LNP THERMOCOMP OFM46XXP compound is based on Polyphenylene Sulfide (PPS). Added features of this material include: high heat resistance, excellent dimensional stability and warpage control, low coefficient of thermal expansion.
| Original Document | Technical Datasheet(English) | |||
| Solutions | Automotive RADAR sensors(4D radar) | |||
| Features | Heat ResistanceDimensional StabilityLow WarpageLow CLTEFilled & Reinforced | |||
| Markets | Electrical / Electronics | |||
| Processing | Injection | |||
| Reinforced | Glass FiberMineralGlass Fiber+Minal | |||
| Physical | Value/Unit(Sign in to View) | Test Standard | Test Condition |
|---|---|---|---|
Density/Specific Gravity | *** g/cm³ | ASTM D792 | |
Mold Shrinkage | |||
Flow | ***~*** % | Internal | |
Across Flow | ***~*** % | Internal | |
Water Absorption | |||
In Water, 23°C, 24h | *** % | ISO 62 | |
23°C, 50% RH, 24h | *** % | ISO 62 | |
| Mechanical | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Tensile Modulus | |||
- | *** Mpa | ISO 527 | 1 mm/min |
- | *** Mpa | ASTM D638 | 5 mm/min |
Tensile Strength | |||
Break | *** Mpa | ISO 527 | 5 mm/min |
Break | *** Mpa | ASTM D638 | Type I, 5 mm/min |
Tensile Elongation | |||
Break | *** % | ASTM D638 | Type I, 5 mm/min |
Break | *** % | ISO 527 | 5 mm/min |
Flexural Modulus | |||
- | *** Mpa | ISO 178 | 2 mm/min |
- | *** Mpa | ASTM D790 | 1.3 mm/min, 50 mm span |
Flexural Strength | |||
- | *** Mpa | ASTM D790 | 1.3 mm/min, 50 mm span |
- | *** Mpa | ISO 178 | 2 mm/min |
| Impact | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Charpy Notched Impact Strengh | |||
23℃ (73℉) | *** kJ/m² | ISO 179/1eA | 80*10*4 |
Charpy Unnotched Impact Strengh | |||
23℃ (73℉) | *** kJ/m² | ISO 179/1eU | 80*10*4 |
Izod Notched Impact Strengh | |||
23℃ (73℉) | *** J/m | ASTM D256 | |
23℃ (73℉) | *** kJ/m² | ISO 180/1A | 80*10*4 |
Izod Unnotched Impact Strengh | |||
23℃ (73℉) | *** J/m | ASTM D4812 | |
23℃ (73℉) | *** kJ/m² | ISO 180/1U | 80*10*4 |
| Thermal | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Heat Deflection Temperature(HDT) | |||
0.45 Mpa (66 psi)（4.6kg/cm²） | *** °C | ISO 75/Bf | Flatw 80*10*4 sp=64mm |
0.45 Mpa (66 psi), Unannealed | *** °C | ASTM D648 | 3.2 mm |
1.8 Mpa (264 psi)（18.6kg/cm²） | *** °C | ISO 75/Af | Flatw 80*10*4 sp=64mm |
1.8 Mpa (264 psi), Unannealed | *** °C | ASTM D648 | 3.2 mm |
Relative Temperature Index(RTI), Imp | |||
- | *** °C | UL 746B | |
Relative Temperature Index(RTI), Elec | |||
- | *** °C | UL 746B | |
Relative Temperature Index(RTI), Str | |||
- | *** °C | UL 746B | |
Coefficient of Linear Thermal Expansion | |||
Flow | *** E-6/°C | ASTM E831 | -40°C to 40°C |
Flow | *** E-6/°C | ASTM E831 | -40°C to 90°C |
Flow | *** E-6/°C | ISO 11359-2 | -40°C to 40°C |
Flow | *** E-6/°C | ISO 11359-2 | -40°C to 90°C |
Across Flow | *** E-6/°C | ASTM E831 | -40°C to 40°C |
Across Flow | *** E-6/°C | ASTM E831 | -40°C to 90°C |
Across Flow | *** E-6/°C | ISO 11359-2 | -40°C to 40°C |
Across Flow | *** E-6/°C | ISO 11359-2 | -40°C to 90°C |
| Flammability | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Flame Rating | |||
V-1 | *** mm | UL94 | |
V-0 | *** mm | UL94 | |
| Electrical | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Dielectric Constant(Permittivity) | |||
1.9 GHz | *** - | Internal | |
5 GHz | *** - | Internal | |
Dissipation Factor | |||
1.9 GHz | *** E-4 | Internal | |
5 GHz | *** E-4 | Internal |
The information presented on this datasheet was acquired by AjiEng.com from the producer of the material. AjiEng.com makes substantial efforts to assure the accuracy of this data. However, AjiEng.com assumes no responsibility for the data values and strongly encourages that upon final material selection, data points are validated with the material supplier.