High flow high gloss polyetherimide (PEI) blend with internal mold release and enhanced ductility.
| Original Document | Technical Datasheet(English) | |||
| Solutions | Smart Watch FramesCell Phone Camera Deco RingsFront Frame for Mobile Phones | |||
| Features | Flame RetardantHigh GlossHigh Surface HardnessVacuum Deposition(Physical Vapor Deposition)Mold ReleaseNo PFASHigh Flow | |||
| Additive | Release Agent | |||
| Applications | Electronics & Electrical Applications | |||
| Processing | Injection | |||
| Physical | Value/Unit(Sign in to View) | Test Standard | Test Condition |
|---|---|---|---|
Density/Specific Gravity | *** g/cm³ | ISO 1183 | |
Density/Specific Gravity | *** g/cm³ | ASTM D792 | |
Melt Mass Flow Rate(MFR) | |||
337°C/6.7 kg | *** g/10 min | ASTM D 1238 | |
350°C/2.16 kg | *** g/10 min | ASTM D 1238 | |
Mold Shrinkage | |||
Flow | *** % | Internal | |
Across Flow | *** % | Internal | |
Water Absorption | |||
23°C, 50% RH, 24h | *** % | ISO 62 | |
| Mechanical | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Tensile Modulus | |||
- | *** Mpa | ISO 527 | 1 mm/min |
- | *** Mpa | ASTM D638 | 50 mm/min |
Tensile Strength | |||
Yield | *** Mpa | ASTM D638 | Type I, 50 mm/min |
Yield | *** Mpa | ISO 527 | 50 mm/min |
Break | *** Mpa | ISO 527 | 50 mm/min |
Break | *** Mpa | ASTM D638 | Type I, 50 mm/min |
Tensile Elongation | |||
Yield | *** % | ASTM D638 | Type I, 50 mm/min |
Yield | *** % | ISO 527 | 50 mm/min |
Break | *** % | ASTM D638 | Type I, 50 mm/min |
Break | *** % | ISO 527 | 50 mm/min |
Flexural Modulus | |||
- | *** Mpa | ISO 178 | 2 mm/min |
- | *** Mpa | ASTM D790 | 1.3 mm/min, 50 mm span |
Flexural Strength | |||
- | *** Mpa | ASTM D790 | 1.3 mm/min, 50 mm span |
- | *** Mpa | ISO 178 | 2 mm/min |
| Impact | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Charpy Notched Impact Strengh | |||
23℃ (73℉) | *** kJ/m² | ISO 179/1eA | 80*10*4 |
Charpy Unnotched Impact Strengh | |||
23℃ (73℉) | *** kJ/m² | ISO 179/1eU | 80*10*4 |
Izod Notched Impact Strengh | |||
23℃ (73℉) | *** J/m | ASTM D256 | |
23℃ (73℉) | *** kJ/m² | ISO 180/1A | 80*10*4 |
Izod Unnotched Impact Strengh | |||
23℃ (73℉) | *** J/m | ASTM D4812 | |
23℃ (73℉) | *** kJ/m² | ISO 180/1U | 80*10*4 |
| Thermal | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Heat Deflection Temperature(HDT) | |||
0.45 Mpa (66 psi)（4.6kg/cm²） | *** °C | ISO 75/Bf | 80*10*4 |
0.45 Mpa (66 psi), Unannealed | *** °C | ASTM D648 | 3.2 mm |
1.8 Mpa (264 psi)（18.6kg/cm²） | *** °C | ISO 75/Af | 80*10*4 |
1.8 Mpa (264 psi), Unannealed | *** °C | ASTM D648 | 3.2 mm |
Vicat Softening Temperature(VST) | |||
50N(5.1kg), 50℃/hr | *** °C | ISO 306 | |
50N(5.1kg), 50℃/hr | *** °C | ASTM D1525 | |
50N(5.1kg), 120℃/hr | *** °C | ISO 306 | |
50N(5.1kg), 120℃/hr | *** °C | ASTM D1525 | |
Relative Temperature Index(RTI), Imp | |||
- | *** °C | UL 746B | |
Relative Temperature Index(RTI), Elec | |||
- | *** °C | UL 746B | |
Relative Temperature Index(RTI), Str | |||
- | *** °C | UL 746B | |
Coefficient of Linear Thermal Expansion | |||
Flow | *** E-6/°C | ASTM E831 | 23°C to 150°C |
Flow | *** E-6/°C | ISO 11359-2 | 23°C to 150°C |
Across Flow | *** E-6/°C | ASTM E831 | 23°C to 150°C |
Across Flow | *** E-6/°C | ISO 11359-2 | 23°C to 150°C |
| Flammability | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Flame Rating | |||
V-0 | ≥ *** mm | UL94 |
The information presented on this datasheet was acquired by AjiEng.com from the producer of the material. AjiEng.com makes substantial efforts to assure the accuracy of this data. However, AjiEng.com assumes no responsibility for the data values and strongly encourages that upon final material selection, data points are validated with the material supplier.