ULTEM 1010UCL resin is an amorphous, transparent polyetherimide (PEI) thermoplastic offering enhanced flow and a glass transition temperature (Tg) of 217°C. 1010UCL offers the same performance as ULTEM 1010 resin and offers further enhanced cleanliness control for (optical) applications.
The natural (uncolored) version of this grade is compliant with RoHS and also with Halogen Free standards as IEC 61249-2-21 and e.g. IPC 4101E. For colored versions, compliance needs to be checked case by case.
| Original Document | Technical Datasheet(English) | |||
| Solutions | Optical Sensor LensesBoard to Board Connectors | |||
| Resin ID | PEI | |||
| Availability | AsiaEuropeNorth AmericaLatin AmericaSouth & Central America | |||
| Features | Heat ResistanceFlame RetardantHalogen FreeIR transmittanceLight TransmissionDimensional StabilityLow WarpageLow ShrinkageCreep ResistantEasy processingMetal PlatingLow Smoke DensityNon(Low)ToxicNo PFASChemical ResistanceHydrolysis ResistanceHigh Flow | |||
| Applications | Optical Lenses | |||
| Appearance | Pellets/GranulesClear/Transparent | |||
| Processing | Injection | |||
| Compliance | RoHS | |||
| Technical Notes | Transmittance-Temperature | |||
| Physical | Value/Unit(Sign in to View) | Test Standard | Test Condition |
|---|---|---|---|
Density/Specific Gravity | *** g/cm³ | ISO 1183 | |
Density/Specific Gravity | *** g/cm³ | ASTM D792 | |
Melt Volume Flow Rate(MVR) | |||
340°C/5.0 kg | *** cm³/10 min | ISO 1133 | |
360°C/5.0 kg | *** cm³/10 min | ISO 1133 | |
Melt Mass Flow Rate(MFR) | |||
367°C/6.6 kg | *** g/10 min | ASTM D 1238 | |
Mold Shrinkage | |||
Flow | ***~*** % | Internal | 3.2 mm |
Water Absorption | |||
Saturation, 23°C | *** % | ISO 62 | |
Saturation, 23°C | *** % | ASTM D570 | |
In Water, 23°C, 24h | *** % | ASTM D570 | |
Equilibrium, 23°C, 50% RH | *** % | ISO 62 | |
Abrasion resistance | |||
Taber Abrasion, CS-17, 1 kg, 1000cy | *** mg | Internal | |
Taber Abrasion, CS-17, 1 kg, 1000cy | *** mg | ASTM D1044 | |
| Mechanical | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Tensile Modulus | |||
- | *** Mpa | ISO 527 | 1 mm/min |
- | *** Mpa | ASTM D638 | 1 mm/min |
Tensile Strength | |||
Yield | *** Mpa | ASTM D638 | 5 mm/min |
Yield | *** Mpa | ISO 527 | 50 mm/min |
Break | *** Mpa | ISO 527 | 50 mm/min |
Tensile Elongation | |||
Yield | *** % | ASTM D638 | 5 mm/min |
Yield | *** % | ISO 527 | 50 mm/min |
Break | *** % | ASTM D638 | 5 mm/min |
Break | *** % | ISO 527 | 50 mm/min |
Flexural Modulus | |||
- | *** Mpa | ISO 178 | 2 mm/min |
- | *** Mpa | ASTM D790 | 2.6 mm/min, 100 mm span |
Flexural Strength | |||
Yield | *** Mpa | ASTM D790 | 2.6 mm/min, 100 mm span |
Yield | *** Mpa | ISO 178 | 2 mm/min |
| Impact | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Izod Notched Impact Strengh | |||
-30℃ (-22℉) | *** kJ/m² | ISO 180/1A | 80*10*4 |
23℃ (73℉) | *** J/m | ASTM D256 | |
23℃ (73℉) | *** kJ/m² | ISO 180/1A | 80*10*4 |
Izod Unnotched Impact Strengh | |||
-30℃ (-22℉) | *** kJ/m² | ISO 180/1U | 80*10*4 |
23℃ (73℉) | *** J/m | ASTM D4812 | |
23℃ (73℉) | *** kJ/m² | ISO 180/1U | 80*10*4 |
Falling Dart Impact | *** J | ASTM D 3029 | |
Reverse Impact | |||
Izod, notched 23°C | *** J/m | ASTM D 256 | |
| Hardness | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Rockwell M | *** M | ASTM D 785 | |
Ball Indentation Hardness | |||
H358/30 | *** Mpa | ISO 2039-1 | |
| Thermal | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Heat Deflection Temperature(HDT) | |||
0.45 Mpa (66 psi)（4.6kg/cm²） | *** °C | ISO 75/Be | Edgew 120*10*4 sp=100mm |
0.45 Mpa (66 psi), Unannealed | *** °C | ASTM D648 | 6.4 mm |
1.8 Mpa (264 psi)（18.6kg/cm²） | *** °C | ISO 75/Ae | Edgew 120*10*4 sp=100mm |
1.8 Mpa (264 psi), Unannealed | *** °C | ASTM D648 | 6.4 mm |
Vicat Softening Temperature(VST) | |||
10N(1kg), 50℃/hr | *** °C | ISO 306 | |
50N(5.1kg), 50℃/hr | *** °C | ISO 306 | |
50N(5.1kg), 50℃/hr | *** °C | ASTM D1525 | |
50N(5.1kg), 120℃/hr | *** °C | ISO 306 | |
Coefficient of Linear Thermal Expansion | |||
Flow | *** E-6/°C | ASTM E831 | |
Flow | *** E-6/°C | ISO 11359-2 | 23°C to 150°C |
Across Flow | *** E-6/°C | ISO 11359-2 | 23°C to 150°C |
Thermal Conductivity | |||
- | *** W/m-°C | ISO 8302 | |
- | *** W/m-°C | ASTM C177 | |
Ball Pressure Test | *** °C | IEC 60695-10-2 | |
| Electrical | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Volume Resistivity | *** Ohm-cm | ASTM D257 | |
Volume Resistivity | *** Ohm-cm | IEC 60093 | |
Surface Resistivity | > *** Ohm | IEC 60093 | |
Dielectric Constant(Permittivity) | |||
50/60 Hz | *** - | IEC 60250 | |
1 kHz | *** - | ASTM D 150 | |
1MHz | *** - | IEC 60250 | |
Dissipation Factor | |||
50/60 Hz | *** E-4 | IEC 60250 | |
1 kHz | *** E-4 | ASTM D 150 | |
1MHz | *** E-4 | IEC 60250 | |
2450 MHz | *** E-4 | IEC 60250 | |
2450 MHz | *** E-4 | ASTM D 150 | |
Dielectric Strength | |||
In oil, 0.8 mm | *** kV/mm | IEC 60243-1 | |
In oil, 1.6 mm | *** kV/mm | IEC 60243-1 | |
In oil, 1.6 mm | *** kV/mm | ASTM D149 | |
In oil, 3.2 mm | *** kV/mm | IEC 60243-1 | |
In air, 1.6 mm | *** kV/mm | ASTM D149 | |
| Optical | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Light Transmission | |||
1.0mm | *** % | ASTM D1003 | 1350 nm |
1.0mm | *** % | ASTM D1003 | 850 nm |
Refractive Index | *** - | ISO 489 | 1350 nm |
Refractive Index | *** - | ISO 489 | 850 nm |
Abbe Number | *** - | ISO 489 |
The information presented on this datasheet was acquired by AjiEng.com from the producer of the material. AjiEng.com makes substantial efforts to assure the accuracy of this data. However, AjiEng.com assumes no responsibility for the data values and strongly encourages that upon final material selection, data points are validated with the material supplier.