LNP COLORCOMP DX09304C is an unfilled polycarbonate (PC) resin. Added features of this grade include: easy molding, very low level of leachable ions and low outgassing.
| Original Document | Technical Datasheet(English) | |||
| Solutions | Semiconductor/Hard Disk Drive (HDD) | |||
| Features | Easy processingLow Out-gassingNo PFASLow leachable ions | |||
| Processing | Injection | |||
| Physical | Value/Unit(Sign in to View) | Test Standard | Test Condition |
|---|---|---|---|
Density/Specific Gravity | *** g/cm³ | ASTM D792 | |
Melt Mass Flow Rate(MFR) | |||
300℃/1.2 kg | *** g/10min | ASTM D1238 | |
Mold Shrinkage | |||
Flow | *** % | Internal | |
Across Flow | *** % | Internal | |
Water Absorption | |||
Saturation, 23°C | *** % | ISO 62 | |
| Mechanical | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Tensile Modulus | |||
- | *** Mpa | ISO 527 | 1 mm/min |
- | *** Mpa | ASTM D638 | 50 mm/min |
Tensile Strength | |||
Yield | *** Mpa | ASTM D638 | Type I, 50 mm/min |
Yield | *** Mpa | ISO 527 | 50 mm/min |
Break | *** Mpa | ISO 527 | 50 mm/min |
Break | *** Mpa | ASTM D638 | Type I, 50 mm/min |
Tensile Elongation | |||
Yield | *** % | ASTM D638 | Type I, 50 mm/min |
Break | *** % | ASTM D638 | Type I, 50 mm/min |
Break | *** % | ISO 527 | 50 mm/min |
Flexural Modulus | |||
- | *** Mpa | ISO 178 | 2 mm/min |
- | *** Mpa | ASTM D790 | 1.3 mm/min, 50 mm span |
Flexural Strength | |||
Yield | *** Mpa | ASTM D790 | 1.3 mm/min, 50 mm span |
Yield | *** Mpa | ISO 178 | 2 mm/min |
| Impact | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Charpy Notched Impact Strengh | |||
-30℃ (-22℉) | *** kJ/m² | ISO 179/1eA | Edgew 80*10*4 sp=62mm |
23℃ (73℉) | *** kJ/m² | ISO 179/1eA | Edgew 80*10*4 sp=62mm |
Charpy Unnotched Impact Strengh | |||
23℃ (73℉) | *** kJ/m² | ISO 179/1eU | Edgew 80*10*4 sp=62mm |
Izod Notched Impact Strengh | |||
-30℃ (-22℉) | *** J/m | ASTM D256 | |
-30℃ (-22℉) | *** kJ/m² | ISO 180/1A | 80*10*4 |
23℃ (73℉) | *** J/m | ASTM D256 | |
23℃ (73℉) | *** kJ/m² | ISO 180/1A | 80*10*4 |
Izod Unnotched Impact Strengh | |||
23℃ (73℉) | *** J/m | ASTM D4812 | |
23℃ (73℉) | *** kJ/m² | ISO 180/1U | 80*10*4 |
| Thermal | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Heat Deflection Temperature(HDT) | |||
0.45 Mpa (66 psi), Unannealed | *** °C | ASTM D648 | 3.2 mm |
1.8 Mpa (264 psi), Unannealed | *** °C | ASTM D648 | 3.2 mm |
Vicat Softening Temperature(VST) | |||
10N, 120℃/hr (A120/Loading1, RateB) | *** °C | ISO 306 | |
Coefficient of Linear Thermal Expansion | |||
Flow | *** E-6/°C | ISO 11359-2 | 23°C to 80°C |
Across Flow | *** E-6/°C | ISO 11359-2 | 23°C to 80°C |
The information presented on this datasheet was acquired by AjiEng.com from the producer of the material. AjiEng.com makes substantial efforts to assure the accuracy of this data. However, AjiEng.com assumes no responsibility for the data values and strongly encourages that upon final material selection, data points are validated with the material supplier.