| Physical | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Density/Specific Gravity |
*** g/cm³
| ISO 1183 | |
Density/Specific Gravity |
*** g/cm³
| ASTM D792 | |
Melt Mass Flow Rate(MFR) | | | |
367°C/6.6 kg |
*** g/10 min | ASTM D 1238 | |
Mold Shrinkage | | | |
Flow |
***~*** % | Internal | flow, 3.2 mm |
Water Absorption |
*** %
| ASTM D570 | 23°C/48hrs |
Water Absorption |
*** %
| ISO 62 | 23°C/sat |
| Mechanical | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Tensile Modulus |
*** Mpa
| ASTM D638 | 5 mm/min |
Tensile Modulus |
*** Mpa
| ISO 527 | 1 mm/min |
Tensile Strength | | | |
Yield |
*** Mpa | ASTM D638 | Type I, 5 mm/min |
Yield |
*** Mpa | ISO 527 | 5 mm/min |
Break |
*** Mpa | ISO 527 | 5 mm/min |
Break |
*** Mpa | ASTM D638 | Type I, 5 mm/min |
Tensile Elongation | | | |
Yield |
*** % | ASTM D638 | Type I, 5 mm/min |
Yield |
*** % | ISO 527 | 5 mm/min |
Break |
*** % | ASTM D638 | Type I, 5 mm/min |
Break |
*** % | ISO 527 | 5 mm/min |
Flexural Modulus |
*** Mpa
| ASTM D790 | 1.3 mm/min, 50 mm span |
Flexural Modulus |
*** Mpa
| ISO 178 | 2 mm/min |
Flexural Strength | | | |
Yield |
*** Mpa | ASTM D790 | 1.3 mm/min, 50 mm span |
Yield |
*** Mpa | ISO 178 | 2 mm/min |
| Impact | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Charpy Notched Impact Strengh | | | |
23℃ (73℉) |
*** kJ/m² | ISO 179/1eA | V-notch Edgew 80*10*4 sp=62mm |
Izod Notched Impact Strengh | | | |
23℃ (73℉) |
*** J/m | ASTM D256 | |
23℃ (73℉) |
*** kJ/m² | ISO 180/1A | 80*10*4 |
Instrumented Impact Energy | | | |
23℃ (73℉)Total Energy |
*** J | ASTM D3763 | |
| Thermal | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Heat Deflection Temperature(HDT) | | | |
0.45 Mpa (66 psi)（4.6kg/cm²） |
*** °C | ASTM D648 | 3.2 mm, unannealed |
1.8 Mpa (264 psi)（18.6kg/cm²） |
*** °C | ASTM D648 | 3.2 mm, unannealed |
1.8 Mpa (264 psi)（18.6kg/cm²） |
*** °C | ASTM D648 | 6.4 mm, unannealed |
1.8 Mpa (264 psi)（18.6kg/cm²） |
*** °C | ISO 75/Af | Flatw 80*10*4 sp=64mm |
Vicat Softening Temperature(VST) |
*** °C
| ASTM D1525 | Rate B/50 |
Vicat Softening Temperature(VST) |
*** °C
| ISO 306 | Rate B/120 |
Vicat Softening Temperature(VST) |
*** °C
| ISO 306 | Rate B/50 |
Coefficient of Linear Thermal Expansion | | | |
Flow |
*** E-6/°C | ISO 11359-2 | 23°C to 150°C, flow |
Across Flow |
*** E-6/°C | ISO 11359-2 | 23°C to 150°C, xflow |
| Flammability | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Flame Rating | | | |
V-0 |
*** mm | UL94 | |
The information presented on this datasheet was acquired by AjiEng.com from the producer of the material. AjiEng.com makes substantial efforts to assure the accuracy of this data. However, AjiEng.com assumes no responsibility for the data values and strongly encourages that upon final material selection, data points are validated with the material supplier.