25% Glass Fiber Reinforced, Heat Stabilized
| Original Document | Technical Datasheet(English) | |||
| Resin ID | PA46-GF25 | |||
| Features | Heat ResistanceHeat StabilizedFilled & Reinforced | |||
| Additive | Heat Stabilizer | |||
| Processing | Injection | |||
| Automotive Specs | PSA Peugeot-Citroen Yes: UnspecifiedStellantis Yes: Unspecified | |||
| Diagrams | Stress-strainSecant modulus-strain | |||
| Reinforced | 25% Glass Fiber | |||
| Physical | Dry/Cond.(Sign in to View) | Unit | Test Standard | Test Condition |
|---|---|---|---|---|
Density/Specific Gravity | ***/ *** | g/cm³ | ISO 1183 | |
Mold Shrinkage | ||||
Flow | ***/ * | % | ISO 294-4 | |
Across Flow | ***/ * | % | ISO 294-4 | |
Water Absorption | ***/ * | % | ISO 62 | |
Water Absorption | ***/ * | % | ISO 62 | in water at 23°C after 24h |
Moisture /Humidity Absorption | ***/ * | % | ISO 62 | |
| Mechanical | Dry/Cond.(Sign in to View) | Unit | Test Standard | Test Condition |
Tensile Modulus | ***/ *** | Mpa | ISO 527-1/-2 | |
Tensile Modulus | ***/ *** | Mpa | ISO 527-1/-2 | -40°C |
Tensile Modulus | ***/ *** | Mpa | ISO 527-1/-2 | 120°C |
Tensile Modulus | ***/ * | Mpa | ISO 527-1/-2 | 150°C |
Tensile Modulus | ***/ * | Mpa | ISO 527-1/-2 | 180°C |
Tensile Modulus | ***/ * | Mpa | ISO 527-1/-2 | 65°C |
Tensile Modulus | ***/ * | Mpa | ISO 527-1/-2 | 90°C |
Tensile Strength | ||||
Break | ***/ *** | Mpa | ISO 527-1/-2 | |
Break | ***/ *** | Mpa | ISO 527-1/-2 | -40°C |
Break | ***/ *** | Mpa | ISO 527-1/-2 | 120°C |
Break | ***/ * | Mpa | ISO 527-1/-2 | 150°C |
Break | ***/ * | Mpa | ISO 527-1/-2 | 180°C |
Break | ***/ * | Mpa | ISO 527-1/-2 | 65°C |
Break | ***/ * | Mpa | ISO 527-1/-2 | 90°C |
Tensile Elongation | ||||
Break | ***/ *** | % | ISO 527-1/-2 | |
Break | ***/ *** | % | ISO 527-1/-2 | -40°C |
Break | ***/ * | % | ISO 527-1/-2 | 120°C |
Break | ***/ * | % | ISO 527-1/-2 | 150°C |
Break | ***/ * | % | ISO 527-1/-2 | 180°C |
Break | ***/ * | % | ISO 527-1/-2 | 65°C |
Break | ***/ * | % | ISO 527-1/-2 | 90°C |
Flexural Modulus | ***/ *** | Mpa | ISO 178 | |
Flexural Strength | ||||
- | ***/ *** | Mpa | ISO 178 | |
Weld strength | ***/ *** | Mpa | ISO 527-1/-2 | 4mm |
Weld elongation | ***/ *** | % | ISO 527-1/-2 | 4mm |
| Impact | Dry/Cond.(Sign in to View) | Unit | Test Standard | Test Condition |
Charpy Notched Impact Strengh | ||||
23℃ (73℉) | ***/ *** | kJ/m² | ISO 179/1eA | |
| Thermal | Dry/Cond.(Sign in to View) | Unit | Test Standard | Test Condition |
Heat Deflection Temperature(HDT) | ||||
1.8 Mpa (264 psi)（18.6kg/cm²） | ***/ * | °C | ISO 75-1/-2 | |
Coefficient of Linear Thermal Expansion | ||||
Flow | ***/ * | E-6/°C | ASTM D 696 | |
Across Flow | ***/ * | E-6/°C | ASTM D 696 | |
Melt Temperature(Tm) | ***/ * | °C | ISO 11357-1/-3 | 10°C/min |
Glass Transition Temperature | ***/ * | °C | ISO 11357-1/-2 | 10°C/min |
The information presented on this datasheet was acquired by AjiEng.com from the producer of the material. AjiEng.com makes substantial efforts to assure the accuracy of this data. However, AjiEng.com assumes no responsibility for the data values and strongly encourages that upon final material selection, data points are validated with the material supplier.