Low/Medium Viscosity, Food Contact Quality
EcoPaXX® Q150-D is a long aliphatic polyamide that offers low moisture uptake, good dimensional stability and excellent retention of properties.
| Original Document | Technical Datasheet(English) | |||
| Resin ID | PA410 | |||
| Features | Dimensional StabilityBio-basedFood ContactLow viscosityMedium viscosityLow Moisture Absorption | |||
| Processing | Injection | |||
| Diagrams | Stress-strainStress-strain (Cond.)Dynamic tensile modulus(E storage)-temperatureDynamic Shear modulus (G storage)-temperatureDynamic Shear modulus-temperatureDynamic tensile modulus-temperatureSecant modulus-strainSecant modulus-strain (Cond.) | |||
| Biobased/Renewable | Yes | |||
| Physical | Dry/Cond.(Sign in to View) | Unit | Test Standard | Test Condition |
|---|---|---|---|---|
Density/Specific Gravity | ***/ *** | g/cm³ | ISO 1183 | |
Mold Shrinkage | ||||
Flow | ***/ * | % | ISO 294-4 | |
Across Flow | ***/ * | % | ISO 294-4 | |
Moisture /Humidity Absorption | ***/ * | % | ISO 62 | |
Viscosity | ***/ * | Pa-s | ISO 307, 1157, 1628 | |
Melt Density | ***/ * | g/cm³ | - | |
| Mechanical | Dry/Cond.(Sign in to View) | Unit | Test Standard | Test Condition |
Tensile Modulus | ***/ *** | Mpa | ISO 527-1/-2 | |
Tensile Modulus | ***/ *** | Mpa | ISO 527-1/-2 | -40°C |
Tensile Modulus | ***/ *** | Mpa | ISO 527-1/-2 | 100°C |
Tensile Modulus | ***/ *** | Mpa | ISO 527-1/-2 | 120°C |
Tensile Modulus | ***/ * | Mpa | ISO 527-1/-2 | 160°C |
Tensile Modulus | ***/ * | Mpa | ISO 527-1/-2 | 180°C |
Tensile Modulus | ***/ * | Mpa | ISO 527-1/-2 | 200°C |
Tensile Strength | ||||
Yield | ***/ *** | Mpa | ISO 527-1/-2 | |
Yield | ***/ * | Mpa | ISO 527-1/-2 | -40°C |
Yield | ***/ * | Mpa | ISO 527-1/-2 | 100°C |
Tensile Elongation | ||||
Yield | ***/ *** | % | ISO 527-1/-2 | |
Yield | ***/ * | % | ISO 527-1/-2 | -40°C |
Nominal Tensile Strain at Break | ***/> *** | % | ISO 527-1/-2 | |
Nominal Tensile Strain at Break | ***/ *** | % | ISO 527-1/-2 | -40°C |
Nominal Tensile Strain at Break | > ***/ * | % | ISO 527-1/-2 | 100°C |
Flexural Modulus | ***/ *** | Mpa | ISO 178 | |
Flexural Strength | ||||
- | ***/ *** | Mpa | ISO 178 | |
Weld strength | ***/ *** | Mpa | ISO 527-1/-2 | 4mm |
Weld elongation | ***/ *** | % | ISO 527-1/-2 | 4mm |
| Impact | Dry/Cond.(Sign in to View) | Unit | Test Standard | Test Condition |
Charpy Notched Impact Strengh | ||||
-30℃ (-22℉) | ***/ *** | kJ/m² | ISO 179/1eA | |
23℃ (73℉) | ***/ *** | kJ/m² | ISO 179/1eA | |
Charpy Unnotched Impact Strengh | ||||
-30℃ (-22℉) | ***/ *** | kJ/m² | ISO 179/1eU | |
23℃ (73℉) | ***/ *** | kJ/m² | ISO 179/1eU | |
| Thermal | Dry/Cond.(Sign in to View) | Unit | Test Standard | Test Condition |
Heat Deflection Temperature(HDT) | ||||
0.45 Mpa (66 psi)（4.6kg/cm²） | ***/ * | °C | ISO 75-1/-2 | |
1.8 Mpa (264 psi)（18.6kg/cm²） | ***/ * | °C | ISO 75-1/-2 | |
Coefficient of Linear Thermal Expansion | ||||
Flow | ***/ * | E-6/°C | ISO 11359-1/-2 | |
Across Flow | ***/ * | E-6/°C | ISO 11359-1/-2 | |
Melt Temperature(Tm) | ***/ * | °C | ISO 11357-1/-3 | 10°C/min |
| Flammability | Dry/Cond.(Sign in to View) | Unit | Test Standard | Test Condition |
Flame Rating | ||||
HB | ***/ * | mm | UL94 | |
HB | ***/ * | mm | IEC 60695-11-10 | |
Glow Wire Flammability Index(GWFI) | ||||
0.8mm | ***/ * | °C | IEC 60695-2-12 | |
Glow Wire Ignition Test(GWIT) | ||||
0.8mm | ***/ * | °C | IEC 60695-2-13 |
The information presented on this datasheet was acquired by AjiEng.com from the producer of the material. AjiEng.com makes substantial efforts to assure the accuracy of this data. However, AjiEng.com assumes no responsibility for the data values and strongly encourages that upon final material selection, data points are validated with the material supplier.