Blow Molding Grade, Heat Stabilized
| Original Document | Technical Datasheet(English) | |||
| Resin ID | TPC-ET | |||
| Features | Heat Stabilized | |||
| Additive | Heat Stabilizer | |||
| Processing | Blow Molding | |||
| Automotive Specs | Renault Yes: UnspecifiedGM(General Motors) Yes: UnspecifiedVAG(Volkswagen Group) VW 50123-022-04-TPC-ETPSA Peugeot-Citroen FTM 78 0026 | |||
| Diagrams | Stress-strain (TPE)Dynamic tensile modulus(E storage)-temperatureDynamic tensile modulus-temperature | |||
| Physical | Value/Unit(Sign in to View) | Test Standard | Test Condition |
|---|---|---|---|
Density/Specific Gravity | *** g/cm³ | ISO 1183 | |
Melt Volume Flow Rate(MVR) | |||
230°C/10 kg | *** cm³/10min | ISO 1133 | |
Mold Shrinkage | |||
Flow | *** % | ISO 294-4 | |
Across Flow | *** % | ISO 294-4 | |
Water Absorption | *** % | ISO 62 | |
Moisture /Humidity Absorption | *** % | ISO 62 | |
| Mechanical | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Tensile Modulus | *** Mpa | ISO 527-1/-2 | |
Tensile Strength | |||
Break | *** Mpa | ISO 527-1/-2 | |
Break | *** Mpa | ISO 527-1/-2 | normal, die cutting |
at 5% strain | *** Mpa | ISO 527-1/-2 | |
at 5% strain | *** Mpa | ISO 527-1/-2 | normal, die cutting |
at 10% strain | *** Mpa | ISO 527-1/-2 | |
at 10% strain | *** Mpa | ISO 527-1/-2 | 100°C, parallel, die cutting |
at 10% strain | *** Mpa | ISO 527-1/-2 | normal, die cutting |
at 10% strain | *** Mpa | ISO 527-1/-2 | parallel, die cutting |
at 50% strain | *** Mpa | ISO 527-1/-2 | |
at 50% strain | *** Mpa | ISO 527-1/-2 | normal, die cutting |
at 100% strain | *** Mpa | ISO 527-1/-2 | |
at 100% strain | *** Mpa | ISO 527-1/-2 | normal, die cutting |
Tensile Elongation | |||
Break | *** % | ISO 527-1/-2 | normal, die cutting |
Nominal Tensile Strain at Break | *** % | ISO 527-1/-2 | |
Flexural Modulus | *** Mpa | ISO 178 | |
Flexural Modulus | *** Mpa | ISO 178 | 120°C |
Tear Strength | *** kN/m | ISO 34 | normal, die cutting |
Tear Strength | *** kN/m | ISO 34 | parallel, die cutting |
Compression Set | *** % | ISO 815 | 70 °C |
| Impact | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Charpy Notched Impact Strengh | |||
-30℃ (-22℉) | *** kJ/m² | ISO 179/1eA | |
23℃ (73℉) | *** kJ/m² | ISO 179/1eA | |
Charpy Unnotched Impact Strengh | |||
-30℃ (-22℉) | *** kJ/m² | ISO 179/1eU | |
23℃ (73℉) | *** kJ/m² | ISO 179/1eU | |
| Hardness | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Shore A hardness | *** A | ISO 868 | 3s |
Shore D hardness | *** D | ISO 868 | 3s |
| Thermal | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Heat Deflection Temperature(HDT) | |||
0.45 Mpa (66 psi)（4.6kg/cm²） | *** °C | ISO 75-1/-2 | |
Melt Temperature(Tm) | *** °C | ISO 11357-1/-3 | 10°C/min |
Glass Transition Temperature | *** °C | ISO 11357-1/-2 | 10°C/min |
The information presented on this datasheet was acquired by AjiEng.com from the producer of the material. AjiEng.com makes substantial efforts to assure the accuracy of this data. However, AjiEng.com assumes no responsibility for the data values and strongly encourages that upon final material selection, data points are validated with the material supplier.