LNP KONDUIT WTF2C compound is based on Polybutylene Terephthalate (PBT) resin containing mineral and glass fiber. Added features of this grade include Thermally Conductive, Electrically Insulative, CTI-0 and having a stable di-electric property over a wide temperature range.
| Original Document | Technical Datasheet(English) | |||
| Solutions | Automotive RADAR sensors | |||
| Features | Heat ResistanceThermal ConductiveElectrically InsulatingEasy processingLaser Welding/Laser TransparentNo PFASFilled & Reinforced | |||
| Markets | AutomotiveElectrical / Electronics | |||
| Processing | Injection | |||
| Reinforced | Glass FiberMineralGlass Fiber+Minal | |||
| Physical | Value/Unit(Sign in to View) | Test Standard | Test Condition |
|---|---|---|---|
Density/Specific Gravity | *** g/cm³ | ISO 1183 | |
Density/Specific Gravity | *** g/cm³ | ASTM D792 | |
Mold Shrinkage | |||
Flow | *** % | Internal | |
Flow | *** % | ASTM D955 | |
Across Flow | *** % | Internal | |
Across Flow | *** % | ASTM D955 | |
Water Absorption | |||
In Water, 23°C, 24h | *** % | ISO 62 | |
In Water, 23°C, 24h | *** % | ASTM D570 | |
Equilibrium, 23°C, 50% RH | *** % | ISO 62 | |
23°C, 50% RH, 24h | *** % | ISO 62 | |
| Mechanical | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Tensile Modulus | |||
- | *** Mpa | ISO 527 | 1 mm/min |
- | *** Mpa | ASTM D638 | 5 mm/min |
Tensile Strength | |||
Break | *** Mpa | ISO 527 | 5 mm/min |
Break | *** Mpa | ASTM D638 | Type I, 5 mm/min |
Tensile Elongation | |||
Yield | *** % | ASTM D638 | Type I, 5 mm/min |
Yield | *** % | ISO 527 | 5 mm/min |
Break | *** % | ASTM D638 | Type I, 5 mm/min |
Flexural Modulus | |||
- | *** Mpa | ASTM D790 | 1.3 mm/min, 50 mm span |
Flexural Strength | |||
- | *** Mpa | ASTM D790 | 1.3 mm/min, 50 mm span |
| Impact | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Izod Notched Impact Strengh | |||
23℃ (73℉) | *** J/m | ASTM D256 | |
23℃ (73℉) | *** kJ/m² | ISO 180/1A | 80*10*4 |
Izod Unnotched Impact Strengh | |||
23℃ (73℉) | *** kJ/m² | ISO 180/1U | 80*10*4 |
| Thermal | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Heat Deflection Temperature(HDT) | |||
0.45 Mpa (66 psi)（4.6kg/cm²） | *** °C | ISO 75/Bf | Flatw 80*10*4 sp=64mm |
0.45 Mpa (66 psi), Unannealed | *** °C | ASTM D648 | 3.2mm |
1.8 Mpa (264 psi)（18.6kg/cm²） | *** °C | ISO 75/Af | Flatw 80*10*4 sp=64mm |
1.8 Mpa (264 psi), Unannealed | *** °C | ASTM D648 | 3.2mm |
Vicat Softening Temperature(VST) | |||
50N, 50℃/hr (B50/Loading2, RateA) | *** °C | ISO 306 | |
50N, 120℃/hr (B120/Loading2, RateB) | *** °C | ISO 306 | |
Coefficient of Linear Thermal Expansion | |||
Flow | *** E-6/°C | ISO 11359-2 | -40°C to 150°C |
Across Flow | *** E-6/°C | ISO 11359-2 | -40°C to 150°C |
Thermal Conductivity | |||
In Plane | *** W/(m K) | ISO 22007-2 | 60*60*3mm plaque |
Through Plane | *** W/(m K) | ISO 22007-2 | 60*60*3mm plaque |
- | *** W/m-°C | ISO 8302 | |
| Electrical | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Volume Resistivity | > *** Ohm-cm | ASTM D257 | |
Volume Resistivity | > *** Ohm-cm | IEC 60093 | |
Surface Resistivity | > *** Ohm | ASTM D257 | |
Surface Resistivity | > *** Ohm | IEC 60093 | |
Comparative Tracking Index (CTI) | |||
- | *** V | IEC 60112 | |
Comparative Tracking Index (CTI)-PLC | |||
PLC0 (≥ 600V) | *** - | UL 746A |
The information presented on this datasheet was acquired by AjiEng.com from the producer of the material. AjiEng.com makes substantial efforts to assure the accuracy of this data. However, AjiEng.com assumes no responsibility for the data values and strongly encourages that upon final material selection, data points are validated with the material supplier.