LNP KONDUIT 8TF36E compound is based on Liquid Crystal Polymer (LCP) resin containing 15% glass fibers and proprietary thermal filler. Added features of this grade include: Thermally Conductive, Electrically Insulative, High flow, Low Moisture Absorption, Low CTE values and suitable for light colors.
| Original Document | Technical Datasheet(English) | |||
| Solutions | Thermally Conductive(Heat Sinks) | |||
| Features | Heat ResistanceThermal ConductiveElectrically InsulatingLow CLTENo PFASHigh FlowLow Moisture AbsorptionFilled & Reinforced | |||
| Markets | Industrial ApplicationsElectrical / Electronics | |||
| Processing | Injection | |||
| Reinforced | 15% Glass Fiber | |||
| Physical | Value/Unit(Sign in to View) | Test Standard | Test Condition |
|---|---|---|---|
Density/Specific Gravity | *** g/cm³ | ASTM D792 | |
Melt Mass Flow Rate(MFR) | |||
345°C/2.16 kg | *** g/10min | ASTM D1238 | |
Mold Shrinkage | |||
Flow | *** % | Internal | |
Across Flow | *** % | Internal | |
Water Absorption | |||
In Water, 23°C, 24h | *** % | ISO 62 | |
| Mechanical | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Tensile Modulus | |||
- | *** Mpa | ISO 527 | 1 mm/min |
- | *** Mpa | ASTM D638 | 5 mm/min |
Tensile Strength | |||
Break | *** Mpa | ISO 527 | 5 mm/min |
Break | *** Mpa | ASTM D638 | Type I, 5 mm/min |
Tensile Elongation | |||
Break | *** % | ASTM D638 | Type I, 5 mm/min |
Break | *** % | ISO 527 | 5 mm/min |
Flexural Modulus | |||
- | *** Mpa | ISO 178 | 2 mm/min |
- | *** Mpa | ASTM D790 | 1.3 mm/min, 50 mm span |
Flexural Strength | |||
- | *** Mpa | ASTM D790 | 1.3 mm/min, 50 mm span |
- | *** Mpa | ISO 178 | 2 mm/min |
| Impact | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Charpy Notched Impact Strengh | |||
-30℃ (-22℉) | *** kJ/m² | ISO 179/1eA | Edgew 80*10*3 sp=62mm |
-30℃ (-22℉) | *** kJ/m² | ISO 179/1eA | Edgew 80*10*4 sp=62mm |
23℃ (73℉) | *** kJ/m² | ISO 179/1eA | Edgew 80*10*3 sp=62mm |
23℃ (73℉) | *** kJ/m² | ISO 179/1eA | Edgew 80*10*4 sp=62mm |
Charpy Unnotched Impact Strengh | |||
-30℃ (-22℉) | *** kJ/m² | ISO 179/1eU | Edgew 80*10*3 sp=62mm |
-30℃ (-22℉) | *** kJ/m² | ISO 179/1eU | Edgew 80*10*4 sp=62mm |
23℃ (73℉) | *** kJ/m² | ISO 179/1eU | Edgew 80*10*3 sp=62mm |
23℃ (73℉) | *** kJ/m² | ISO 179/1eU | Edgew 80*10*4 sp=62mm |
Izod Notched Impact Strengh | |||
-30℃ (-22℉) | *** J/m | ASTM D256 | |
-30℃ (-22℉) | *** kJ/m² | ISO 180/1A | 80*10*3 |
-30℃ (-22℉) | *** kJ/m² | ISO 180/1A | 80*10*4 |
23℃ (73℉) | *** J/m | ASTM D256 | |
23℃ (73℉) | *** kJ/m² | ISO 180/1A | 80*10*3 |
23℃ (73℉) | *** kJ/m² | ISO 180/1A | 80*10*4 |
Izod Unnotched Impact Strengh | |||
-30℃ (-22℉) | *** kJ/m² | ISO 180/1U | 80*10*3 |
-30℃ (-22℉) | *** kJ/m² | ISO 180/1U | 80*10*4 |
-30℃ (-22℉) | *** J/m | ASTM D 4812 | |
23℃ (73℉) | *** J/m | ASTM D4812 | |
23℃ (73℉) | *** kJ/m² | ISO 180/1U | 80*10*3 |
23℃ (73℉) | *** kJ/m² | ISO 180/1U | 80*10*4 |
Instrumented Impact Energy | |||
23℃ (73℉)peak | *** J | ASTM D3763 | |
23℃ (73℉)Total Energy | *** J | ASTM D3763 | |
| Thermal | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Heat Deflection Temperature(HDT) | |||
0.45 Mpa (66 psi)（4.6kg/cm²） | > *** °C | ISO 75/Bf | Flatw 80*10*4 sp=64mm |
0.45 Mpa (66 psi), Unannealed | *** °C | ASTM D648 | 3.2 mm |
1.8 Mpa (264 psi)（18.6kg/cm²） | *** °C | ISO 75/Af | Flatw 80*10*4 sp=64mm |
1.8 Mpa (264 psi), Unannealed | *** °C | ASTM D648 | 3.2 mm |
Vicat Softening Temperature(VST) | |||
50N, 50℃/hr (B50/Loading2, RateA) | *** °C | ISO 306 | |
50N, 120℃/hr (B120/Loading2, RateB) | *** °C | ISO 306 | |
Coefficient of Linear Thermal Expansion | |||
Flow | *** E-6/°C | ASTM E831 | 23°C to 150°C |
Flow | *** E-6/°C | ISO 11359-2 | 23°C to 150°C |
Across Flow | *** E-6/°C | ASTM E831 | 23°C to 150°C |
Across Flow | *** E-6/°C | ISO 11359-2 | 23°C to 150°C |
Thermal Conductivity | |||
In Plane | *** W/(m K) | ASTM E1461 | 25*0.4mm disc |
Through Plane | *** W/(m K) | ASTM E1461 | 10*10*3mm sample |
| Electrical | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Volume Resistivity | *** Ohm-cm | ASTM D257 | |
Surface Resistivity | *** Ohm | ASTM D257 | |
Dielectric Constant(Permittivity) | |||
1.1 GHz | *** - | Internal | |
1.9 GHz | *** - | Internal | |
5 GHz | *** - | Internal | |
10 GHz | *** - | Internal | |
Dissipation Factor | |||
1.1 GHz | *** E-4 | Internal | |
1.9 GHz | *** E-4 | Internal | |
5 GHz | *** E-4 | Internal | |
10 GHz | *** E-4 | Internal |
The information presented on this datasheet was acquired by AjiEng.com from the producer of the material. AjiEng.com makes substantial efforts to assure the accuracy of this data. However, AjiEng.com assumes no responsibility for the data values and strongly encourages that upon final material selection, data points are validated with the material supplier.