m | ASTM D256 | |
23℃ (73℉) |
*** kJ/m² | ISO 180/1A | 80*10*4 |
| Hardness | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Rockwell L |
*** L
| ISO 2039-2 | |
Shore D hardness |
*** D
| ISO 868 | |
Ball Indentation Hardness |
*** Mpa
| ISO 2039-1 | |
| Thermal | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Heat Deflection Temperature(HDT) | | | |
0.45 Mpa (66 psi)（4.6kg/cm²） |
*** °C | ISO 75/Bf | Flatw 80*10*4 sp=64mm |
1.8 Mpa (264 psi)（18.6kg/cm²） |
*** °C | ASTM D648 | 3.2mm, unannealed |
1.8 Mpa (264 psi)（18.6kg/cm²） |
*** °C | ISO 75/Af | Flatw 80*10*4 sp=64mm |
Vicat Softening Temperature(VST) |
*** °C
| ISO 306 | Rate A/120 |
Vicat Softening Temperature(VST) |
*** °C
| ISO 306 | Rate A/50 |
Vicat Softening Temperature(VST) |
*** °C
| ISO 306 | Rate B/120 |
Vicat Softening Temperature(VST) |
*** °C
| ISO 306 | Rate B/50 |
| Electrical | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Volume Resistivity |
*** Ohm-cm
| IEC 60093 | |
The information presented on this datasheet was acquired by AjiEng.com from the producer of the material. AjiEng.com makes substantial efforts to assure the accuracy of this data. However, AjiEng.com assumes no responsibility for the data values and strongly encourages that upon final material selection, data points are validated with the material supplier.